ELECTROCHEMICAL DEVICES, ELECTRONIC DEVICES

Abstract

An electrochemical device and electronic device, including a positive electrode plate and a negative electrode plate, wherein the positive electrode plate includes a positive electrode current collector and a positive electrode active material, and the negative electrode plate includes a negative electrode current collector and a group of step coatings disposed on surface of the negative electrode current collector close to the positive electrode plate, and a weight of the positive electrode active material per unit area on the positive electrode current collector is g.sub.a expressed in cm.sup.2, a gram capacity of the positive active material is C.sub.a expressed in mAh/g, a thickness of the step coating is L expressed in μm, and a theoretical volume gram capacity of sodium metal is X expressed in mAh/cm.sup.3, and L satisfies Formula (I) are described.

[00001]$\begin{array}{cc}L=\frac{C_a*g_a}{X}*10000*\left(1\pm 0\text{.1}\right).& \left(I\right)\end{array}$

Claims

1. An electrochemical device, comprising a positive electrode plate and a negative electrode plate, wherein the positive electrode plate comprises a positive electrode current collector and a positive electrode active material, and the negative electrode plate comprises a negative electrode current collector and a group of step coatings disposed on surface of the negative electrode current collector close to the positive electrode plate, and a weight of the positive electrode active material per unit area on the positive electrode current collector is g.sub.a expressed in g/cm.sup.2, a gram capacity of the positive active material is C.sub.a expressed in mAh/g, a thickness of the step coating is L expressed in μm, and a theoretical volume gram capacity of sodium metal is X expressed in mAh/cm.sup.3, and L satisfies Formula (I): $\begin{array}{cc}L=\frac{C_a*g_a}{X}*10000*\left(1\pm 0\text{.1}\right).& \left(I\right)\end{array}$

2. The electrochemical device according to claim 1, wherein a width of the step coating is w expressed in mm, and a width of the negative electrode current collector is W expressed in mm, where 1≤w≤0.05 W.

3. The electrochemical device according to claim 2, wherein the width W of the negative electrode current collector is 100 mm to 1000 mm, and the width w of the step coating satisfies: 1 mm≤w≤(from 5 mm to 50 mm).

4. The method according to claim 1, wherein the step coating comprises a binder comprising at least one of polyvinylidene fluoride, sodium carboxymethyl cellulose, styrene-butadiene rubber, sodium alginate, lithium polyacrylate, sodium polyacrylate, polytetrafluoroethylene, polyimide, and polyurethane.

5. The method according to claim 1, wherein the step coating comprises a binder and a ceramic material, wherein (1) the the binder and the ceramic material are in a mass ratio of the binder to the ceramic material being (from 1 to 8):(from 1 to 9); (2) the ceramic material includes at least one of Al.sub.2O.sub.3, γ-AlOOH, SiO.sub.2, SiC, Si.sub.3N.sub.4, AlN, BN, Al.sub.4C.sub.3; and/or (3) the binder comprises at least one of polyvinylidene fluoride, sodium carboxymethyl cellulose, styrene-butadiene rubber, sodium alginate, lithium/sodium polyacrylate, polytetrafluoroethylene, polyimide, and polyurethane.

6. The electrochemical device according to claim 1, wherein the negative electrode current collector comprises at least one of a metal foil current collector, a metal foam current collector, a metal mesh current collector, a carbon felt current collector, a carbon cloth current collector and a carbon paper current collector.

7. The method according to claim 1, wherein in negative electrode current collector comprises an aluminum-based current collector comprising: at least one of aluminum foil and aluminum alloy foil,

8. The method according to claim 7, wherein the aluminum-based collector current collector comprises a polymer base film, and aluminum foils and/or aluminum alloy foils formed on both sides of the polymer base film.

9. The method according to claim 8, wherein the polymer base film is selected from polyamide, polyethylene terephthalate, polyimide, polyethylene, polypropylene, polystyrene, polyvinyl chloride, acrylonitrile-butadiene-styrene copolymer, polybutylene terephthalate, polyparaphenylene terephthalamide, poly(ethylene-co-propylene), polyoxymethylene, epoxy resin, phenolic resin, polytetrafluoroethylene, polyvinylidene fluoride, silicone rubber, and polycarbonate.

10. The electrochemical device according to claim 7, wherein the aluminum-based current collector has a surface roughness of from 0.3 μm to 1.5 μm.

11. The electrochemical device according to claim 1, wherein a distance between two step coatings is greater than the width of the positive electrode active material, and the two step coatings are not directly opposite to the positive electrode active material.

