HONEYCOMB-LIKE HOMO-TYPE HETEROJUNCTION CARBON NITRIDE COMPOSITE MATERIAL AND PREPARATION METHOD THEREOF, AND APPLICATION IN CATALYTIC TREATMENT OF WASTE GAS

Abstract

Disclosed are a honeycomb-like homo-type heterojunction carbon nitride composite material and a preparation method thereof, and an application of the honeycomb-like homo-type heterojunction carbon nitride composite material in catalytic treatment of waste gas. The preparation method includes the following steps: with two different carbon nitride precursors namely urea and thiourea as raw materials, weighing certain amounts of the urea and the thiourea, adding the urea and the thiourea into a crucible, adding a certain amount of ultrapure water, placing the crucible in a muffle furnace, and carrying out calcination molding. The honeycomb-like homo-type heterojunction carbon nitride prepared by the one-step method has good photocatalytic effect to catalytic degradation of NO; meanwhile, the honeycomb-like homo-type heterojunction carbon nitride composite material has the advantages of rich and easily-available production raw materials, good stability, reusability, etc., and has application prospects in the field of treatment of NO in the air.

Claims

1. A preparation method of a honeycomb-like homo-type heterojunction carbon nitride composite material, comprising the following steps: using urea and thiourea as precursors, in the presence of water, calcining the precursors to obtain the honeycomb-like homo-type heterojunction carbon nitride composite material.

2. The preparation method of a honeycomb-like homo-type heterojunction carbon nitride composite material according to claim 1, wherein first mixing urea, thiourea and water to react, then calcining to prepare the honeycomb-like homo-type heterojunction carbon nitride composite material; the calcination is carried out in air; the calcination includes first calcination and second calcination.

3. The preparation method of a honeycomb-like homo-type heterojunction carbon nitride composite material according to claim 2, wherein, the reaction is carried out at room temperature for 20 to 45 minutes; and in the first calcination, the heating rate is 10 C./min, the calcination time is 1 h, the calcination temperature is 400 C.; in the second calcination, the heating rate is 10 C./min, the calcination time is 1 h, and the calcination temperature is 450 C.

4. The preparation method of a honeycomb-like homo-type heterojunction carbon nitride composite material according to claim 1, wherein the mass ratio of urea and thiourea to water is 5: (6 to 7); the quality of thiourea is between 1% and 10% of the total mass of urea and thiourea.

5. A treatment method of exhaust gas, comprising the steps of: using urea and thiourea as precursors, in the presence of water, calcining the precursors to obtain the honeycomb-like homo-type heterojunction carbon nitride composite material; and then letting the exhaust gas pass through the honeycomb-like homo-type heterojunction carbon nitride composite material to complete the exhaust gas treatment.

6. The treatment method of exhaust gas according to claim 5, wherein first mixing urea, thiourea and water to react, then calcining to prepare the honeycomb-like homo-type heterojunction carbon nitride composite material; the calcination is carried out in air; the calcination includes first calcination and second calcination; the exhaust gas treatment is taken under light.

7. The treatment method of exhaust gas according to claim 6, wherein the reaction is carried out at room temperature for 20 to 45 minutes; and in the first calcination, the heating rate is 10 C./min, the calcination time is 1 h, the calcination temperature is 400 C.; in the second calcination, the heating rate is 10 C./min, the calcination time is 1 h, and the calcination temperature is 450 C., the light is 300 W xenon illumination.

8. The treatment method of exhaust gas according to claim 5, wherein the mass ratio of urea and thiourea to water is 5: (6 to 7); the quality of thiourea is between 1% and 10% of the total mass of urea and thiourea.

9. A honeycomb-like homo-type heterojunction carbon nitride composite material prepared by the preparation method of a honeycomb-like homo-type heterojunction carbon nitride composite material according to claim 1.

10. The application of the honeycomb-like homo-type heterojunction carbon nitride composite material according to claim 9 for catalytically treating exhaust gas.

11. The application of the honeycomb-like homo-type heterojunction carbon nitride composite material according to claim 9 for preparing exhaust gas treatment composite material.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0018] FIG. 1 is the SEM image of the honeycomb-like carbon nitride isotype heterojunction after calcination at 450 C.

