TWO-COMPONENT SOLVENTLESS ADHESIVE COMPOSITIONS

Abstract

Two-component solventless polyurethane adhesive compositions comprising an isocyanate component and an isocyanate-reactive component are disclosed, the compositions comprising an isocyanate component comprising an isocyanate-terminated prepolymer, and an isocyanate-reactive component comprising a polyether polyol, a phosphate ester adhesion promoter, and, a bio-based polyol. Methods for forming laminate structures are also disclosed, the methods comprising forming an adhesive composition by mixing an isocyanate adhesive component comprising an isocyanate-terminated prepolymer and an isocyanate-reactive adhesive component comprising a polyether polyol, a phosphate ester adhesion promoter, and a bio-based polyol, applying the adhesive composition to a surface of a first substrate, and bringing a surface of a second substrate into contact with the adhesive composition on the surface of the first substrate, thereby forming the laminate structure. Laminate structures are also disclosed.

Claims

1. A two-component solventless adhesive composition, comprising: an isocyanate component comprising an isocyanate-terminated prepolymer; and an isocyanate-reactive component comprising: a polyether polyol; a phosphate ester adhesion promoter; and a bio-based polyol.

2. The two-component solventless adhesive composition of claim 1, wherein the polyether polyol accounts for 10 to 90 percent of the total weight of the isocyanate-reactive component.

3. The two-component solventless adhesive composition of claim 1, wherein the phosphate ester is made from a tri-functional propylene glycol, a polyphosphoric acid, and a polyisocyanate.

4. The two-component solventless adhesive composition of claim 1, wherein the phosphate ester adhesion promoter accounts for 0.5 to 15 percent of the total weight of the isocyanate-reactive component.

5. The two-component solventless adhesive composition of claim 1, wherein the bio-based polyol accounts for 5 to 80 percent of the total weight of the isocyanate-reactive component.

6. The two-component solventless adhesive composition of claim 1, wherein the bio-based polyol is castor oil.

7. The two-component solventless adhesive composition of claim 1, wherein the mole ratio of the NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 0.8:1.0 to 1.6:1.0.

8. A laminate structure comprising the two-component solventless adhesive composition of claim 1.

9. A method for forming a laminate structure, comprising: forming an adhesive composition by mixing an isocyanate adhesive component comprising an isocyanate-terminated prepolymer and an isocyanate-reactive adhesive component comprising a polyether polyol, a phosphate ester adhesion promoter, and a bio-based polyol; applying the adhesive composition to a surface of a first substrate; and bringing a surface of a second substrate into contact with the adhesive composition on the surface of the first substrate, thereby forming the laminate structure.

10. The method for forming a laminate structure of claim 1, wherein mixing the isocyanate adhesive component and the isocyanate-reactive adhesive component occurs at a mole ratio of the NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 0.8:1.0 to 1.6:1.0.

11. The method for forming a laminate structure of claim 1, wherein the first substrate and the second substrate are each independently selected from the group consisting of a wood material, a metallic material, a plastic material, a composite material, a paper material, a fabric material, and combinations of two or more thereof.

Description

DETAILED DESCRIPTION OF THE DISCLOSURE

[0012] In some embodiments, the two-component solventless adhesive compositions according to this disclosure include an isocyanate component and an isocyanate-reactive component.

[0013] Isocyanate Component

[0014] In some embodiments, the isocyanate component comprises an isocyanate-terminated prepolymer. In some embodiments, the isocyanate-terminated prepolymer is the reaction product of a polyisocyanate and a polyol component. In such a reaction, the polyisocyanate is present in excess in order to produce an isocyanate-terminated prepolymer. As used herein, a polyisocyanate is any compound that contains two or more isocyanate groups. In some embodiments, the polyisocyanate can be isocyanate monomers. In some embodiments, polyisocyanates may include dimers, trimers, etc.

