METHOD OF MANUFACTURING A SUBSTRATE FOR A FLOOR PANEL

Abstract

Method for manufacturing a single- or multi-layered substrate (9), which is suitable for a floor panel (1), wherein, for forming a substrate layer (9A-9B-9C), thermoplastic material (23A-23B-23C) is strewn, for example, onto a transport device (25), and this strewn thermoplastic material is consolidated under the influence of pressure and/or heat, preferably in a press device (27), characterized in that the thermoplastic material (23A-23B-23C) to be strewn comprises micronized material.

Claims

1.-18. (canceled)

19. A method for manufacturing a single- or multi-layered substrate, which is suitable for a floor panel, wherein, for forming a substrate layer, thermoplastic material is strewn, for example, onto a transport device, and this strewn thermoplastic material is consolidated under the influence of pressure and/or heat, preferably in a press device, wherein the thermoplastic material to be strewn comprises micronized material.

20. The method according to claim 19, wherein the micronized material is obtained by comminuting granulate or rendering it finer.

21. The method according to claim 19, wherein the average particle size of the micronized material, expressed as the D50 value or the median of the distribution, is situated between 100 and 750 micrometer and preferably between 100 and 500 micrometer.

22. The method according to claim 19, wherein the micronized material comprises one or more of the following characteristics: the micronized material comprises PVC, preferably rigid PVC, the micronized material comprises filler, preferably in an amount situated between 20 and 70 percent by weight in respect to the total weight of the micronized material, or between 30 and 60 percent by weight; and the micronized material comprises a vinyl acetate-based copolymer.

23. The method according to claim 19, wherein the thickness of the substrate layer after consolidating is situated between 0.4 and 0.6 millimeters.

24. The method according to claim 19, wherein the thermoplastic material to be strewn is heated prior to being strewn or during said strewing.

25. The method according to claim 19, wherein the thermoplastic material to be strewn is strewn onto a glass fiber layer, or a glass fiber layer is provided on the strewn, however, still not yet consolidated thermoplastic material.

26. The method according to claim 25, wherein the glass fiber layer is impregnated with the strewn thermoplastic material or at least with a portion of this thermoplastic material, for example, with a part of the micronized material, preferably during the consolidation.

27. The method according to claim 25, wherein the weight of the glass fiber layer is less than 65 grams per square meter and preferably is maximum 50 grams per square meter.

28. The method according to claim 19, wherein the strewn thermoplastic material is foamed and to this aim the thermoplastic material to be strewn comprises the micronized material and a blowing agent.

29. The method according to claim 28, wherein the thermoplastic material to be strewn is a mixture of at least the micronized material and a dryblend material with the blowing agent.

30. The method according to claim 29, wherein the dryblend material shows one or more of the following characteristics: the dryblend material is pre-mixed with the blowing agent; the dryblend material comprises PVC, preferably rigid PVC; the dryblend material comprises PVC, preferably with a K (Fikentscher) value of maximum 60; the dryblend material comprises a copolymer, preferably a vinyl acetate-based copolymer, such as vinyl chloride-vinyl acetate, which preferably has a K (Fikentscher) value of maximum 60 or maximum 58; the dryblend material comprises E-PVC; and the dryblend material comprises filler, preferably in an amount of less than 20 percent by weight in respect to the total weight of the dryblend material, or less than 15 percent by weight or less than 10 percent by weight.

31. The method according to claim 29, wherein the weight percentage of the dryblend provided with the blowing agent in respect to the total weight of the blend is situated between 1% and 25% or between 5% and 15%.

32. The method according to claim 29, wherein the weight percentage of the micronized material in respect to the total weight of the blend is situated between 75% and 99% or between 85% and 95%.

33. The method according to claim 29, wherein the micronized material itself is free from blowing agent.

34. The method according to claim 28, wherein the strewn thermoplastic material is foamed while this strewn thermoplastic material is consolidated, for example, in the press device.

35. The method according to claim 19, wherein the press device is a double-belt press.

36. The method according to claim 19, wherein the aforementioned micronized material shows a particle size distribution showing the feature that (D50D10)/D50 is larger than 50%, wherein D50 is the median and D10 relates to the tenth percentile of the particle size distribution.

37. The method according to claim 20, wherein the average particle size of the micronized material, expressed as the D50 value or the median of the distribution, is situated between 100 and 750 micrometer and preferably between 100 and 500 micrometer.

