OUTDOOR COLOR CHANGEABLE FILM WITH SELF RECOVERING FUNCTIONS

Abstract

Disclosed is an outdoor color changeable film with self recovering functions which has self recovering functions such as water repellent, anti-fouling, and antibacterial functions, can block ultraviolet rays, and can be used in various fields due to a long-lasting film property and an insecticidal effect. The outdoor color changeable film is a color changeable film which is constituted by a hard coating pearl layer capable of self recovering, a transparent base film with the hard coating pearl layer formed on the surface, an adhesive coating layer formed on the bottom of the transparent base film, and a release film detachably laminated below the adhesive coating layer and is constituted by mixing pearl particles with a hard coating agent forming the hard coating pearl layer.

Claims

1. An outdoor color changeable film with self recovering functions, the color changeable film comprising: a hard coating pearl layer (10) capable of self recovering, a transparent base film (20) with the hard coating pearl layer (10) formed on the surface, an adhesive coating layer (30) formed on the bottom of the transparent base film (20), and a release film (40) detachably laminated below the adhesive coating layer (30), wherein the hard coating pearl layer (10) is constituted by mixing pearl particles with a hard coating agent, a color base film (50) in which a color adhesive layer (50c) is laminated on a surface facing the hard coating layer (10) is further laminated between the transparent base film (20) and the adhesive coating layer (30), the transparent base film (20) is any one of polyethylene terephthalate (PET), polyimide (PI), and polycarbonate (PC) which have low elasticity and hardness, the hard coating agent forming the hard coating pearl layer (10) has the viscosity of 40 to 45 cps and the self-recovering coating agent: the pearl particles: the curing agent are mixed at a weight ratio of 90 to 100:0.5 to 2:35 to 40, the self-recovering coating agent uses a mixture of 5 to 30 parts by weight of a trimethylene oxide-reactive polyurethane prepolymer with respect to 100 parts by weight of a coating agent-based chitosan-reactive polyester prepolymer, and the pearl particles are plate-shaped particles having a reflective angle larger than that of spherical particles and a particle size of 1 to 100 m so as to enhance a glare effect.

Description

DESCRIPTION OF DRAWINGS

[0034] FIG. 1 illustrates a laminated structure of an example of an outdoor color changeable film with self recovering functions according to the present invention.

[0035] FIG. 2 illustrates a laminated structure of another example of an outdoor color changeable film with self recovering functions according to the present invention.

MODES OF THE INVENTION

[0036] The present invention may have various modifications and various exemplary embodiments and specific exemplary embodiments will be described in detail in the detailed description. However, this does not limit the present invention to specific exemplary embodiments, and it should be understood that the present invention covers all the modifications, equivalents and replacements included within the idea and technical scope of the present invention.

[0037] In the description of each drawing, like reference numerals are used for like constitute elements. In describing the present invention, when it is determined that the detailed description of the publicly known art related to the present invention may obscure the gist of the present invention, the detailed description thereof will be omitted.

[0038] According to the present invention, it is possible to simplify a manufacturing process of a self-recovering color changeable film and reduce manufacturing cost without performing a separate process in order to exhibit a pearl effect by forming a hard coating layer by mixing pearl particles with the hard coating layer requiring lamination.

[0039] An outdoor color changeable film with self recovering functions of the present invention is a color changeable film which is constituted by a hard coating pearl layer 10 capable of self recovering, a transparent base film 20 with the hard coating pearl layer 10 formed on the surface, an adhesive coating layer 30 formed on the bottom of the transparent base film 20, and a release film 40 detachably laminated below the adhesive coating layer 30 and is constituted by mixing pearl particles with a hard coating agent forming the hard coating pearl layer 10.

[0040] The outdoor color changeable film with self recovering functions of the present invention is installed on a flat surface such as glass of a vehicle or a building as described above, and it is preferred that the transparent base film 20 has low elasticity and hardness so as to be easily adhered on the flat surface.

[0041] Accordingly, the transparent base film 20 used any one of polyethylene terephthalate (PET), polyimide (PI), and polycarbonate (PC) which have low elasticity and hardness.

[0042] Various hard coating agents for forming the hard coating pearl layer 10 may be used, but it is preferred that the viscosity is 40 to 45 cps so that the mixed pearl particles may be evenly distributed.

[0043] Further, when the viscosity of the hard coating agent is low, a liquid flow phenomenon occurs when the hard coating agent is coated on the transparent base film 20 and the coating surface may become uneven, and thus, it is preferred that the viscosity of the hard coating agent is adjusted to the viscosity in the viscosity range. In addition, if the viscosity is too high, a mash pattern may be formed due to a characteristic of micro gravure in a process of coating the micro gravure.

[0044] The hard coating agent may be made of various compositions, but preferably, made of a self-recovering coating agent, pearl particles, and a curing agent, and it is preferred that the content of self-recovering coating agent: pearl particles: curing agent is a weight ratio of 90 to 100:0.5 to 2:35 to 40.

[0045] The self-recovering coating agent uses a mixture of 5 to 30 parts by weight of a trimethylene oxide-reactive polyurethane prepolymer with respect to 100 parts by weight of a coating agent-based chitosan-reactive polyester prepolymer.

[0046] The pearl particles may have various shapes. That is, the pearl particles may have either spherical particles or plate-shaped particles. However, in the case of the spherical particles, a reflective angle is small and the glare is reduced, and thus it is preferable to use the plate-shaped particles.