12. The electrochemical device according to claim 1, wherein the positive active material comprises a sodium transition metal oxide, a polyanionic compound, and/or a Prussian blue compound.

13. The electrochemical device according to claim 1, wherein the step coating can be formed by transfer coating, extrusion coating and/or spray coating.

14. The electrochemical device according to claim 1, wherein the space formed by the negative electrode current collector and the step coating is used for accommodating the sodium source de-intercalated from the positive electrode plate.

15. The electrochemical device according to claim 14, wherein the space formed by the negative electrode current collector and the step coating is of a basin shape.

16. An electronic device, comprising the electrochemical device according to claim 1.

Description

DESCRIPTION OF THE DRAWING

[0022] The present application will be further described below in conjunction with the accompanying drawings and examples.

[0023] FIG. 1 is a schematic structural diagram of a battery of the present application;

[0024] FIG. 2 is a schematic structural diagram of a comparative example without a step coating described in the application;

[0025] FIG. 3 is a schematic structural diagram of a comparative example with volume expansion of sodium metal in the present application.

[0026] In the drawings: 100 represents a positive current collector; 200 represents a positive active material; 300 represents a separator; 400 represents a step coating; 500 represents a negative current collector.

DETAILED DESCRIPTION

[0027] In order to make the object, technical solution, and technical effects of the present application clearer, the present application will be further described in detail below in conjunction with embodiments. It should be understood that the embodiments described in the present description are merely used to illustrate the present application, but not intended to limit the present application.

[0028] The following descriptions are related to preferred implementations of the embodiments of the present application. It should be pointed out that without departing from the principles of the embodiments of the present application, several improvements and modifications can be made by those skilled in the art. These improvements and modifications should also be regarded as falling within the protection scope of the embodiments of the present application.

[0029] The terms used in the embodiments of the present application are only for the purpose of describing specific embodiments, and are not intended to limit the present application. As used in the embodiments of this application and the appended claims, the singular forms “a,” “the,” and “the” are intended to include the plural forms as well, unless the context clearly dictates otherwise.

[0030] It should be understood that the term “and/or” as used herein is only an association relationship to describe the associated objects, indicating that there can be three kinds of relationships. For example, “A and/or B” may represents three kinds of relationships, including A alone, B alone, and both A and B at the same time. In addition, the character “/” as used herein generally indicates that the related objects are in an “or” relationship.

[0031] As shown in FIG. 1, an embodiment of the present application provides an electrochemical device, including a positive electrode plate and a negative electrode plate, wherein the positive electrode plate includes a positive electrode current collector 100 and a positive electrode active material 200, and the negative electrode plate includes a negative electrode current collector 500 and a group of step coatings 400 disposed on surface of the negative electrode current collector 500 close to the positive electrode plate, and a weight of the positive electrode active material per unit area on the positive electrode current collector is g.sub.a expressed in g/cm.sup.2, a gram capacity of the positive active material is C.sub.a expressed in mAh/g, and a thickness of the step coating is L expressed in μm, and L satisfies Formula (I):

[00003]$\begin{array}{cc}L=\frac{C_a*g_a}{X}*10000*\left(1\pm 0\text{.1}\right).& \left(I\right)\end{array}$

[0032] In the above formula, the theoretical volumetric capacity of sodium metal is X mAh/cm.sup.3=1166 mAh/g*0.97 g/cm.sup.3, wherein 1166 mAh/g is the theoretical reversible gram capacity of sodium metal, 0.97 g/cm.sup.3 is the theoretical density of sodium metal. Through the constraint of the above Formula (I), the “basin-shaped” space constructed by the negative electrode current collector and the step coatings 400 on both ends can accommodate the volume of the sodium source de-intercalated from the positive electrode, avoiding the huge volume variation caused by sodium deposition. The coefficient (1±0.1) in formula (I) takes into account the fluctuation and effect of thickness tolerance of the actual step coating 400 during the preparation process. In the case that the thickness of the step coating 400 is less than 90% of the theoretically calculated coating thickness, the “basin-shaped” space cannot accommodate all the sodium sources de-intercalated from the positive electrode, thus the volume expansion of the negative electrode plate is still relatively large, and the battery cell has poor structural stability, resulting in poor cycle performance of the battery cell. However, in the case that the thickness of the step coating 400 is greater than 110% of the theoretically calculated coating thickness, too much “basin-shaped” space will cause the reduction of the volumetric energy density of the cell. 10000 means the conversion between cm and μm.

