METHOD AND DEVICE FOR PROCESSING OF FILTER MATERIAL, PRODUCT OBTAINED THEREOF

Abstract

Filter material, mainly in form of industrial remnants from the production of the filter fillings, is processed without the intake of the heat in such a way that it is cut in the disintegrator (4) at the presence of the air, where the material is during retention time repeatedly led to the contact with the rotating blades and bunches emerge in the disintegrator (4) through aeration. The flat carrier (3) is thus at least partially disintegrated to the original fibers (1); the released fibers (1) intertwine into bunches and the active carbon (2) is released from the original bond with the flat carrier (3). The swirl (vortex) created inside the disintegrator (4) carries the dust particles of the active carbon (2) and they adhere to the surface of the fibers (1). Part of the released active carbon (2) isafter the separationcarried away from the emergin bunches, which in the lower part of the disintegrator (4) run through the sieve out of the disintegrator (4). The resulting product is advantageously applicable as heat and noise isolation in all fields of technology, for example construction. The separated active carbon (2) in form of granules is also a resulting product of processing.

Claims

1. A method for processing a filter material with an active carbon, where the filter material includes at least partially permeable flat carrier (3), whereby the active carbon (2) in form of granules is applied on the flat carrier (3); the flat carrier (3) includes mutually connected fibers (1) from a thermoplastic polymer; whereby the filter material as a waste is processed mechanically without an intake of a heat, the filter material is processed in a rotational disintegrator (4) at a presence of an air, whereby during a retention period the material is repeatedly brought into contact with rotating elements (8) and bunches emerge in the disintegrator (4) by means of an aeration in such a way that the flat carrier (3) is at least partially disintegrated to the original fibers (1), the method comprising the steps of: mutually interwining the released fibers (1), separating the active carbon (2) from the flat carrier (3), crumbling to smaller particles a part of the released active carbon (2) by hitting the elements (8), and adhering the particles adhere to a surface of the fibers (1); in a lower part of the disintegrator (4) the bunches of fibers pass out through openings in a cover of the disintegrator (4); part of the released active carbon (2) is led away from the emerging bunches after the separation wherein a specific volume weight bunches of the fibers decreases below 1,4 p/cm.sup.3, preferably below 0.3 g/cm.sup.3, especially preferably below 0.1 g/cm.sup.3.

2. The method of the processing of the filter material with the active carbon according to the claim 1, wherein the fibers (1) are selected from a group of material consisting of polyolefins, polypropylene, and polyethylene.

3. (canceled)

4. (canceled)

5. The method of the processing of the filter material with the active carbon according to claim 1, wherein a rotation of the elements (8) in the disintegrator (4) creates an air swirl which carries dust particles of the active carbon (2) and distributes them on the surface of the fibers (1).

6. The method of the processing of the filter material with the active carbon according to claim 1, wherein a circumferential speed of rotating blades ranges from 20 to 300 m.s.sup.?1.

7. (canceled)

8. The method of the processing of the filter material with the active carbon according to claim 1, wherein before an entry of the material to the disintegrator (4) the material is planarly divided to pieces whose dimensions of less than 10 cm.

9. The method of the processing of the filter material with the active carbon according to claim 8, wherein the material is planarly divided in an independent shredder (5) which is placed before the disintegrator (4); an output from the shredder (5) leads directly to the input of the disintegrator (4).

10. The method of the processing of the filter material with the active carbon according to claim 9, wherein the material is disintegrated on its edges during the planar division.

11. The method of the processing of the filter material with the active carbon according to claim 8, wherein the material entering the disintegrator (4) is planarly divided to the pieces already during a separation of a semi-finished product for a production of a filter filling; preferably the pieces are held together in a single grouping by means of connecting strips which are later disconnected in the disintegrator (4).

12. The method of the processing of the filter material with the active carbon according to claim 1, wherein the bunches of the fibers coming out from the disintegrator (4) pass through a sieve, whereby the active carbon (2) in form of the granules falls down through the sieve.

13. The method of the processing of the filter material with the active carbon according to claim 1, wherein the bunches of fibers coming out from the disintegrator (4): pass to a separator (6) which separates the active carbon (2) from the bunches of fibers; or pass on a sloped surface of a rotational sieve, whereby a change of the slope and/or a number of rotations changes the retention period and therefore it changes an amount of the active carbon (2) in a resulting product.

14. (canceled)

15. The method of the processing of the filter material with the active carbon according to claim 1, wherein the active carbon (2) in the form of the granules is separated in the disintegrator (4) and/or the separator (6), collected in a vessel for a further use; preferably the active carbon (2) remains in the resulting product in the amount up to 0.01 g/cm.sup.3 of a volume of the resulting product in an uncompressed state.

16. The method of the processing of the filter material with the active carbon according to claim 1 wherein an adhesive which has held the active carbon (2) on the flat carrier (3) is separated during the separation of the active carbon (2) from the flat carrier (3) in the disintegrator; preferably the adhesive is simultaneously aggregated into clusters.