[0015] In some embodiments, suitable polyisocyanates for use according to this disclosure can be selected from the group consisting of an aliphatic polyisocyanate, a cycloaliphatic polyisocyanate, an aromatic polyisocyanate, and combinations of two or more thereof. An aromatic polyisocyanate is a polyisocyanate that an isocyanate radical bonded to an aromatic radical and contains one or more aromatic rings. An aliphatic polyisocyanate contains no isocyanate radical directly bonded to an aromatic ring or is better defined as an isocyanate which contains an isocyanate radical bonded to an aliphatic radical which can be bonded to other aliphatic groups, a cycloaliphatic radical or an aromatic ring (radical). A cycloaliphatic polyisocyanate is a subset of aliphatic polyisocyanates, wherein the chemical chain is ring-structured.

[0016] Suitable aromatic polyisocyanates include, but are not limited to, 1,3- and 1,4-phenylene diisocyanate, 1,5-naphthylene diisocyanate, 2,6-tolulene diisocyanate (2,6-TDI), 2,4-tolulene diisocyanate (2,4-TDI), 2,4-diphenylmethane diisocyanate (2,4-MDI), 4,4-diphenylmethane diisocyanate (4,4-MDI), 3,3-dimethyl-4,4-biphenyldiisocyanate (TODI), and mixtures of two or more thereof. Suitable aliphatic polyisocyanates have 3 to 16 carbon atoms, or 4 to 12 carbon atoms, in the linear or branched alkylene residue, such as hexamethylene diisocyanate (HDI) and 1,4-diisocyanatobutane, and mixtures of the of two or more thereof.

[0017] Suitable cycloaliphatic polyisocyanates have 4 to 18 carbon atoms, or 6 to 15 carbon atoms, in the cycloalkylene residue. Cycloaliphatic diisocyanates refer to both cyclically and aliphatically bound NCO groups, such as isophorone diisocyanate (IPDI), 1,3/1,4-diisocyanatocyclohexane 1,3-/1,4-bis(isocyanatomethyl)cyclohexane, and diisocyanatodicyclohexylmethane (H12MDI), and mixtures of the of two or more thereof.

[0018] Suitable aliphatic and cycloaliphatic polyisocyanates include, but are not limited to, cyclohexane diisocyanate, methylcyclohexane diisocyanate, ethylcyclohexane diisocyanate, propylcyclohexane diisocyanate, methyldiethylcyclohexane diisocyanate, propane diisocyanate, butane diisocyanate, pentane diisocyanate, hexane diisocyanate, heptane diisocyanate, octane diisocyanate, nonane diisocyanate, nonane triisocyanate, such as 4-isocyanatomethyl-1,8-octane diisocyanate (TIN), decane di- and triisocyanate, undecane di- and triisocyanate and dodecane di- and triisocyanate, isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), diisocyanatodicyclohexylmethane (H12MDI), 2-methylpentane diisocyanate (MPDI), 2,2,4-trimethylhexamethylene diisocyanate/2,4,4-trimethylhexamethylene diisocyanate (TMDI), norbornane diisocyanate (NBDI), xylylene diisocyanate (XDI), tetramethylxylylene diisocyanate, and dimers, trimers, and mixtures of the of two or more thereof. Additional polyisocyanates suitable for use according to this disclosure include, but are not limited to, 4-methyl-cyclohexane 1,3-diisocyanate, 2-butyl-2-ethylpentamethylene diisocyanate, 3(4)-isocyanatomethyl-1-methylcyclohexyl isocyanate, 2-isocyanatopropylcyclohexyl isocyanate, 2,4-methylenebis(cyclohexyl) diisocyanate, 1,4-diisocyanato-4-methyl-pentane, and mixtures of the of two or more thereof.

[0019] In some embodiments, the isocyanate component has a NCO content of at least 3%, or at least 6%, or at least 10%. In some embodiments, the isocyanate component has a NCO content not to exceed 25%, or 18%, or 14%. In some embodiments, the isocyanate component has a NCO content of from 3 to 25%, or from 6 to 18%, or from 10 to 14%. NCO content is determined according to ASTM D2572. In some embodiments, the isocyanate component has viscosity at 25 C. of from 300 to 40,000 mPa.Math.s, or from 500 to 20,000 mPa.Math.s, or from 1,000 to 10,000 mPa.Math.s, as measured by the method of ASTM D2196.