[0019] FIG. 2 is the TEM images of the honeycomb-like carbon nitride isotype heterojunction after calcination at 450 C.

[0020] FIG. 3 shows the visible-light photocatalytic activities of the honeycomb-like carbon nitride isotype heterojunction for removal of NO in air.

[0021] FIG. 4 shows the cycling run in the photocatalytic reaction process.

DETAILED DESCRIPTION OF THE INVENTION

Implementation 1

[0022] Preparation of the honeycomb-like carbon nitride isotype heterojunction, the specific steps are as follows:

[0023] In a typical synthesis, the urea and thiourea (a total of 15 g) were mixed in 20 mL ultrapure water at room temperature and ultrasonicated for 30 min. The as-obtained mixture was then put in an alumina crucible with a cover and heated in a muffle furnace. The temperature was raised to 400 C. with a ramping rate of 10 C./min and was kept at this temperature for 1 h. After which, the temperature was further increased to 450 C. and maintained at this temperature for 1 h. To investigate the effect of thiourea mass ratios on the photoactivity of this isotype heterojunction, different weight percentage of thiourea in (urea+thiourea) were selected (0%, 1%, 2%, 5%, 10% and 100%) and discussed.

[0024] FIG. 1 showed the SEM images of the honeycomb-like carbon nitride isotype heterojunction after calcination at 450 C. It can be seen from the figure that some holes are irregularly scattered on the surface of the carbon nitride. FIG. 2 showed the TEM images of the honeycomb-like carbon nitride isotype heterojunction after calcination at 450 C. From the figure, it can be seen more clearly and intuitively that there are a large number of cellular voids distributed in the carbon nitride layers, with inconsistent pore sizes and irregular shapes.

Implementation 2

Photocatalytic Activity to NO

[0025] The volume of the cylindrical reactor made of glass was 1.6 L (1020 cm) and 50 mg of catalyst was placed in the center of it. The Xenon lamp was vertically placed outside the reactor above the reactor. NO gas was supplied by a compressed gas cylinder at a concentration of 100 ppm of NO (N.sub.2 balance). The initial concentration of NO was diluted to about 600 ppb via air stream provided by a compressed air cylinder. The two gas streams were premixed in a three-way valve and the flow rate of the mixed gas was controlled at 2.4 L min.sup.1. The desired humidity level of the air flow was controlled at 50% by passing the air stream through a humidification chamber. When the adsorption-desorption equilibrium among photocatalyst, gas and water vapor was achieved, the Xenon lamp was turned on. The concentration of NO was consequently measured every one minute by using a NO.sub.x analyzer (Thermo Environmental Instruments, Inc., 42i-TL).

[0026] FIG. 3 showed the visible-light photocatalytic activities of the honeycomb-like carbon nitride isotype heterojunction for removal of NO in air. It can be seen from the figure that about 65% of NO is removed catalytically within 10 minutes under light irradiation conditions in the composite photocatalyst of the honeycomb-like carbon nitride isotype heterojunction; after 30 minutes, the NO concentration keep steady. In this experiment, due to the formation of isotype heterojunction with urea and thiourea, as well as honeycomb morphology, the catalytic efficiency of photocatalysts for NO was substantially increased.

Implementation 3

Cyclic Experiment

[0027] After the end of the implementation 2, turn off the xenon lamp and wait for the concentration of gas NO to return to 600 ppb again and keep it stable. After the adsorption equilibrium is reached, turn on the xenon lamp and start timing. Record the data for 30 minutes. After that, the above operation was repeated and recorded four times to obtain the catalyst cycle data.

[0028] FIG. 4 showed the cycling run in the photocatalytic reaction process. In the experiment, it can be seen that during the above three repeated uses, the composite material has high stability and always maintains excellent photocatalytic performance. Under the NO concentration of 600 ppb, the final removal efficiency of NO is more than 65%. Therefore, the catalyst can be reused and has good stability.

[0029] In the invention, the honeycomb-like carbon nitride isotype heterojunction, a metal-free, conjugated, earth-abundant polymeric semiconductor, and it has high physicochemical stability, favorable electronic band structure and facile synthesis by thermal polymerization of abundant nitrogen-rich precursors. In particular, urea is a very inexpensive and abundant industrial reagent and is a good precursor.