17. The method of the processing of the filter material with the active carbon according to claim 16, wherein the adhesive is separated in the cyclone separator (6) during the separation of the active carbon (2) from the bunches of fibers.

18. The method of the processing of the filter material with the active carbon according to claim 1, wherein an additive is added to the bunches of fibers after the separation of the active carbon (2); preferably a flame retardant is added.

19. A device for a processing of a filter material with an active carbon, where the device comprising: a disintegrator (4) with a rotating elements (8) which are rotationally placed on a rotor, whereby the disintegrator (4) has in its upper part an opening for an insertion of the processed filter material and in its lower part the disintegrator (4) has an outlet opening the disintegrator (4) has in its upper part a zone with a tightened, narrowed cross-section located between the rotor and a surface with protrusions (7) in a chamber of the disintegrator (4) it has a broadened zone between rotor blades and an inner cylindrical surface of a body of the disintegrator, in the narrowed zone of the chamber of the disintegrator (4) there is the a support surface which is oriented opposite to the rotating elements (8); the support surface has the protrusions (7) heading inside the disintegrator (4); in the lower part of the disintegrator (4) a cover of the chamber has openings for falling out of bunches of the disintegrated material, and a gap between the protrusions (7) and the rotating elements (8) is at least 3 mm, preferably at least 5 mm.

20. The device for the processing of the filter material with the active carbon according to the claim 19, wherein an axis of rotation of the rotor with the rotating elements (8) in the disintegrator (4) is horizontal.

21. (canceled)

22. The device for the processing of the filter material with the active carbon according to claim 19, wherein the device further includes a shredder (5) which is placed before the disintegrator (4), whereby the shredder (5) function is to separate the filter material to pieces with dimensions smaller than 10 cm.

23. The device for the processing of the filter material with the active carbon according claim 19, wherein the device further includes a separator (6) for a separation of the active carbon (2) in form of granules from the bunches of fibers, whereby the separator (6) is placed after the disintegrator (4).

24. A fiber product having a lenght of fibers of less than 10 cm, the fibers are made of a polyolefin group, the fiber product comprising: a specific volume weight less than 1.4 g/cm.sup.3, preferably the fibers (1) are mutually intertwined to form bunches of fibers, the fibers (1) are covered by a dust from an active carbon (2), and the fibers (1) are recycled from a filter material with the active carbon (2).

25. The product according to the claim 24, wherein the fibers (1) are from polypropylene and/or polyethylene.

26. The product according to the claim 24, wherein the granules of the active carbon (2) are stuck between the fibers (1) and total amount of the granules of the active carbon (2) is up to 0.01 g/cm.sup.3 of the volume of the resulting product in the uncompressed state.

27. The product according to claim 24 wherein the fiber product further contains an additive such as flame retardant.

28. The product according to claim 24 wherein the fiber product is a heat insulator, an acoustic insulator, or a filter filling for gas separators.

29. (canceled)

30. (canceled)

Description

BRIEF DESCRIPTION OF DRAWINGS

[0044] The invention is further disclosed by the drawings 1 to 7. The elements and devices are depicted schematically, the ratio of their sizes is for illustration purposes only and cannot be interpreted as limiting the scope of protection. The depiction of the particular group of fibers as well as the spatial arrangement of the individual machines in the system is for illustration purposes, too.

[0045] FIGS. 1 and 2 depict the filter material according to the state of the art which is being processed.

[0046] FIG. 1 depicts the two-layer carrier with the active carbon between the layers; FIG. 2 is an example of the shaped semi-finished product for the production of the filter filling;

[0047] FIG. 3 depicts the device for processing of the filter material in the most basic system which has only the disintegrator. The dotted lines denote the inscribed circle within the chamber of the disintegrator;

[0048] FIG. 4 is a view of the device which involves the preliminary planar divider and disintegrator. The arrows denote the movement of the material during processing;

[0049] FIG. 5 depicts the device which includes the preliminary planar divider, disintegrator and the rotational sieve. The arrows denote the movement of the material during processing;

[0050] FIG. 6 is a microscopic view of the bunch with the polypropylene fibers, where the granules of the active carbon are captured between the fibers; and

[0051] FIG. 7 depicts gradual distribution of the blades in the planar divider.

EXAMPLES OF REALIZATION

Example 1

[0052] In this example according to FIGS. 1, 2, 3, 5 to 7 the filter material which remains from the production of the cabin air filters is being processed. The semi-finished product for the filter filling is cut from the strip which is rolled from the pack. The filter material has two layers of the flat carrier 3, whereby the active carbon 2 is distributed among them in form of granules with the surface weight 350 g/m.sup.2. The weight of a single layer of the flat carrier 3 is 60 g/m.sup.2.

[0053] The flat carrier 3 is formed by the polypropylene non-woven system of the fibers 1 with air gaps between them. In this example the active carbon 2 is produced from the biological basis, for example from coconut. The active carbon 2 in this example is held on the flat carrier 3 by means of the harmless adhesive, which also holds both layers of the flat carrier 3 together; in other cases the active carbon 2 can be held between the layers of the flat carrier 3, whereby the layers are stuck together by the heat. After the cutting of the desired shape of the semi-finished product for the filter filling, the cut-outs and strips of various sizes remain from the original strip of the filter material. These remnants are thrown to the planar divider 5, where during a single passage smaller pieces are produced; these fragments' dimensions do not surpass 6 to 10 cm. This leads to flat division; the edges of the produced pieces can have frayed edges, which signals their partial disintegration on the edgeshowever, this disintegration on the edges is still marginal and insignificant.

