REFLECTIVE FILM ASSEMBLED ON A COMPOSITE STRUCTURE

Abstract

A space vehicle including a reflective component on the side thereof for reflecting electromagnetic radiation, such as a mirror, the composite being formed by the steps of providing a composite support structure; providing a release liner including a metallic layer having a thickness between 1 and 5 microns on a surface thereof; situating the release liner against the surface of the composite support structure so that the metallic layer of the release liner is placed in direct, physical contact with the surface of the support structure; removing the release liner so that the metallic layer remains attached to the surface of the support structure; and mounting the support structure on a support on the exterior of the space vehicle.

Claims

1. A mirrored structure comprising: a composite support structure comprising a polymer matrix and fibers, and having a surface; a uniform metal layer over the surface; and a release layer covering the uniform metal layer, wherein the release layer has an adhesion to the uniform metal layer less than the adhesion of the uniform metal layer to the surface of the composite support structure such that the release layer can be peeled away and removed from the uniform metal layer to expose the uniform metal layer without disconnecting the uniform metal layer from the surface of the composite support structure.

2. The mirrored structure of claim 1 wherein the composite support structure comprises a plurality of laminated layers.

3. The mirrored structure of claim 1 wherein polymer matrix is a cyanate ester resin.

4. The mirrored structure of claim 1 wherein the composite support structure has a thickness between 1 mil and 20 mil.

5. The mirrored structure of claim 1 wherein the fibers are carbon fibers.

6. The mirrored structure of claim 1 wherein uniform metal layer comprises aluminum, silver, gold or a combination thereof.

7. The mirrored structure of claim 1 wherein uniform metal layer has a thickness between 1 micron and 5 microns.

8. The mirrored structure of claim 1 wherein the release liner comprise polyimide.

9. The mirrored structure of claim 1 wherein the release liner comprises 4,4-oxydiphenylene-promellitimide.

10. The mirrored structure of claim 1 wherein the release liner has a thickness from 25 microns to 100 microns.

11. The mirrored structure of claim 1 wherein the composite support structure comprises 6 laminated layers of uni-directional plies arranged in sequential direction layup to provide quasi-isotropic properties, wherein the release liner comprises polyimide, and wherein the wherein uniform metal layer comprises aluminum, silver, gold or a combination thereof and has a thickness between 1 micron and 5 microns.

12. The mirrored structure of claim 1 wherein the surface has a spherical shape.

13. The mirrored structure of claim 1 wherein the surface has a planar shape.

14. The mirrored structure of claim 1 wherein the surface has a parabolic shape.

15. A method for making a mirrored structure comprising: providing a composite support structure; placing a metallized release liner comprising a release liner and a metal layer against the composite support structure with the metal layer against a surface of the composite support structure to provide direct, physical contact of the metal layer to the surface so as to uniformly adhere the metal layer over the entire surface of the support structure; and peeling away and removing the release layer from the uniform metal layer to expose the uniform metal so that the metallic layer remains attached to the surface of the composite support structure.

16. A spacecraft comprising: a support mounted on the spacecraft; and a mirrored structure attached to the support and comprising a composite structure with a uniform metal layer with a thickness between 1 micron and 5 microns on a surface of the composite structure and functioning as a reflective element of electromagnetic radiation on the surface of the spacecraft, wherein the composite structure comprises a plurality of laminated layers with fibers in a polymer matrix.

18. The spacecraft of claim 16 wherein the spacecraft is a Cubesat with one or more cubic structures attached to each other.