[0020] In some embodiments, the polyol component, to be reacted with the polyisocyanate to form the isocyanate-terminated prepolymer, comprises a polyol having a hydroxyl functionality of two or greater. As used herein, the term hydroxyl functionality refers to the number of isocyanate-reactive sites on a molecule. For polyols, an average hydroxyl functionality is generally the total moles of OH divided by the total moles of polyol. In some embodiments, the polyol having a functionality of two or greater and is selected from the group consisting of a polyester polyol, a polyether polyol, and mixtures thereof.

[0021] The isocyanate component can further comprise other constituents commonly known to those of ordinary skill in the art.

[0022] Isocyanate-Reactive Component

[0023] In some embodiments, the isocyanate-reactive component comprises a polyether polyol, a phosphate ester adhesion promoter, and a bio-based polyol.

[0024] In some embodiments, the polyether polyol has a hydroxy functionality of two or more (e.g., di-functional, tri-functional, and so on). In some embodiments, the polyether polyol has a hydroxyl number from 100 to 400 mg KOH/g, measured according to ASTM D4274. In some embodiments, the polyether polyol has a number average molecular weight from 100 to 3,000, from 200 to 2,500, or from 350 to 1,500. In some embodiments, the polyether polyol has a viscosity at 25 C. from 50 to 1000 cps, measured according to ASTM D4878. Commercially available examples of polyether polyols suitable for use according to this disclosure include products sold under the trade names VORANOL CP-450, VORANOL CP-755, VORANOL CP-1055, VORANOL 220-260, VORANOL 220-056N and VORANOL 220-110N, each available from The Dow Chemical Company. In some embodiments, the polyether polyol further comprises a triol with molecular weight less than 300. Commercially available examples of the triol suitable for use according to this disclosure include trimethylolpropane (TMP) available from Sigma-Aldrich. In some embodiments, the amount of the polyether polyol in the isocyanate-reactive component is, by weight based on the weight of the isocyanate-reactive component, from 10 to 90 wt %, or from 40 to 80 wt %, or from 55 to 70 wt %.

[0025] In some embodiments, the phosphate ester adhesion promoter comprises a phosphate ester-based polyol. In some embodiments, the phosphate ester-based polyol is made from a tri-functional or di-functional propylene glycol, a polyphosphoric acid, and a polyisocyanate. In some embodiments, the phosphate ester-based polyol has a phosphoric acid content of less than 4 weight percent based on the weight of the phosphate ester polyol, or a phosphoric acid content of from 0.1 to 3 weight percent based on the weight of the phosphate ester polyol, or a phosphoric acid content of from 1.5 to 2.5 weight percent based on the weight of the phosphate ester polyol. In some embodiments, the phosphate ester-based polyol has a viscosity less than 40,000 cps at 25 C., or less than 30,000 cps at 25 C., as measured by the method of ASTM D2196. In some embodiments, the phosphate ester-based polyol has a hydroxyl number from 200 to 350 mg KOH/g, measured according to ASTM D4274. In some embodiments, the amount of the phosphate ester adhesion promoter in the isocyanate-reactive component is, by weight based on the weight of the isocyanate-reactive component, from 0.5 to 15 wt %, or from 1 to 10 wt %, or from 2 to 5 wt %. One example of a technique for preparing a suitable phosphate ester adhesion promoter is provided in the Examples of the Disclosure, below.

[0026] In some embodiments, the bio-based polyol is a castor oil or other naturally-derived oil. Commercially available examples of castor oil suitable for use according to this disclosure include urethane grade castor oil available from Campbell & Co. In some embodiments, the amount of the bio-based polyol in the isocyanate-reactive component is, by weight based on the weight of the isocyanate-reactive component, from 5 to 80 wt %, or from 20 to 50 wt %, or from 30 to 40 wt %.

