GREEN TEA MEMORY FOAM AND ITS METHOD OF FABRICATING

Abstract

A kind of green tea memory foam and its fabricating method comprises the following components at the weight ratio of 4045 percent of polyether polyol A, 2535 percent of polyether polyol B, 2030 percent of toluene diisocyanate, 13 percent of green tea powder, 0.52 percent of water, 0.010.1 percent of silicone oil, 0.010.03 percent of ammonia, 0.010.03 percent of stannous octoate, and 0.0050.015 percent of mill base. The present invention belongs to the technical field of memory foam, particularly the memory foam with a fragrance of green tea which can effectively remove the unpleasant chemical smell with a natural smell of green tea to further improve the quality of sleep.

Claims

1. A kind of green tea memory foam comprising the components at the weight ratio of 4045 percent of polyether polyol A, 2535 percent of polyether polyol B, 2030 percent of toluene diisocyanate, 13 percent of green tea powder, 0.52 percent of water, 0.010.1 percent of silicone oil, 0.010.03 percent of ammonia, 0.010.03 percent of stannous octoate, and 0.0050.015 percent of mill base.

2. The green tea memory foam of claim 1, further comprising the following components at the weight ratio of 43 percent of polyether polyol A, 29.08 percent of polyether polyol B, 24.5 percent of toluene diisocyanate, 2.2 percent of green tea powder, 1.1 percent of water, 0.06 percent of silicone oil, 0.025 percent of ammonia, 0.025 percent of stannous octoate, and 0.01 percent of mill base.

3. The green tea memory foam of claim 1, wherein the hydroxyl value of the said polyether polyol A is 3260 mgKOH/g.

4. The green tea memory foam of claim 1, wherein the hydroxyl value of the said polyether polyol B is 295315 mgKOH/g.

5. A fabricating method for green tea memory foam comprising the procedures as below: 1) Taking every component according to the weight ratio; 2) Mixing uniformly the polyether polyol A, polyether polyol B, green tea powder and mill base according to the ratio for standby application; 3) Adding the water, silicone oil, ammonia and stannous octoate according to the ratio into the mixture of procedure 2) then mixing uniformly for standby application; 4) Adding the toluene diisocynate according to the ratio into the mixture of procedure 3) then mixing uniformly and quickly for 46 seconds to get a new mixture; 5) Pouring the mixture of procedure 4) into a mold for foaming to foam into an intermediate green tea memory foam then taking it out from the mold after 1020 minitues, and then airing it for 2030 hours to get the green tea memory foam.

Description

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0015] The technical solutions of the embodiments will be described clearly and completely. Obviously, the embodiments are just a part not all of the implementations. Based on the implementations of the present invention, the other implementations obtained by those skilled in the art without creative work will all fall within the scope of the invention.

[0016] Embodiment 1, a kind of green tea memory foam comprises the following components at the weight ratio of 43 percent of polyether polyol A, 29.08 percent of polyether polyol B, 24.5 percent of toluene diisocyanate, 2.2 percent of green tea powder, 1.1 percent of water, 0.06 percent of silicone oil, 0.025 percent of ammonia, 0.025 percent of stannous octoate, and 0.01 percent of mill base.

[0017] A fabricating method for the green tea memory foam comprises the following procedures: [0018] 1) Taking every component according to the weight ratio; [0019] 2) Mixing uniformly the polyether polyol A, polyether polyol B green tea powder and mill base according to the ratio for standby application; [0020] 3) Adding the water, silicone oil, ammonia and stannous octoate according to the ratio into the mixture of procedure 2) then mixing uniformly for standby application; [0021] 4) Adding the toluene diisocynate according to the ratio into the mixture of procedure 3) then mixing uniformly and quickly for 46 seconds to get a new mixture; [0022] 5) Pouring the mixture of procedure 4) into a mold for foaming to foam into an intermediate green tea memory foam then taking it out from the mold after 1020 minitues, and then airing it for 2030 hours to get the green tea memory foam.

[0023] Embodiment 2, a kind of green tea memory foam comprises the following components at the weight ratio of 41 percent of polyether polyol A, 30 percent of polyether polyol B, 25 percent of toluene diisocyanate, 2 percent of green tea powder, 1.9 percent of water, 0.05 percent of silicone oil, 0.02 percent of ammonia, 0.02 percent of stannous octoate, and 0.01 percent of mill base.

[0024] A fabricating method for the green tea memory foam comprises the following procedures: [0025] 1) Taking every component according to the weight ratio; [0026] 2) Mixing uniformly the polyether polyol A, polyether polyol B green tea powder and mill base according to the ratio for standby application; [0027] 3) Adding the water, silicone oil, ammonia and stannous octoate according to the ratio into the mixture of procedure 2) then mixing uniformly for standby application; [0028] 4) Adding the toluene diisocynate according to the ratio into the mixture of procedure 3) then mixing uniformly and quickly for 46 seconds to get a new mixture; [0029] 5) Pouring the mixture of procedure 4) into a mold for foaming to foam into an intermediate green tea memory foam then taking it out from the mold after 1020 minitues, and then airing it for 2030 hours to get the green tea memory foam.

[0030] Embodiment 3, a kind of green tea memory foam comprises the following components at the weight ratio of 45 percent of polyether polyol A, 29 percent of polyether polyol B, 22 percent of toluene diisocyanate, 1.9 percent of green tea powder, 2 percent of water, 0.05 percent of silicone oil, 0.03 percent of ammonia, 0.015 percent of stannous octoate, and 0.015 percent of mill base.

[0031] A fabricating method for the green tea memory foam comprises the following procedures: [0032] 1) Taking every component according to the weight ratio; [0033] 2) Mixing uniformly the polyether polyol A, polyether polyol B green tea powder and mill base according to the ratio for standby application; [0034] 3) Adding the water, silicone oil, ammonia and stannous octoate according to the ratio into the mixture of procedure 2) then mixing uniformly for standby application; [0035] 4) Adding the toluene diisocynate according to the ratio into the mixture of procedure 3) then mixing uniformly and quickly for 46 seconds to get a new mixture; [0036] 5) Pouring the mixture of procedure 4) into a mold for foaming to foam into an intermediate green tea memory foam then taking it out from the mold after 1020 minitues, and then airing it for 2030 hours to get the green tea memory foam.

[0037] The green tea memory foam of the present invention has a color of green tea and the preservation time of the green tea aroma can be more than 6 months, mainly used for healthy sleep and rest. The main products of the present invention include bedding articles, pillows, mattresses, waist pillows, cushions; car accessories, seat cushions, back cushions, headrests and so on. The green tea memory foam of the invention has the advantages of effectively improving the environmental quality of the human body in the rest and sleep with fragrant smell, which highly satisfies the customers.

[0038] The detailed description above is just the embodiments of the present invention and not to limit the patent scope of the invention. All the equivalent structures and process modifications based on the specification of the present invention as well as the applications directly or indirectly in the other relevant technical field should also fall within the scope of the invention.