[0033] Owing to the small size of the step coating 400, a micrometer is used in the present application to measure the thickness of the step coating 400, and a soft ruler with a minimum quantile of 0.5 mm is used to measure the width and spacing of the step coating 400.

[0034] In the above technical solution, a width of the step coating 400 is w expressed in mm, and a width of the negative electrode current collector 500 is W expressed in mm, where 1≤w≤0.05 W. Generally, the width W of the negative electrode current collector 500 is from 100 mm to 1000 mm, then the width of the step coating 400 is from 1 mm≤w≤(from 5 mm to 50 mm). In the case that the width w of the step coating 400 is lower than 1 mm, the step coating of the electrode plate is too narrow and has insufficient strength, so that the step coating 400 of the electrode plate is easily damaged during preparation process of battery cell (winding/hot pressing, etc.), thereby losing the original design purpose. However, in the case that the width w of the step coating is higher than 50 mm, the space occupied by the step coating 400 in electrode plate is too large, which affects the volume energy density of the battery cell.

[0035] In the above technical solution, the step coating 400 can be a binder, or a combination of a binder and a ceramic material. The binder includes at least one of polyvinylidene fluoride, sodium carboxymethyl cellulose, styrene-butadiene rubber, sodium alginate, lithium polyacrylate, sodium polyacrylate, polytetrafluoroethylene, polyimide, and polyurethane. The ceramic material includes at least one of Al.sub.2O.sub.3, γ-AlOOH, SiO.sub.2, SiC, Si.sub.3N.sub.4, AlN, BN, Al.sub.4C.sub.3. The mass ratio of the binder and the ceramic material is (from 1 to 8):(from 1 to 9), specifically, the mass ratio of the binder and the ceramic material can be 1:9, 1:5, 2:1, 5:1, 7:1, 8:1, etc. Both the binder and ceramic material are electronic insulating materials, and do not chemically react with sodium, so as to ensure that the sodium source de-intercalated from the positive electrode is preferentially deposited on the surface of the negative electrode current collector 500, rather than on the surface of the step coating 400, thereby avoiding additional consumption of the sodium source caused by the chemical reaction of the step coating 400. The additional consumption results in the loss of the battery capacity and the first Coulomb efficiency. The binder has good heat resistance, does not react chemically with the sodium source, and the binder can bond well with the current collector without need of adding additional reagents. The ceramic material has the advantages such as high melting point, high hardness, high abrasion resistance, and oxidation resistance, and can be combined with the binder for use as the step coating 400 to provide stable performance meanwhile the deformation is not easy to occur.

[0036] In the above technical solution, the step coating 400 can be formed by any one of transfer coating, extrusion coating and spray coating. Specifically, the binder material is first dissolved in a solvent, which is water or N-methylpyrrolidone, and then placed in a high-speed mixer under stirring evenly at a high speed, and the obtained slurry is injected into a transfer coater, extrusion coater or spray coater for coating/spraying and drying, to finally obtain the step coating 400. If the ceramic material needs to be added, the binder material is dissolved in the solvent, and then added together with the ceramic material into a high-speed mixer under stirring evenly at a high speed. Preferably, the step coating 400 is prepared by a transfer coating method, which can better control the dimensions of the step coating 400.

[0037] In the above technical solution, the negative electrode current collector 500 used in the negative electrode plate may include at least one of a metal foil current collector, a metal foam current collector, a metal mesh current collector, a carbon felt current collector, a carbon cloth current collector and a carbon paper current collector. Sodium ions do not form alloys with aluminum. Based on the consideration of reducing cost and reducing weight, in the present application, an aluminum-based composite current collector is preferably used, which has better ductility and is conducive to maintaining the integrity of the electrode during the sodium deposition/de-intercalation process. The aluminum-based current collector includes any one of aluminum foil, aluminum alloy foil and aluminum-based composite current collector. The aluminum-based composite current collector includes a polymer base film as well as and/or aluminum alloy foils formed on both sides of the polymer base film. Specifically, the aluminum-based composite current collector has a “sandwich” structure, the polymer base film is located in the middle, and aluminum foils are arranged on both sides of the polymer base film, or aluminum alloy foils are arranged on both sides of the polymer base film, or aluminum foil is arranged on one side of the polymer base film and, aluminum alloy foil is arranged on the other side. The polymer base film is any one of polyimide, polyethylene terephthalate, polyimide, polyethylene, polypropylene, polystyrene, polyvinyl chloride, acrylonitrile-butadiene-styrene copolymer, polybutylene terephthalate, polyparaphenylene terephthalamide, poly(ethylene-co-propylene), polyoxymethylene, epoxy resin, phenolic resin, polytetrafluoroethylene, polyvinylidene fluoride, silicone rubber, and polycarbonate. In the above technical solution, the aluminum-based current collector 500 may have a surface roughness of from 0.3 μm to 1.5 μm, and specifically, the surface roughness of the aluminum-based current collector 500 may be 0.3 μm, 0.4 μm, 0.5 μm, 0.6 μm, 0.7 μm, 0.8 μm, 0.9 μm, 1.0 μm, 1.0 μm, 1.2 μm, 1.3 μm, 1.4 μm, 1.5 μm, etc., but not limited hereto. By controlling the surface roughness of the aluminum-based current collector 500 within the above ranges, it ensures good bonding force between the deposited sodium and the aluminum-based current collector 500. When the roughness is less than 0.3 μm, the surface of the aluminum-based current collector 500 is too smooth, the bonding force between the deposited sodium and the aluminum-based current collector 500 is insufficient, thereby resulting in high probability of peeling off and drop powder during use and the loss of contact with the conductive network and finally resulting in electrical insulation, which affects the capacity and cycle life of battery cell. When the roughness is greater than 1.5 μm, it is easy to cause uneven deposition of sodium at the local highly active tip sites, and it is more likely to form dendrites, resulting in the safety risk of the battery cell.