19. The spacecraft of claim 16 further comprising solar cell assemblies attached to the support.

20. The spacecraft of claim 16 wherein the support comprises a polyimide layer.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0028] To complete the description and in order to provide for a better understanding of the disclosure, a set of drawings is provided. Said drawings form an integral part of the description and illustrate embodiments of the disclosure, which should not be interpreted as restricting the scope of the disclosure, but just as examples of how the disclosure can be carried out. The drawings comprise the following figures:

[0029] FIG. 1 is a cross-sectional view of a release liner according to the present disclosure;

[0030] FIG. 2A is a cross-sectional view of a composite structure in one embodiment of the present disclosure;

[0031] FIG. 2B is a cross-sectional view of a composite structure in a second embodiment of the present disclosure;

[0032] FIG. 3A is a cross-sectional view of the composite structure of FIG. 2B after the next process step of mounting the release liner;

[0033] FIG. 3B is a cross-sectional view of the composite structure of FIG. 3A after the next step process step of peeling the supporting polyimide film away from the bottom metallic layer bonded to the surface of the composite structure;

[0034] FIG. 4 is a cross-sectional view of the composite structure of FIG. 3B after the next process step after the polyimide film has been detached away from the bottom metallic layer which is bonded to the surface of the composite structure; and

[0035] FIG. 5 is a perspective view of a space vehicle incorporating a mirror constructed according to the process of the present disclosure.

DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

[0036] Details of the present invention will now be described including exemplary aspects and embodiments thereof. Referring to the drawings and the following description, like reference numbers are used to identify like or functionally similar elements, and are intended to illustrate maj or features of exemplary embodiments in a highly simplified diagrammatic manner. Moreover, the drawings are not intended to depict every feature of the actual embodiment nor the relative dimensions of the depicted elements, and are not drawn to scale.

[0037] FIG. 1 is a cross-sectional view of a release liner 100 according to the present disclosure. The bottom surface 102 of the liner 100 is composed of a metallic layer that is from one to five microns in thickness. The bulk of the release liner 100 is composed of a polyimide layer or film, in a thickness from 25 microns (or one mil) to several hundred microns. Such materials are commercially available, off the shelf items used for a variety of industrial application available from a variety of suppliers. The metallic layer may be composed of aluminum, silver, gold, or other metals, or combinations and layers thereof, depending upon the application.

[0038] FIG. 2A is a cross-sectional view of a composite structure 200 in one embodiment of the present disclosure. The structure 200 includes concave region 103 with corners 104. This figure illustrates the difficulty in achieving uniform thickness of a metallic layer using a prior art PVD technique. Because of the shape of the exposed surfaces of the structure, the coatings will not cover the concave regions 103 and corners 104 adequately.

[0039] FIG. 2B is a cross-sectional view of a composite structure 300 in a second embodiment of the present disclosure, including a concave parabolic surface 301. In some embodiments, the structure may be a closed cell foam substrate. The thickness of the substrate may range from 1 inch to several inches or more.

[0040] FIG. 3A is a cross-sectional view of the composite structure 300 of FIG. 2B after the next process step of mounting the release liner 100 directly over the surface 301.

[0041] FIG. 3B is a cross-sectional view of the composite structure 300 of FIG. 3A after the next process step of peeling the film 101 away from the bottom metallic layer 102 so that the layer 102 remains bonded to the surface 301.

[0042] FIG. 4 is a cross-sectional view of the composite structure 300 of FIG. 3B after the next process step with the film 101 entirely peeled away from the bottom metallic layer 102, and the layer 102 remains bonded to the surface 301.

[0043] One application of the composite structure 300 is for use in a space vehicle, such as a CubeSat illustrated in FIG. 5. CubeSats are a type of miniaturized space vehicles or satellites. A typical CubeSat is a 10 cm10 cm10 cm cube, thus having a volume of one liter. CubeSats can be attached to one another in strings or blocks to provide functionalities and capabilities that would not otherwise be practically available in a single CubeSat. For example, one CubeSat can be used as a power source to supply power necessary for other attached CubeSats to perform their functions such as imaging, sensing, or communications.

[0044] The composite structures described herein can be particularly advantageous for attaching to a CubeSat. For example, the composite structures can be attached directly to the surface of the CubeSat without a need for a frame (e.g., an aluminum frame). Further, the solar cell modules can include a light weight flexible support (e.g., a polyimide support) or a non-flexible support (egg shell support).