38. The method according to claim 20, wherein the micronized material comprises one or more of the following characteristics: the micronized material comprises PVC, preferably rigid PVC, the micronized material comprises filler, preferably in an amount situated between 20 and 70 percent by weight in respect to the total weight of the micronized material, or between 30 and 60 percent by weight; and the micronized material comprises a vinyl acetate-based copolymer.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0050] With the intention of better showing the characteristics of the invention, herein below, as examples without any limitative character, some preferred embodiments are described, with reference to the accompanying drawings, wherein:

[0051] FIG. 1 in top plan view represents a floor panel which is obtained by means of a method according to the invention;

[0052] FIG. 2 represents a cross-section according to line II-II in FIG. 1;

[0053] FIGS. 3 and 4 represent how a plurality of the floor panels of FIG. 1 can be coupled;

[0054] FIG. 5 in an enlarged view represents what is indicated by frame F5 in FIG. 2;

[0055] FIG. 6 represents an alternative to FIG. 2; and

[0056] FIG. 7 represents some steps in the method by which the floor panel of FIG. 1 is manufactured.

DETAILED DESCRIPTION OF THE INVENTION

[0057] In FIG. 1 in top plan view a floor panel 1 is shown. It is a decorative floor panel 1 with a wood decor 2. The panel 1 is rectangular and oblong and thus has a pair of long sides 3-4 and a pair of short sides 5-6. The long sides 3-4 are provided with coupling parts 7-8 which allow effecting a mechanical locking between two of such panels 1. The structure thereof will be described later in respect to FIG. 2. The short sides 5-6, too, can be provided with such coupling parts.

[0058] From FIG. 2, the composition of the floor panel 1 becomes clear. The panel 1 comprises, from bottom to top, a multi-layered substrate 9, a decor carrier 10 with the decor 2, a transparent or translucent wear layer 11 and a transparent or translucent lacquer layer 12.

[0059] The substrate 9 consists of four substrate layers 9A-9B-9C-9D. Each of the substrate layers 9A-9B-9C-9D has a substantially or entirely homogeneous composition. The substrate layers 9A-9B-9C-9D all are composed of thermoplastic material. However, while the substrate layers 9A-9B-9C consist of rigid PVC, in the substrate layer 9D this is semi-rigid or flexible PVC. The composition of the thermoplastic material is described in greater detail with reference to FIG. 7. That the substrate 9 in part is made of rigid PVC implies various advantages. Due to its inherent rigidity, the rigid PVC forms a barrier against telegraphy. Due to the rigid character, the panel 1 as a whole also is easier to install, as it will bend less easily than, for example, flexible LVT (Luxury Vinyl Tile) panels. Strong coupling parts 7-8 can be milled from the rigid part of the substrate 9. These provide for a strong mechanical locking between mutually coupled panels 1. Moreover, the more flexible substrate layer 9D provides for an agreeable walking comfort. It also damps the sound occurring when the panels 1 are walked upon. The rigid substrate layers 9A-9B-9C all are unfoamed. Those are also called compact layers. As they are unfoamed, they offer a good resistance against telegraphy and indentation. The density of the layers 9A-9B-9C is situated between 1500 and 2000 kg per cubic meter. The more flexible substrate layer 9D also is unfoamed. The thicknesses of the substrate layers 9A-9B-9C-9D fulfill the following:

[0060] The thickness T1 of the substrate layer 9A is situated between 0.5 and 1.5 mm;

[0061] the thickness T2 of the substrate layer 9B is situated between 1.35 and 2.65 mm;

[0062] the thickness T3 of the substrate layer 9C is situated between 0.4 and 0.6 mm; and

[0063] the thickness T4 of the substrate layer 9D is situated between 0.4 and 0.9 mm.

[0064] The total thickness TS of the substrate 9 is situated between 2.65 and 5.65 mm.

[0065] In the substrate 9, two light-weight glass fiber fleeces 13A-13B are present. They each weigh less than 65 grams per square meter. The glass fleeces 13A-13B are situated offset from the center of the panel 1, the one 13A in the lower half and the other 13B in the upper half. Each of the glass fleeces 13A-13B is enclosed between rigid substrate layers. The lower glass fleece 13A is enclosed between the layers 9A and 9B, and the upper glass fleece 13B between the layers 9B and 9C. This offers a particularly stable sandwich structure having a reduced risk of warping.