[0038] In the above technical solution, the distance between the two step coatings 400 is greater than the width of the positive electrode active material 200, and the two step coatings 400 are not directly opposite to the positive electrode active material 200, to ensure that during the first charging and stripping of sodium (de-sodiumization) process, sodium from the positive electrode active material 200 is deposited on the negative electrode current collector 500, rather than on the step coating 400, thereby avoiding the loss of the sodium source.

[0039] The electrochemical device of the present application may include any device in which an electrochemical reaction occurs, and specific examples thereof may include all kinds of primary batteries, secondary batteries, fuel cells, solar cells or capacitors. The electrochemical device is a sodium metal battery, and the battery may include at least one of soft pack, square aluminum case, square steel case, cylindrical aluminum case and cylindrical steel case batteries.

[0040] In some embodiments, the present application provides an electronic device comprising the aforementioned electrochemical device.

[0041] The use of the electrochemical device of the present application is not particularly limited, and the electrochemical device can be used in any electronic device known in the art. In some embodiments, the electrochemical device of the present application may be used in, but not limited to, notebook computers, pen input computers, mobile computers, e-book players, portable telephones, portable fax machines, portable copiers, portable printers, head-mounted stereos headphones, VCRs, LCD TVs, portable cleaners, portable CD players, mini discs, transceivers, electronic notepads, calculators, memory cards, portable recorders, radios, backup power, motors, automobiles, motorcycles, power-assisted bicycles, bicycles, lighting equipment, toys, game consoles, clocks, power tools, flashlights, cameras, large batteries for household use, energy storage and sodium ion capacitors, etc.

[0042] The positive electrode includes a positive electrode current collector 100 and a positive electrode active material 200, and specifically:

The positive active material 200 may include at least one of sodium transition metal oxides, polyanionic compounds, and Prussian blue compounds. In the sodium transition metal oxides, the transition metal may be one or more of Mn, Fe, Ni, Co, Cr, Cu, Ti, Zn, V, Zr and Ce. The sodium transition metal oxide is, for example, Na.sub.xMO.sub.2, where M is one or more of Ti, V, Mn, Co, Ni, Fe, Cr and Cu, wherein 0<x≤1. The polyanionic compound may include one or more of sodium vanadium trifluorophosphate Na.sub.3V.sub.2(PO.sub.4).sub.2F.sub.3, sodium vanadium fluorophosphate NaVPO.sub.4F, sodium vanadium phosphate Na.sub.3V.sub.2(PO.sub.4).sub.3, Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7, NaFePO.sub.4, Na.sub.3V.sub.2(PO.sub.4).sub.3. Prussian blue compounds are Na.sub.xM.sup.1M.sup.2(CN).sub.6, where M.sup.1 and M.sup.2 are one or more of Fe, Mn, Co, Ni, Cu, Zn, Cr, Ti, V, Zr, and Ce, where 0<x≤2.

[0043] A binder and/or a conductive agent may also be added in the positive active material 200. There is no limitation on the type of the binder and the conductive agent in the application, which can be selected according to actual needs. For example, the above-mentioned binder may be one or more of polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), polyacrylic acid (PAA), polyvinyl alcohol (PVA), and styrene-butadiene rubber (SBR), and the above-mentioned conductive agent may be one or more of graphite, superconducting carbon, acetylene black, carbon black, carbon nanotube, graphene and carbon nanofiber.