[0027] In some embodiments, one or more additives can optionally be included in the adhesive compositions. Examples of suitable additives include, but are not limited to, tackifiers, plasticizers, rheology modifiers, adhesion promoters, antioxidants, fillers, colorants, surfactants, defoamers, wetting agents, leveling agents, solvents, and combinations of two or more thereof.

[0028] The isocyanate-reactive component can further comprise other constituents commonly known to those of ordinary skill in the art, e.g., additional polyols, isocyanates, etc.

[0029] In some embodiments, the mole ratio of NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 0.8:1.0 to 1.6:1.0, or from 1.0:1.0 to 1.5:1.0, or from 1.2:1.0 to 1.4:1.0. The mix ratio, by weight, for the isocyanate component and isocyanate-reactive component can be determined based upon the desired ratio of NCO groups to OH groups. In some embodiments, the mix ratio, by weight, of the isocyanate component to the isocyanate-reactive component in the final adhesive composition can be from 100:45 to 100:75, or from 100:50 to 100:70.

[0030] In some embodiments, the isocyanate component and isocyanate-reactive component can be made and sold in a package. In some embodiments, the isocyanate component and isocyanate-reactive component can each be made and sold individually.

[0031] Laminate Formation

[0032] A laminate comprising the disclosed adhesive compositions can be formed by mixing the isocyanate and isocyanate-reactive components of the adhesive composition and then applying the mixed adhesive composition to a film. As used herein, a film is any structure that is 0.5 mm or less in one dimension and is 1 cm or more in both of the other two dimensions. A polymer film is a film that is made of a polymer or mixture of polymers. The composition of a polymer film is, typically, 80 percent by weight or more by weight one or more polymers.

[0033] For instance, a layer of the mixed adhesive is applied to a surface of a first substrate. The surface of the first substrate comprising the mixed adhesive composition is brought into contact with a surface of the second substrate, and then the two substrates run through a device for applying external pressure to the first and second substrates, such as nip roller. Arrangements of such rollers in an application apparatus are commonly known in the art. The mixed adhesive composition is then cured or allowed to cure at any temperature from room temperature (i.e., approximately 25 C.) up to 50 C. or higher. In some embodiments, the coating weight of the applied adhesives to the film substrates is from 1.2 g/m.sup.2 to 3.5 g/m.sup.2, in some embodiments, from 1.6 g/m.sup.2 to 3.0 g/m.sup.2.

[0034] Suitable substrates in the laminate structure include films such as paper, woven and nonwoven fabric, metal foil, polymer films, and metal-coated polymer films. Some films optionally have a surface on which an image is printed with ink which may be in contact with the adhesive composition. The substrates are layered to form a laminate structure, with an adhesive composition according to this disclosure adhering one or more of the substrates together.

Examples of the Disclosure

[0035] The present disclosure will now be explained in further detail by describing examples illustrating the disclosed adhesive compositions and existing adhesive compositions (collectively, the Examples). However, the scope of the present disclosure is not, of course, limited to the Examples.

[0036] Raw Materials

[0037] Pertinent raw materials used in the following Examples are detailed in Table 1.