[0066] The decor carrier 10 is a PVC film which is printed with the wood decor 2. The thickness thereof is approximately 0.1 mm. The wear layer 11 is a PVC film. The thickness T5 of the wear layer 11 is situated between 0.25 and 0.75 mm and here approximately 0.55 mm. The lacquer layer 12 is realized on the basis of a UV-curable PU lacquer. It is not excluded to provide more than one lacquer layer. This is described as such in the document BE 2016/5732, also by the present applicant, however, not yet published when filing the present application.

[0067] The thickness T of the entire panel 1 is situated between 3 and 6.5 mm and here approximately 4.5 mm.

[0068] The panel 1 is provided with a chamfer or bevel 14 along the upper edge of the long sides 3-4. The bevels 14 do not extend deeper than the wear layer 11. In a variant, the bevels 14 can extend up into the substrate 9. These deeper bevels preferably are decorated. This can be performed, for example, by providing a separate paint layer thereon.

[0069] The coupling parts 7-8 substantially are manufactured from the rigid substrate layers 9A-9B-9C. This provides for that they are strong and, as a result, provide a strong mechanical locking between mutually coupled panels 1. The coupling parts 7-8 consist of a tongue 15 and a groove 16. The groove 16 is bordered by an upper lip 17 and a longer lower lip 18. The cooperation between the upper side of the tongue 15 and the lower side of the upper lip 17 in the coupled condition effects the locking in the direction V. Moreover, locking elements 19-20 are present, which counteract the moving apart of the tongue 15 and the groove 16 in the direction H. The locking elements 19-20 are provided at the lower side of the tongue 15 and the upper side of the lower lip 18. The lower glass fleece 13A is situated in the lower lip 18 and extends uninterruptedly therein. This provides for a strongly made lip. This strength is advantageous, considering that this lip 18 is bent out during coupling and thus is subjected to a certain load. Even after coupling, the lip 18 still can be bent in order to supply a tensioning force which presses the coupled panels 1 towards each other. In this case, this is called pretension, such as known as such from document WO 97/47834.

[0070] The coupling parts 7-8 are of the angling type. This means that they can be joined into each other by means of a movement W, such as illustrated in FIG. 3. The locking elements 19-20 are brought one behind the other by means of an angling movement.

[0071] Moreover, they are also of the snap type. This means that the coupling parts 7-8 can be joined into each other by means of a movement S, as illustrated in FIG. 4. The locking elements 19-20 are brought behind each other by means of a translation movement substantially or entirely parallel to the plane of the panels 1. Herein, a snap effect occurs due to the elastic movement of the lower lip 18.

[0072] It is also noted that at the short sides 5-6, too, coupling parts can be provided. They can be of the same type of have the same shape as the coupling parts 7-8, however, this is not necessarily the case. They can be of the angling and/or snap type; however, they can also be of the push-lock type. Such coupling parts can be joined into each other by means of a translation movement substantially or entirely perpendicular to the plane of the floor panels. In this case, the panel 1 can also be coupled, in one and the same angling movement, at its long side as well as at its short side to adjacent panels 1. This is called a fold-down panel, such as known as such from document WO 01/75247.

[0073] FIG. 5 is an enlarged representation of what is indicated by frame F5 in FIG. 2. It clearly shows that in the upper surface of the panel 1 a relief 21 is present. This relief 21 is used for simulating a wood texture. It is formed by means of mechanical embossing. To this aim, a roller can be employed. The relief 21 consists of a plurality of indentations 22. The relief 21 may or may not be realized in register with the wood decor 2. The relief 21 does not reach deeper than the wear layer 11. In a variant, a deeper relief can be applied. To this aim, the substrate 9 can be deformed. Herein, the use of the more flexible substrate layer 9D is advantageous, as, due to the inherent flexibility, it can be indented easily, for example, by the roller.