[0044] The material of the positive electrode current collector 100 is not limited, and would be determined by those skilled in the art according to actual needs, and a metal is preferably used, for example, a metal including but not limited to aluminum foil.

[0045] The positive electrode plate can be prepared according to the conventional methods in the art. Generally, the positive electrode active material 200 and the optional conductive agent and binder are dispersed in a solvent which is usually N-methylpyrrolidone (NMP) to form a uniform positive electrode slurry. The positive electrode slurry is applied on at least one surface of the positive electrode current collector 100, and after steps including drying and cold-pressing, the positive electrode plate is obtained.

[0046] Further, the electrochemical device further includes a separator 300, the separator 300 arranged between the positive electrode and the negative electrode to prevent short circuit. The material and shape of the separator 300 are not specially limited and would be determined by those skilled in the art according to actual needs.

[0047] In some embodiments, the separator 300 includes a substrate layer, and the substrate layer is a non-woven fabric, a membrane or a composite membrane with a porous structure. In some embodiments, the material of the substrate layer includes at least one of polyethylene, polypropylene, polyethylene terephthalate, and polyimide. In some embodiments, the material of the substrate layer includes polypropylene porous film, polyethylene porous film, polypropylene non-woven fabric, polyethylene non-woven fabric or polypropylene-polyethylene-polypropylene porous composite membrane.

[0048] In some embodiments, a surface treatment layer is provided on at least one surface of the substrate layer. In some embodiments, the surface treatment layer may be a polymer layer, an inorganic substance layer, or a layer formed of a mixed polymer and inorganic substance. In some embodiments, the polymer layer includes a polymer, and the material of the polymer includes at least one of polyamide, polyacrylonitrile, acrylate polymer, polyacrylic acid, polyacrylic salt, polyvinylpyrrolidone, polyvinyl ether, polyvinylidene fluoride, poly(vinylidene fluoride-hexafluoropropylene).

[0049] In some embodiments, the inorganic substance layer further comprises inorganic particles and a binder. In some embodiments, the inorganic particles include one or a combination of more of aluminum oxide, silicon oxide, magnesium oxide, titanium oxide, hafnium dioxide, tin oxide, ceria, nickel oxide, zinc oxide, calcium oxide, zirconium oxide, yttrium oxide, carbide silicon, boehmite, aluminum hydroxide, magnesium hydroxide, calcium hydroxide and barium sulfate.

[0050] In some embodiments, the binder includes one or a combination of more of polyvinylidene fluoride, copolymers of vinylidene fluoride-hexafluoropropylene, polyamide, polyacrylonitrile, polyacrylate, polyacrylic acid, polyacrylic salt, polyvinylpyrrolidone, polyvinyl ether, polymethyl methacrylate, polytetrafluoroethylene and polyhexafluoropropene.

[0051] Further, the electrochemical device further includes an electrolyte, and the electrolyte includes a sodium salt and an organic solvent. Specifically, the organic solvent in the electrolytic solution is not particularly limited, and the organic solvent may be an organic solvent commonly used in the electrolytic solution in the art. As an example, the organic solvent may be selected from at least one of ethylene carbonate, propylene carbonate, diethyl carbonate, dimethyl carbonate, ethyl methyl carbonate, propylene carbonate, methyl acetate, ethyl propionate, fluoroethylene carbonate, ethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, and methyl tert-butyl ether, and preferably ether solvents, to adjust deposition morphology of sodium ion, thereby inhibiting the massive growth of sodium dendrites. In the electrochemical device of the present application, the sodium salt in the electrolyte is not particularly limited, and the sodium salt may be a sodium salt commonly used in the art for the electrolyte. As an example, the sodium salt may be selected from at least one of sodium hexafluorophosphate, sodium bisfluorosulfonimide, sodium bistrifluoromethanesulfonimide, sodium trifluoromethanesulfonate, sodium tetrafluoroborate, sodium difluorophosphate, perchloric acid sodium and sodium chloride.

[0052] In the electrochemical device of the present application, in order to improve the performance of the electrolyte, suitable additives may also be added to the electrolyte.