TABLE-US-00001 TABLE 1 Raw Materials Material Description Supplier MOR-FREE L75-191 Isocyanate-terminated polyurethane The Dow Chemical prepolymer Company MOR-FREE L75-164 Isocyanate-terminated polyurethane The Dow Chemical prepolymer Company MOR-FREE C-411 Polyester/polyether polyol blend The Dow Chemical Company CR-85 Polyol blend The Dow Chemical Company VORANOL CP-1055 Tri-functional polyether polyol The Dow Chemical Company VORANOL 220-260 Di-functional polyether polyol The Dow Chemical Company Trimethylolpropane Trimethylolpropane Sigma-Aldrich (TMP) Phosphate ester Phosphate ester-based polyol The Dow Chemical adhesion promoter Company Bio-based polyol Urethane-grade castor oil Campbell & Co. ISONATE 125M Pure diphenylmethane diisocyanate The Dow Chemical (MDI) mixture composed of Company approximately 98 percent 4,4- diphenylmethane diisocyanate and 2 percent 2,4-diphenylmethane diisocyanate VORANOL CP-450 Di-functional polyether polyol The Dow Chemical Company GF-19 High slip, low density polyethylene Berry Plastics film, thickness 1.5 mil Corp. GF-10 Low density polyethylene film, Berry Plastics thickness 1.0 mil Corp. PET (48LBT) Polyester film, poly(ethylene glycol- E. I. du Pont de terephthalate) Nemours and Company Nylon Bi-axially oriented nylon 6 film, Honeywell thickness 15 m International Inc. Met-PET Metallized polyester film, thickness FILMtech Inc. 25.4 m

[0038] Preparation of Phosphate Ester Adhesion Promoter

[0039] Add 55.1 grams of VORANOL CP-450 and 1.5 grams of polyphosphoric acid to a reactor under nitrogen purge at room temperature. Then set the reactor temperature to 100 C. and agitate the reactor contents for 1 hour. Bring the reactor temperature down to 50 C. and then introduce 18.4 grams of ISONATE 125M into the reactor. The reactor temperature increases to 80 C. due to the exothermic reaction. Control the reaction temperature at 78 C. for 2 hours. The resulting phosphate ester adhesion promoter has hydroxyl number of 293 mg KOH/g, measured according to ASTM D4274 and a viscosity of 18,000 cps at 25 C. as measured according to ASTM D2196.

[0040] Preparation of Isocyanate-Reactive Components

[0041] Pertinent ingredients for the isocyanate-reactive components of Examples 1 to 3 are detailed in Table 2. Using the isocyanate-reactive component of Example 3 as a typical example for sample preparation, about 600 grams of VORANOL 220-260, about 360 grams of bio-based polyol, about 20 grams of phosphate ester adhesion promoter, and about 20 grams of TMP are charged to a glass reactor. The reactor is heated to about 70 C. and the mixture is stirred for about 2 hours, maintain the temperature. The reactor contents are then cooled to about 60 C., and the sample is transferred and packaged for later use.

TABLE-US-00002 TABLE 2 Isocyanate-Reactive Component Compositions Example 1 Example 2 Example 3 Raw materials wt % wt % wt % VORANOL CP 1055 29 Bio-based polyol 30 36 36 Phosphate ester adhesion 5 3 2 promoter VORANOL 220-260 36 59 60 TMP 2 2 Total Weight 100 100 100

[0042] Adhesive Formulations

[0043] Detailed formulations of various adhesives are identified in Table 3.

TABLE-US-00003 TABLE 3 Adhesive Formulations Mixing Ratio (Isocyanate Isocyanate- Component/ Isocyanate Reactive Coreactant, Example ID Component Component parts by weight) Comparative MOR-FREE MOR-FREE 100:40 Example 1 L75-164 C-411 Comparative MOR-FREE CR-85 100:50 Example 2 L75-191 Example 4 MOR-FREE Example 1 100:66 L75-191 Example 5 MOR-FREE Example 2 100:54 L75-191 Example 6 MOR-FREE Example 3 100:54 L75-191

[0044] Laminate Structures

[0045] Laminate structures are prepared using a LABO-COMBI laminator with the nip temperature was set to 120 F. and line speed was set to 100 feet/min Coating weight is adjusted to be about 1 to 1.2 lbs/rm (1.6 to 1.9 g/m.sup.2). Around 100 feet of laminates are prepared for each formulation with some bond strips inserted to facilitate bond testing. The formed laminate structures are allowed to cure at room temperature for 1 week. Various structures are evaluated, including 48-LBT/GF-19, NYLON/GF-10, and 48LBT/Met-PET.