[0074] In FIG. 6, an alternative substrate construction is shown. The substrate 9 consists of five substrate layers 9A-9B-9C-9D-9E. Each of these substrate layers 9A-9B-9C-9D-9E also has a substantially or entirely homogeneous composition. All of the substrate layers 9A-9B-9C-9D-9E are composed of thermoplastic material. Just like in FIG. 2, a number of these layers are made of rigid PVC and not foamed. Those are the substrate layers 9A and 9C. The substrate layer 9B also consists of rigid PVC, however, is foamed. The advantage thereof is that the entire panel 1 can be made thicker without being much heavier. Also, such layer has proven to be more stable under the influence of temperature variations than non-foamed layers. The substrate layer 9D then again consists of semi-rigid or flexible PVC. The substrate layer 9E consists of XPE foam and is glued to the substrate layer 9A. This one primarily provides for sound damping. In a variant, this layer 9D can be composed of another sound-damping material, such as cork or the like. The thicknesses of the substrate layers 9A-9B-9C-9D-9E fulfill the following:

[0075] the thickness T1 of the substrate layer 9A is situated between 0.5 and 1.5 mm and here in particular approximately 0.9 mm;

[0076] the thickness T2 of the substrate layer 9B is situated between 2.35 and 3.15 mm and here in particular approximately 2.8 mm;

[0077] the thickness T3 of the substrate layer 9C is situated between 0.4 and 0.6 mm and here in particular approximately 0.5 mm;

[0078] the thickness T4 of the substrate layer 9D is situated between 0.4 and 0.9 mm; and

[0079] the thickness T5 of the substrate layer 9E is situated between 1 and 2 mm.

[0080] The overall thickness TS of the substrate 9 is situated between 4.65 and 8.15 mm.

[0081] In the substrate 9, again two light-weight glass fleeces 13A-13B are present. They each weigh less than 65 grams per square meter. They enclose the foamed substrate layer 9B, and along their other side they are bordered by the substrate layers 9A and 9C, respectively. This again results in a very stable sandwich structure.

[0082] The decor carrier 10, the wear layer 11 and the lacquer layer 12 are similar or identical to those from FIG. 2.

[0083] The thickness T of the whole panel 1 is situated between 5 and 9 mm and here approximately 7 mm.

[0084] Bevels 14 are provided, too. In the upper surface of the panel 1, a relief is present, which, however, is not represented here.

[0085] The coupling parts 7-8 are realized similar to those from FIG. 2. They also are of the angling and snap type.

[0086] It is also noted that the panel and substrate construction shown in FIGS. 2 and 6 is known as such from documents BE 2016/5868 and BE 2016/5869, both by the same applicant, however, not yet published when filing the present application. Variants described therein can be applied here as well.

[0087] FIG. 7 shows how the substrate 9 from FIGS. 2 and 6 can be manufactured. For forming the substrate layer 9A, thermoplastic material 23A is strewn. This material 23A is strewn onto the transport conveyor 25 by means of the strewing unit 24A. The material 23A consists entirely of micronized material. This micronized material shows the following characteristics:

[0088] the micronized material comprises rigid PVC and maximum 10 phr plasticizer;

[0089] the micronized material comprises filler, such as chalk, talc and/or lime, with a weight percentage situated between 30% and 60% in respect to the total weight of the micronized material and here with a weight percentage of approximately 45%; and

[0090] the micronized material comprises between 20 and 40 phr vinyl chloride-vinyl acetate and here approximately 30 phr of this copolymer.

[0091] Micronizing has been performed offline. During micronization, granulate with the same characteristics as herein above has been ground. The grains of the granulate were disk-shaped. From this ground granulate, the micronized material was selected by sieving. The not-selected and thus coarser material was recirculated and again sent to the grinding process. The D50 value of the micronized material is situated between 100 and 750 micrometer and here approximately 300 micrometer.

[0092] The thermoplastic material 23A is pre-heated in the strewing unit 24A. This may be by thermally radiating this material 23A therein. A variant is possible when a rotating dosing roller is present in the strewing unit 23A. Then this dosing roller can be heated and the material 23A is heated while being transported via this roller.

[0093] The glass fleece 13A is provided on the strewn substrate layer 9A. This glass fleece 13A is wound off the roll 26A.