[0047] The pearl particles may be plate-shaped synthetic pearls or natural pearls, and 0.5 to 2 parts by weight of the hard coating agent is preferably used as described above. When the content of the pearl particles is small, a color changeable effect deteriorates, and when the content is large, the visibility, which is a basic function of the window film, may deteriorate, and thus it is preferred that the pearl particles are mixed in an amount in the above range.

[0048] The particle size of the pearl particles is preferably 1 to 100 m. When the particle size is 1 m or less, the color changeable effect deteriorates, and when the particle size is 100 m or more, the pearl particles are misrecognized as a foreign substance in the coating process or the visibility of the glass deteriorates in the case of being installed on the glass.

[0049] The adhesive coating layer 30 has a function of blocking ultraviolet rays and to this end, the adhesive coating agent is made of an acrylic adhesive, a UV stabilizer, a UV absorber, a mixed solvent of metal ethyl ketone and toluene, and a mixing ratio thereof is a weight ratio of 10:0.1:2:12, and a metal chelate and isocyanate may be added as the curing agent.

[0050] The amount of the curing agent is preferably 1 to 30 parts by weight with respect to the total weight of the adhesive coating agent.

[0051] Further, in the outdoor color changeable film with self recovering functions according to the present invention, a color base film 50 laminated with a color adhesive layer 50c may be further laminated between the transparent base film 20 and the adhesive coating layer 30 so as to implement more various colors.

[0052] The color adhesive layer 50c is laminated on a surface facing the hard coating layer 10 and may be formed of an infrared blocking agent and an adhesive mixed with a pigment or a dye.

[0053] The color adhesive layer 50c is made of an adhesive formed by mixing a pigment or a dye with a substrate formed by acryl and epoxy, a urethane adhesive and an acrylic pressure-sensitive adhesive, and the amount of the pigment or the dye is preferably 0.5 to 2 parts by weight with respect to the total weight of the adhesive. When the pigment or the dye is excessively mixed, the visibility of the glass deteriorates and when the content of pigment or the dye is small, the saturation is lowered.

[0054] An example of the adhesive configuring the color adhesive layer is formed of 23% of a solid by mixing an acrylic pressure-sensitive adhesive, a metal chelate curing agent, an antimony tin oxide infrared blocking agent, a mixed solvent of methyl ethyl ketone and toluene at a weight ratio of 10:0.3:6:8.

[0055] Hereinafter, a method for manufacturing the outdoor color changeable film with self recovering functions according to the present invention configured above will be described.

[0056] The method for manufacturing the outdoor color changeable film with self recovering functions according to the present invention includes a hard coating step of coating a hard coating agent mixed with pearl particles on the upper surface of a transparent base film with a thickness of 12 to 15 m by using a micro gravure coater; a hard-coating agent curing step of thermally curing the transparent base film coated with the hard coating agent in an atmosphere of 125 to 140 C.; and a coating step of coating an adhesive coating agent on the lower surface of the transparent base film with a thickness of 5 to 6 m using the micro gravure coater.

[0057] In the manufacturing method, after the adhesive coating step, it is preferred to perform a process of further laminating a release protective film in order to protect the adhesive coating layer.

[0058] An ultraviolet blocking agent or a ultraviolet absorber may be further mixed with the adhesive coating agent used in the adhesive coating step.

[0059] Further, in order to express more various colors, a color adhesive layer may be further formed and the step of forming the color adhesive layer is performed before the hard coating step.

[0060] That is, the infrared blocking agent and the adhesive mixed with the pigment or dye are coated on the upper surface of the transparent base film with a thickness of 5 to 6 m, a bonding step of bonding a polyethylene terephthalate film (PET) with a thickness of 23 to 100 m on the coating surface of the adhesive is further performed, and then the hard coating layer is formed on the surface of the boned PET film.

[0061] The ultraviolet blocking agent or the ultraviolet absorber mixed with the adhesive coating agent may block ultraviolet rays in a wavelength band of 400 nm and effectively block the incidence of pests.

Experimental Example 1

[0062] The degree of haze according to the content of pearl particles was measured using a haze meter.

TABLE-US-00001 Content of pearl 0.5 1.0 1.5 2.0 particles Haze 0.2 0.5 1.0 1.3 Visibility Good Good Slight poor Poor

[0063] As can be seen in Table above, the content of pearl particles is preferably 0.5 to 1.0 according to the degree of haze.

Experimental Example 2

[0064] The degree of haze according to the size of pearl particles was measured using a haze meter.

TABLE-US-00002 Size of pearl 0.2 to 1 1 to 45 45 to 70 100 m particles m m m or more Visibility Deterioration Good Good Recognized as of visibility foreign substance Haze 4.2 1.5 2.1 2.2

[0065] As can be seen from Table above, when the particle size of the pearl particles is 0.2 to 1 m, the haze due to the diffuse reflection of the pearl particles is increased and the visibility of the film is deteriorated visually. Accordingly, it is preferred to use color changeable pearl particles having a particle size of 1 to 45 m while visibility is sufficiently secured, and it is also possible to use pearl particles having a particle size of 45 to 70 m while the visibility is secured.

[0066] In the case of 100 m or more, the particles are largely shown and recognized as the foreign substance, but the haze is good, but it is inappropriate for window films.

EXPLANATION OF REFERENCE NUMERALS AND SYMBOLS

[0067] 10: Hard coating pearl layer [0068] 20: Transparent base film [0069] 30: Adhesive coating layer [0070] 40: Release film [0071] 50: Color base film [0072] 50c: Color adhesive layer