[0046] Test Methods and Performance Results

[0047] T-peel bond strength is measured on a 1 inch strip of laminate sample at a rate of 10 inch/minute on an Instron tensile tester with a 200 N loading cell. Three strips are tested for each laminate sample and high and mean bond strengths are recorded together with the failure mode. In the case of film tear and film stretch, the high value is reported. In other failure modes, the average T-peel bond strength is reported. Typical failure modes include: AF for adhesive failure (adhesive with primary), AT for adhesive transfer (adhesive with secondary), AS for adhesive split (cohesive failure of adhesive), FT for film tear (destruct bond), FS for film stretch (destruct bond), and MT for metal transfer.

[0048] Primary aromatic amines (PAA) decay is tested after samples are cured at 25 C., 50% RH for 2 days. A cured laminate structure is folded over to form a double layer such that the polyethylene film of one layer is in contact with the polyethylene film of the other layer. The edges are then trimmed with a paper cutter to obtain a folded piece about 6.5 inches7 inches. The edges are then heat sealed to form a pouch with an interior size of 5.5 inches5.6 inches. The pouches are then filled with 100 mL of 3% acetic acid. These pouches are extracted at 70 C. in the air circulation oven for a period of 2 hours. After quench cooling of the pouches in cold tap water, allow the test solution to equilibrate at room temperature, the 100 ml test solution is transferred into a beaker. The amount of primary aromatic amines extracted to 3% acetic acid solution is determined by utilizing a classical colorimetric method.

[0049] Boil-in-bag testing of the laminate structures is also performed. A cured laminate structure (about 9 inches11 inches) is folded over to form a double layer such that the polyethylene film of one layer is in contact with the polyethylene film of the other layer. The edges are then trimmed with a paper cutter to obtain a folded piece about 5 inches7 inches. The edges are then heat sealed to form a pouch with an interior size of 4 inches6 inches. The pouches are then filled 100 mL of 1/1/1 sauce (i.e., a blend of equal parts by weight of catsup, vinegar and vegetable oil) through the open edge. After filling, the pouch is sealed in a manner that minimizes the air entrapped inside of the pouch. The filled pouches are then carefully placed in boiling water and kept immersed in the water for 30 minutes. When completed, the extent of tunneling, delamination, and/or leakage is compared with marked pre-existing flaws. The bags are then emptied and at least three 1 inch strips are cut from the pouches and T-peel bond strength is measured as soon as possible thereafter.

[0050] The results from the various performance tests are summarized in Table 4.

TABLE-US-00004 TABLE 4 Performance Results PAA Bond strength (g/in) Adhesive Structure (ppb) 1 day 7 day Boil-in-bag Comparative 48LBT/Met-PET 135, AF 80, AF Example 1 48LBT/GF-19 2,057, FT/FS 2,098, FT 330, FT NYLON/GF-10 24.9 1,724, FT 2,229, FT 527, FT Comparative 48LBT/Met-PET 82, AF 70, AF Example 2 48LBT/GF-19 1,054, FT 1,439, FT 182, FT/AS NYLON/GF-10 0.825 1,587, FT 1,843, FT .sup.577, FT/AT Example 4 48LBT/Met-PET 301, AF 262, AF/FT 48LBT/GF-19 1,058, FT 948, FT 626, FT NYLON/GF-10 0.482 1,279, FT 1,830, FT 679, FS Example 5 48LBT/Met-PET 279, AF 258, AF 48LBT/GF-19 1,203, FT 974, FT .sup.308, FT/AT NYLON/GF-10 1.539 1,395, FT 1,761, FT .sup.453, AS Example 6 48LBT/Met-PET 247, AS 300, AT 48LBT/GF-19 498, FT 1,089, FT 410, FT NYLON/GF-10 2.274 1,656, FT 1,719, FT .sup.491, AS

[0051] In addition to the embodiments described above and those set forth in the Examples, many embodiments of specific combinations are within the scope of the disclosure, some of which are described below:

Embodiment 1

[0052] A two-component solventless adhesive composition, comprising:

[0053] an isocyanate component comprising an isocyanate-terminated prepolymer; and

[0054] an isocyanate-reactive component comprising: [0055] a polyether polyol; [0056] a phosphate ester adhesion promoter; and [0057] a bio-based polyol.