[0053] In order to illustrate the technical effect of the step coating 400 in the present application, “anode-free” sodium batteries having step coatings 400 with different sizes were prepared in the present application, and compared with sodium metal anode-containing batteries and sodium ion batteries and “anode-free” sodium batteries which are free of step coating. The specific details of battery preparation are as follows:

Example 1

[0054] (1) Preparation of negative electrode: aluminum foil with a thickness of 12 μm was used as the negative electrode current collector, the roughness of the negative electrode current collector was 0.3 μm; polyvinylidene fluoride (PVdF) powder was dissolved in N-methylpyrrolidone (NMP), and after adding Al.sub.2O.sub.3, a high-speed mixer was used for stirring uniformly; the mass ratio of polyvinylidene fluoride (PVdF) and Al.sub.2O.sub.3 was 1:4; then a step coating 400 slurry was applied on both ends of the aluminum foil current collector using an extrusion coater and dried to obtain a negative electrode of sodium battery with the step coating 400. The step coating 400 had a thickness of 32 μm and a width of 3 mm, and the distance between the two step coatings 400 is 101 mm. The values of thickness and width of the step coating 400 and the dimensions of the two step coatings 400 were shown in Table 1 for details.

[0055] (2) Preparation of positive electrode: Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 as positive electrode active material (with gram specific capacity of 120 mAh/g), polyvinylidene fluoride (PVdF) as the binder, and conductive carbon black (Super-P) as the conductive agent in a ratio of 96%:2%:2% were mixed uniformly in N-methylpyrrolidone solvent to prepare positive electrode slurry; the positive electrode slurry was applied on the surface of the aluminum foil by using a extrusion coater at a weight of positive active material 200 per unit area being 30 mg/cm.sup.2 and the coating width of 100 mm, and dried; then the coated electrode plate was cold-pressed by using a cold press machine at the designed compaction density of 2.5 g/cm.sup.3 to prepare the final positive electrode plate.

[0056] (3) Preparation of electrolyte: 1 mol/L of NaPF.sub.6 dissolved in a mixed solvent of diethylene glycol dimethyl ether and tetraethylene glycol dimethyl ether in a volume ratio of 1:1 was used as the electrolyte.

[0057] (4) Assembling the battery: The negative electrode plate from step (1), the positive electrode plate from step (2), and the separator 300 were cut into corresponding sizes and wound into dry battery cell by a winding machine. After standard technological processes such as welding, packaging with aluminum-plastic film, liquid injection, formation, gas extraction, secondary packaging, and volume fixing, a 20 Ah soft-packed sodium metal battery was prepared. The volume of injected electrolyte was set at 3 g/Ah.

Example 2

[0058] Example 2 was different from Example 1 in that: the step coating 400 had a thickness of 25 μm and a width of 3 mm, and the distance between the two step coatings 400 was 101 mm.

Example 3

[0059] Example 3 was different from Example 1 in that: the step coating 400 had a thickness of 38 μm and a width of 3 mm, and the distance between the two step coatings 400 is 101 mm.

Example 4

[0060] Example 4 was different from Example 1 in that: the step coating 400 had a thickness of 32 μm and a width of 0.8 mm, and the distance between the two step coatings 400 was 101 mm.

Example 5

[0061] Example 5 was different from Example 1 in that: the step coating 400 had a thickness of 32 μm and a width of 8 mm, and the distance between the two step coatings 400 was 101 mm.

Example 6

[0062] Example 6 was different from Example 1 in that: the step coating 400 had a thickness of 32 μm and a width of 3 mm, and the distance between the two step coatings 400 was 98 mm.

Example 7

[0063] Example 7 was different from Example 1 in that: the roughness of the negative electrode current collector was 0.2 μm.

Example 8

[0064] Example 8 was different from Example 1 in that: the roughness of the negative electrode current collector was 1 μm.

Example 9

[0065] Example 9 was different from Example 1 in that: the roughness of the negative electrode current collector was 1.5 μm.

Example 10

[0066] Example 10 was different from Example 1 in that: the roughness of the negative electrode current collector was 2 μm.

Comparative Example 1

[0067] A 12 μm aluminum foil was directly used as the current collector without application of the step coating 400, and directly wound with the positive electrode and the separator 300 to prepare the final battery.

Comparative Example 2

[0068] Comparative Example 2 was different from Example 1 in that: hard carbon was used as the negative electrode material. Among them, the negative electrode plate was prepared with a mass ratio of hard carbon:CMC:SBR:Super-P of 96.5%:1%:1%:1.5%. The preparation method of the positive electrode plate was referred to for the negative electrode plate, with the mass per unit area of 9.6 mg/cm.sup.2 and the compaction density of cold pressing being 1.7 g/cm.sup.3.