[0054] The intermediate product from the planar divider 5 is together with the small amount of the released active carbon 2 transferred to the mouth of the disintegrator 4. The intermediate product is captured by the rotating elements 8 of the disintegrator 4, which have high circumferential speed. The elements 8 with high kinetic energy hit the pieces of the flat carrier 3; the hits cause disintegration in the place where the element 8 hits. The disintegrator 4 has a tightened, narrowed zone with the support surface in its upper part which captures the pieces so that they do not start moving concurrently with the rotation of the rotor of the disintegrator 4. The pieces of the material are thrown to protrusions 7 which lead inside the chamber, whereby the protrusions 7 do not enter into direct contact with the rotating elements 8.

[0055] The pieces with the varying degree of disintegration head downward to the sieve in the lower part of the disintegrator 4, whereby they are carried upward to the further contact with the rotating elements 8 in the tightened zone of the disintegrator 4. The movement of the rotor of the disintegrator 4 and the movement of the elements 8 produces strong air swirl (vortex) which halps to carry the pieces from the lower part of the zone of the disintegrator 4; the swirl mainly distributes the dust of the active carbon 2 to the surface of the fibers 1. The air swirl also causes aeration of the resulting bunches. Part of the released active carbon 2 in form of the granules falls through the sieve in the lower part of the disintegrator 4 and this active carbon 2 continues to the separator 6.

[0056] The bunches in the lower zone of the disintegrator 4 have a structure of the intertwined fibers 1, whereby the active carbon 2 in form of granules is randomly captured between them. In this example the rotations of the disintegrator 4 are set to achieve the circumferential speed 59 m.s.sup.?1; the period of retention of the material in the disintegrator 4 is on the order of the tens of seconds. The resulting bunches coming out through the sieve in the lower part of the disintegrator 4 have a specific volume weight 0.011 g/cm.sup.3 in the unpressed (expanded) state.

[0057] The material from the disintegrator 4 is transferred to the rotational separator 6 where the bunches roll and move slowly on the sloped inner surface of the cylindrical separator 6. The granules of active carbon 2 are released from the bunches. The active carbon 2 in form of the dust particles which adhere to the surface of the fibers 1 is no longer released during the movement in the sieve in the separator 6.

[0058] Active carbon 2 in form of granules is gathered below the separator and collected in the vessel together with the active carbon 2 separated already in the disintegration phase in the disintegrator 4.

[0059] The resulting product in this example can be used as heat or noise isolation in the building or house. The active carbon 2 contained in the isolation captures various smells and dangerous substances; it clears the air which runs through the vapor permeable layers of the building envelope. Thanks to the active carbon 2 the isolation is antibacterial, with zero spread and growth of molds and fungus as well as with effective capturing of the harmful substances an smells from the air.

Example 2

[0060] In this example the cutting plan of the semi-finished product is supplied by the fact that the remnants at the same time are divided to smaller pieces. These pieces are connected with tight strips; usually each piece will have at least three connecting strips. The remnants of the filter material with this structure are thrown to the disintegrator 4, where the disconnection of the connecting strips and freeing of the pieces happens at the first contact with the rotating elements 8. The disintegration and aeration subsequently takes place in the disintegrator 4, as described in the previous example. Setting of the rotation speed of the rotor in the disintegrator, as well as retention time in the disintegrator 4, differ compared to previous example. In this example the speed of the rotating elements 8 is approximately 70 m.s.sup.?1.

[0061] The resulting product has specific volume weight 0.008 g/cm.sup.3.

Example 3

[0062] The resulting product is used as a filling for the separator of the gasoline fumes in the motor vehicle. For this purpose the bunches do not run through the separator 6 in order to ensure high share of the active carbon 2 in form of granules, which have absorption function in the application.

Example 4

[0063] Bunches are sprayed by aerosol with flame retardants after they leave the separator 6. At the construction site, the bunches are pressed through the hose to the gaps in building construction by means of a fan; they function as heat and noise isolation.

Example 5

[0064] Planar divider 5 in this example has simplified construction with one line of the moving segments only. In this example, the sieve below the cylinder of the planar divider 5 is used, too, which determines the desire size output.

INDUSTRIAL APPLICABILITY

[0065] Industrial applicability is obvious. According to this invention it is possible to repeatedly produce and use industrial, non-polluted remnants of the filter material which contains active carbon, whereby the original physical and chemical features of the original material are advantageously used without degradation.

LIST OF RELATED SYMBOLS

[0066] 1fiber

[0067] 2active carbon

[0068] 3flat carrier

[0069] 4disintegrator

[0070] 5planar divider

[0071] 6separator

[0072] 7protrusions

[0073] 8element