Embodiment 2

[0058] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the polyether polyol accounts for 10 to 90 percent of the total weight of the isocyanate-reactive component.

Embodiment 3

[0059] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the polyether polyol accounts for 40 to 80 percent of the total weight of the isocyanate-reactive component.

Embodiment 4

[0060] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the polyether polyol accounts for 55 to 70 percent of the total weight of the isocyanate-reactive component.

Embodiment 5

[0061] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the phosphate ester is made from a tri-functional propylene glycol, a polyphosphoric acid, and a polyisocyanate, the phosphate ester having a phosphoric acid content of less than 3 weight percent based on the weight of the phosphate ester.

Embodiment 6

[0062] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the phosphate ester adhesion promoter accounts for 0.5 to 15 percent of the total weight of the isocyanate-reactive component.

Embodiment 7

[0063] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the phosphate ester adhesion promoter accounts for 1 to 10 percent of the total weight of the isocyanate-reactive component.

Embodiment 8

[0064] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the phosphate ester adhesion promoter accounts for 2 to 5 percent of the total weight of the isocyanate-reactive component.

Embodiment 9

[0065] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the bio-based polyol accounts for 5 to 80 percent of the total weight of the isocyanate-reactive component.

Embodiment 10

[0066] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the bio-based polyol accounts for 20 to 50 percent of the total weight of the isocyanate-reactive component.

Embodiment 11

[0067] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the bio-based polyol accounts for 30 to 40 percent of the total weight of the isocyanate-reactive component.

Embodiment 12

[0068] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the bio-based polyol is castor oil.

Embodiment 13

[0069] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the mole ratio of the NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 0.8:1.0 to 1.6:1.0.

Embodiment 14

[0070] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the mole ratio of the NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 1.0:1.0 to 1.5:1.0.

Embodiment 15

[0071] The two-component solventless adhesive composition of any preceding or succeeding Embodiment, wherein the mole ratio of the NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 1.2:1.0 to 1.4:1.0.

Embodiment 16

[0072] A laminate structure comprising the two-component solventless adhesive composition of any preceding or succeeding Embodiment.

Embodiment 17

[0073] A method for forming a laminate structure, comprising: [0074] forming an adhesive composition by mixing an isocyanate adhesive component comprising an isocyanate-terminated prepolymer and an isocyanate-reactive adhesive component comprising a polyether polyol, a phosphate ester adhesion promoter, and a bio-based polyol; [0075] applying the adhesive composition to a surface of a first substrate; and [0076] bringing a surface of a second substrate into contact with the adhesive composition on the surface of the first substrate, thereby forming the laminate structure.

Embodiment 18

[0077] The method for forming a laminate structure of any preceding or succeeding Embodiment, wherein mixing the isocyanate adhesive component and the isocyanate-reactive adhesive component occurs at a mole ratio of the NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 0.8:1.0 to 1.6:1.0.

Embodiment 19

[0078] The method for forming a laminate structure of any preceding or succeeding Embodiment, wherein mixing the isocyanate adhesive component and the isocyanate-reactive adhesive component occurs at a mole ratio of the NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 1.0:1.0 to 1.5:1.0.

Embodiment 20

[0079] The method for forming a laminate structure of any preceding or succeeding Embodiment, wherein mixing the isocyanate adhesive component and the isocyanate-reactive adhesive component occurs at a mole ratio of the NCO groups present in the isocyanate component to OH groups present in the isocyanate-reactive component is from 1.2:1.0 to 1.4:1.0.

Embodiment 21

[0080] The method for forming a laminate structure of any preceding or succeeding Embodiment, wherein the first substrate and the second substrate are each independently selected from the group consisting of a wood material, a metallic material, a plastic material, a composite material, a paper material, a fabric material, and combinations of two or more thereof.