Comparative Example 3

[0069] Comparative Example 3 was different from Example 1 in that: a layer of sodium metal with the thickness of 65 μm was compounded on the surface of the 12 μm aluminum foil current collector by cold-pressing; then the sodium metal negative electrode, the positive electrode, and the separator 300 were wound to prepare the final battery.

TABLE-US-00001 TABLE 1 List of parameters of positive and negative electrodes in battery cells of Examples and Comparative Examples positive electrode weight of gram positive width of negative electrode capacity of active positive distance types of positive material electrode roughness thickness width between positive electrode per unit active negative of current of step of step two electrode material, area, material, electrode current collector, coating, coating, steps, No. material mAh/g mg/cm.sup.2 mm material collector μm μm mm mm Example 1 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 0.3 32 3 101 Example 2 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 0.3 25 3 101 Example 3 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 0.3 38 3 101 Example 4 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 0.3 32 0.8 101 Example 5 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 0.3 32 8 101 Example 6 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 0.3 32 3 98 Example 7 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 0.2 32 3 101 Example 8 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 1 32 3 101 Example 9 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 1.5 32 3 101 Example 10 Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al 2 32 3 101 Comparative Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 \ 12 μm Al \ \ \ \ Example 1 Comparative Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 Hard carbon 12 μm Al \ \ \ \ Example 2 (400 mAh/g) Comparative Na.sub.4Fe.sub.3(PO.sub.4).sub.2P.sub.2O.sub.7 120 30 100 Na 12 μm Al \ \ \ \ Example 3

[0070] Performance Test of Battery

[0071] Examples 1 to 10 and Comparative Examples 1 to 3 were tested as follows:

[0072] (1) A battery tester was used to conduct charge and discharge tests on the battery cells to evaluate the electrochemical performance of the battery cells. The charge-discharge voltage was set to from 2.5 V to 3.65V, and the charge-discharge current was set to 2 A (0.1 C), and the corresponding capacity when the battery cell was discharged from 3.65V to 2.5V for the first time and the corresponding capacity after 200 cycles of charge-discharge cycles and the average voltage plateau were recorded.

[0073] (2) An electronic balance with an accuracy of one thousandth was used to measure the weight of the battery cell.

[0074] (3) A vernier caliper was used to measure the length, width and thickness of battery.

[0075] (4) The weight energy density, volume energy density, thickness expansion rate of fully charged battery cells and capacity retention rate after 200 cycles were calculated by the following formulas. The calculation results were shown in Table 2:

[00004]$\mathrm{weight}\mathrm{energy}\mathrm{density}=\frac{\mathrm{First}\mathrm{disharge}\mathrm{capacity}\mathrm{of}\mathrm{battery}\mathrm{cell}*\mathrm{average}\mathrm{voltage}\mathrm{platform}}{\mathrm{weight}\mathrm{of}\mathrm{battery}\mathrm{cell}}$$\mathrm{volume}\mathrm{energy}\mathrm{density}=\frac{\mathrm{First}\mathrm{disharge}\mathrm{capacity}\mathrm{of}\mathrm{battery}\mathrm{cell}*\mathrm{average}\mathrm{voltage}\mathrm{platform}}{\mathrm{length}*\mathrm{width}*\mathrm{thickness}\mathrm{of}\mathrm{battery}\mathrm{cell}}$$\mathrm{thickness}\mathrm{expansion}\mathrm{rate}\mathrm{of}\mathrm{fully}\mathrm{charged}\mathrm{battery}\mathrm{cell}=\frac{\mathrm{thic}\mathrm{kness}\mathrm{of}\mathrm{battery}\mathrm{cell}\mathrm{fully}\mathrm{charged}\mathrm{to}3.65V}{\mathrm{initial}\mathrm{thickness}\mathrm{of}\mathrm{battery}\mathrm{cell}}*100\%$$\mathrm{capacity}\mathrm{retention}\mathrm{rate}\mathrm{after}200\mathrm{cycles}=\frac{\mathrm{discharge}\mathrm{capacity}\mathrm{of}\mathrm{battery}\mathrm{cell}\mathrm{at}200\mathrm{th}\mathrm{cycle}}{\mathrm{first}\mathrm{discharge}\mathrm{capacity}\mathrm{of}\mathrm{battery}\mathrm{cell}}*100\%$