[0045] A miniature satellite or CubeSat 350 can include the composite structure 354 according to the present disclosure. CubeSats 350 are a type of miniaturized satellites or nanosatellite. A typical CubeSat is a 10 cm10 cm10 cm cube, thus having a volume of one liter. CubeSats can be attached to one another in strings or blocks to provide functionalities and capabilities that would not otherwise be practically available in a single CubeSat. FIG. 5 for example illustrates three individual CubeSats 351, 352, 353 forming a 3-unit CubeSat 350.

[0046] Solar cell assemblies 310, 311, 312, 320, 321, 322 can be mounted on the sides of a CubeSat. For example, the solar cells or solar cell assemblies can be attached directly to the surface of a support 301, 302 which are then mounted via attachment clip 330 directly on the CubeSat component 331 without a need for a frame (e.g., an aluminum or honeycomb frame). Further, the solar cell supports 301, 302 can be composed of a light weight flexible support (e.g., a KAPTON or other polyimide support) or a rigid and non-flexible support. The polyimide sheets as either a continuous layer or a patterned layer designed for a particular application. The base or backplane of the unit is typically a space qualified or qualifiable material (e.g., KAPTON, polyester, polyimide, Aramid, Pyralux) that is lightweight, flexible, and reliable in space applications. Kapton is a poly (4,4-oxydiphenylene-pyromellitimide) material.

[0047] A mirror constructed of the composite structure 300 may be used for directing electromagnetic energy (e.g., microwave, or light) into or away from an object.

[0048] The composite structure 300 serves to provide the shape or contour of the mirror. The contour can be spherical, aspherical, cylindrical, cylindrical aspheric, planar, or any other shape. The composite structure is of a material which provides thermomechanical stability, low mass, and stiffness. It can be made from metals, composite sandwich structures, plastic or in the preferred embodiment Graphite Fiber Reinforced Composite (GFRC). In one embodiment, the composite structure 300 is a six layer GFRC laminate composite in which the plies or layers are uni-directional plies, arranges in a sequential direction layup to provide quasi-isotropic properties and a balanced laminate, such as a (0/60/-60/-60/60/0) with each ply comprising a 0.04 mm layer of graphite fibers, such as Mitsubishi's K13D2U in a cyanate resin ester matrix, such as Tencatels RS3-C control flow cyanate resin. In one embodiment, the six ply GFRC substrate is cured on a shaped forming mandrel machined with high precision to provide the contour of the mirror. Other fibers can also be used. These include M55J graphite fiber from Toray Industries, Inc., or fiberglass, or NOMEX (a registered trademark of E. I. du Pont de Nemours and Company Corporation) fibers, depending on the amount of stiffness and thermal stability required. Fiberglass or other common fibers may also be used for low cost terrestrial applications. Other fiber reinforcement forms, such as woven fabric or felt mats, and other resin matrices, including epoxies, polyimides or bismaleamide resins, or other thermoplastic resins as well as thermosetting plastic resins may also be used.

[0049] It is to be noted that the terms front, back, top, bottom, over, on, under, and the like in the description and in the claims, if any, are used for descriptive purposes and not necessarily for describing permanent relative positions. It is understood that the terms so used are interchangeable under appropriate circumstances such that the embodiments of the disclosure described herein are, for example, capable of operation in other orientations than those illustrated or otherwise described herein.

[0050] The present disclosure can be embodied in various ways. The above described orders of the steps for the methods are only intended to be illustrative, and the steps of the methods of the present disclosure are not limited to the above specifically described orders unless otherwise specifically stated. Note that the embodiments of the present disclosure can be freely combined with each other without departing from the spirit and scope of the disclosure.

[0051] Although some specific embodiments of the present disclosure have been demonstrated in detail with examples, it should be understood by a person skilled in the art that the above examples are only intended to be illustrative but not to limit the scope of the present disclosure. It should be understood that the above embodiments can be modified without departing from the scope and spirit of the present disclosure which are to be defined by the attached claims.