[0094] For forming the substrate layer 9B, thermoplastic material 23B is strewn. This material 23B is strewn by means of the strewing unit 24B onto the transport conveyor 25 and in particular on the glass fleece 13A. This material, too, is pre-heated in the strewing unit 24B. In the substrate layer 9B of FIG. 2, the material 23B shows the same characteristics as mentioned herein above for the material 23A. Thus, it consists entirely of micronized material which is produced in the above-mentioned manner. This is different for the substrate layer 9B of FIG. 6. Here, the material 23B is a mixture of micronized material and dryblend material. The mixture is prepared before it is introduced into the strewing unit 24B. A blowing agent for foaming the material 23B is present in the dryblend material. It is a chemical blowing agent, namely, azodicarbonamide. The blowing agent is pre-mixed into the dryblend material. The micronized material shows the same characteristics as mentioned herein above for the material 23A. It is also manufactured in the same manner by grinding granulate offline. The micronized material itself is free from blowing agent.

[0095] The dryblend material shows the following characteristics:

[0096] the dryblend material comprises rigid PVC and here approximately 12 phr plasticizer;

[0097] the PVC has a K (Fikentscher) value of maximum 60;

[0098] the PVC is S-PVC;

[0099] the dryblend material comprises vinyl chloride-vinyl acetate with a K (Fikentscher) value of maximum 58 and in an amount between 30 and 50 phr and here in an amount of approximately 40 phr; and

[0100] the dryblend material comprises filler, such as chalk, talc and/or lime, with a weight percentage in respect to the total weight of the dryblend material of less than 10% and here with a weight percentage of approximately 7% to 8%.

[0101] The mixture consists of approximately 90% of the micronized material and approximately 10% of the dryblend material provided with blowing agent.

[0102] On the strewn substrate layer 9B the glass fleece 1B is provided. This glass fleece 13B is wound off the roll 26B.

[0103] For forming the substrate layer 9C, thermoplastic material 23B is strewn. This material 23C is strewn by means of the strewing unit 24C onto the transport conveyor 25 and in particular on the glass fleece 13B. The material 23C shows the same characteristics as mentioned herein above for the material 23A. Thus, it consists entirely of micronized material which is produced in the above-mentioned manner. This material 23C, too, is pre-heated in the strewing unit 24C.

[0104] The consolidation of the substrate layers 9A-9B-9C takes place in the heated press device 2. This is a double-belt press with heating elements 28, an S-roller 29 and cooling elements 30. In this press device the glass fleeces 13A-13B are also impregnated with the thermoplastic material of the substrate layers 9A-9B-9C. This is performed particularly smooth as they are relatively light-weight, and due to the use of the micronized material. The foaming of the strewn material of the substrate layer 9B of FIG. 6 also takes place in this press device 27.

[0105] Once out of the press device 27, the substrate 9 can be processed further. The more flexible substrate layer 9D is provided on the substrate layer 9C. This is performed by means of the calendering device 31. The substrate layer 9D is provided as a liquid mass on the consolidated substrate layer 9C by means of at least two calendering rollers 32.

[0106] Thereafter, the decor carrier 10, provided with the decor 2, and the wear layer 11 can be provided on the substrate layer 9D. This can be, for example, by means of a thermal laminating process. Herein, the decor carrier 10 and the wear layer 11 can be provided as a continuous film. They may or may not be provided together.

[0107] Subsequently, the lacquer layer 12 is provided on the wear layer 11. This is preferably performed by means of a roller. The UV-curable PU-lacquer 12 can be provided prior to or after the mechanical embossing of the relief 21. If the lacquer 12 is provided beforehand, the curing preferably is performed thereafter. Herein, it is, however, not excluded that the lacquer 12 is already partially cured before embossing. The curing of the lacquer 12 is performed by means of UV lamps.

[0108] Subsequently, the continuous material web is subdivided into smaller pieces in order to form the panels 1. This can be by means of a sawing or cutting process.

[0109] The substrate layer 9E from FIG. 6 is glued to the substrate layer 9A. This gluing takes place, for example, after subdividing the material web, however, can also be performed before this. For this gluing preferably a waterproof glue is applied. The substrate layer E is extruded. In a variant, the layer 9E, too, can be strewn and be consolidated together with the other strewn layers 9A-9B-8C. To this aim, for example, an additional strewing unit can be provided upstream from the strewing unit 24A.

[0110] After subdividing, the coupling parts 7-8 can be milled from the substrate 9. To this aim preferably rotating milling tools are applied. This is known as such from document WO 97/47834.

[0111] The present invention is in no way limited to the herein above-described embodiments; on the contrary, such floor panels and substrates can be realized according to various variants without leaving the scope of the present invention.