TABLE-US-00002 TABLE 2 List of parameters of properties of battery cells of Examples and Comparative Examples thickness weight energy volume energy expansion capacity density of density of rate of fully retention battery cell, battery cell, charged rate after No. Wh/kg Wh/L battery cell 200 cycles Example 1 182.3 389.1 14% 89% Example 2 182.5 389.1 19% 83% Example 3 169.2 372.4 15% 88% Example 4 181.8 399.5 22% 80% Example 5 153.6 339.2 17% 85% Example 6 173.2 381.1 27% 76% Example 7 182.4 389.2 18% 84% Example 8 182.3 389.1 13% 90% Example 9 182.2 389.0 15% 88% Example 10 182.3 289.1 20% 82% Comparative 190.3 405.7 36% 63% Example 1 Comparative 146.6 298.2 12% 95% Example 2 Comparative 172.7 380.5 33% 66% Example 3

[0076] It can be seen from the performance of battery cells of the above Examples and Comparative Examples in Table 2 that, although the conventional sodium-ion battery using the method of Comparative Example 2 had good cycle performance, both the weight energy density and volume energy density were low; When the sodium metal negative electrode in Comparative Example 3 was used to replace the hard carbon negative electrode, the energy density of the battery cells was improved, but the structure stability of electrode was significantly reduced due to the high activity of the sodium metal negative electrode and the huge volume expansion during the intercalation/de-intercalation process, resulting in significantly decreased cycle performance of the final battery cell. As shown in FIG. 2, when the sodium metal negative electrode was further removed to become a “anode-free” battery cell (Comparative Example 1), the energy density of the battery cell was further higher, but the battery structure after volume expansion was shown in FIG. 3, in which the volume expansion of sodium metal negative electrode resulted in expansion and deformation of the negative electrode plate, and the problem of poor structural stability caused by expansion and contraction was still unsolved. In the present application, by introducing the step coating 400 into the “anode-free” battery cell to reserve the space for the deposition and expansion of the negative electrode sodium, the results of structural stability of the battery cells were significantly improved in Examples 1 to 10, while the cycle performance of the battery cell was significantly improved and the comprehensive electrical performance was optimal when the energy density of the cell was only slightly reduced.

[0077] Further comparing the performance of battery cells with different step coatings 400 with sizes in negative electrode, it can be seen that when the thickness, width and distance of the step coatings 400 are within the ranges required by this application (Example 1), the weight energy density and volume energy density of the battery cells and the thickness expansion rate of the fully charged battery cells, and the cycle performance are all maintained at the optimal level. When the thickness of the step coating 400 is insufficient (Example 2) or the width is insufficient (Example 4), the space reserved for the step coating 400 is not enough to accommodate the volume of deposited sodium, and the step coating 400 has insufficient strength and is easily damaged during the preparation or operation of the battery cell, both of which lead to the decreased structural stability of the electrode plate, the deteriorated interface of the battery cell, the increased side reactions with the electrolyte, and the decreased cycle performance of the battery cell relative to the optimal level. When the thickness of the step coating 400 is too high (Example 3) or the width is too high (Example 5), the space reserved by the inert step coating 400 and the volume occupied are too large, leading to the significantly decreased volume energy density of the battery cell; and the excess space will easily lead to uneven wetting of the electrolyte, which is also detrimental to the long-term cycle performance of the battery cell. When the spacing of the step coating 400 is smaller than the width of the coating layer of the positive electrode active material 200 (Example 6), part of the sodium de-intercalated from the edge region of the positive electrode is directly deposited on the step coating 400 and easily loses electrical contact to form dead sodium, and the sodium is easy to accumulate and form the dendrites and have increased side reactions with the electrolyte, resulting in a decreased cycle performance of the battery cell and a risk of safety performance at the same time.

[0078] Further comparing the performance of the aluminum-based negative electrode current collectors with different roughness values, it can be seen that by using the aluminum-based current collector 500 having a roughness within the ranges required by the application (Example 1, Example 8 and Example 9), an improved bonding force between the deposited sodium and the aluminum-based current collector 500 can be ensured, while maintaining all of the weight energy density, volume energy density of the battery cell, thickness expansion rate, and cycle performance of full-charged battery cell at excellent levels. When the roughness of the aluminum-based current collector 500 is less than 0.3 μm (Example 7), the cycle life of the cell is reduced. When the roughness of the aluminum-based current collector 500 is greater than 1.5 μm (Example 10), dendrites are easily formed, reducing the safety of the battery cell.

[0079] Based on the above description, the sodium battery containing the step coating 400 in negative electrode in the present application has both high energy density and good cycle stability, significantly improves electrochemical performance of a sodium secondary battery.

[0080] The above are only preferred embodiments of the present application, and are not intended to limit the present application. Any modifications, equivalent replacements, improvements, etc. made within the spirit and principles of the present application shall be included in the protection scope of the present application.