Catalyst having a helical outer shape, improving hydrodynamics in reactors

Abstract

A catalyst for catalytic reactors of which the outer shape is a helix with n blades, where n is greater than or equal to 1, wherein the stack void fraction percentage is between 75% and 85% and the surface area/volume ratio is greater than 1000 square meters/square meters.

Claims

1. A catalyst for catalytic reactors, the outer shape of which is a helicoid having n blades with n1, wherein the void fraction percentage of the packing is between 75% and 85%, and wherein the surface area/volume ratio is greater than 1000 m.sup.2/m.sup.3, with said catalyst comprising a support and of an active phase deposited on the support.

2. The catalyst of claim 1, wherein the catalyst has a length between 5 mm and 40 mm and an equivalent cylinder diameter between 5 mm and 10 mm.

3. The catalyst of claim 1, wherein the surface area/volume ratio is greater than 2000 m.sup.2/m.sup.3.

4. The catalyst of claim 1, wherein the catalyst of helicoidal shape comprises between 1.5 and 10 turns.

5. The catalyst of claim 1, wherein the support is of inorganic oxide.

6. The catalyst of claim 1, wherein the inorganic oxides are selected from the group consisting of Al.sub.2O.sub.3, MgO, CaO, ZrO.sub.2, TiO.sub.2, CeO.sub.2 and Ce.sub.2O.sub.3.

7. The catalyst of claim 1, wherein the active phase consists of metal particles selected from the group consisting of Ni, Rh, Pt, Pd, Co, Mo, Cu, Fe, and a mixture thereof.

8. A catalytic reactor comprising a packing of catalysts as claimed in claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) For a further understanding of the nature and objects for the present invention, reference should be made to the following detailed description, taken in conjunction with the accompanying drawings, in which like elements are given the same or analogous reference numbers and wherein:

(2) FIG. 1 illustrate examples of catalyst according various embodiments of the present invention.

(3) FIG. 2 illustrates a reactor utilizing catalysts, in accordance with one embodiment of the present invention.

(4) FIG. 3 illustrates the comparative results indicated in tables 1, 2, and 3, in accordance with one embodiment of the present invention.

(5) FIG. 4 illustrates the comparative results indicated in tables 4, and 5, in accordance with one embodiment of the present invention; and

(6) FIG. 5 illustrates that the axial dispersions (Dax) of the helices are lower than those of the 10-hole barrels, in accordance with one embodiment of the present invention.

DESCRIPTION OF PREFERRED EMBODIMENTS

(7) One solution of the present invention is a catalyst for catalytic reactors, the shape of which is a helicoid having n blades with n1 and is such that the void fraction percentage of the packing (PFVE) is between 75% and 85% and the surface area/volume ratio (S/V) is greater than 1000 m.sup.2/m.sup.3. The term blade will refer to the planar surface attached to the central axis and the term turn will refer to the number of rotations of the blades, preferably n=1, 2 or 3.

(8) Note that the helicoid having 1 blade corresponds to the shape that is commonly referred to as an Archimedes screw; the helicoid having 2 blades corresponds to the shape that is commonly referred to as a double helix and the helicoid having 3 blades corresponds to the shape that is commonly referred to as a triple helix, etc.

(9) Each helicoid according to the invention creates turbulences and the use of a packing of helicoids according to the invention leads to phenomena of ejection of gas from one helicoid to another locally improving the mixing within catalytic reactors.

(10) The void fraction percentage of the packing (PFVE) is directly linked to the pressure drop of the catalytic bed. The PFVE is defined as follows:

(11) $\mathrm{PFVE}=100-\frac{\mathrm{Volume}\mathrm{of}\mathrm{the}\mathrm{helicoid}}{\mathrm{Total}\mathrm{volume}\mathrm{of}\mathrm{the}\mathrm{stack}}100$

(12) The ratio S/V is defined as follows:

(13) $S/V=\frac{\mathrm{Surface}\mathrm{area}\mathrm{of}\mathrm{the}\mathrm{helicoid}}{\mathrm{Volume}\mathrm{of}\mathrm{the}\mathrm{helicoid}}100$

(14) Depending on the case, the catalyst according to the invention may have one or more of the following features: said catalyst has a length between 5 and 40 mm and an equivalent cylinder diameter between 5 and 10 mm; the surface area/volume ratio (S/V) is greater than 2000 m.sup.2/m.sup.3; said catalyst of helicoidal shape comprises between 1.5 and 10 turns; said catalyst consists of a support of inorganic oxide or mixture of inorganic oxides type; said catalyst consists of a support and of an active phase deposited on the support; the support of the catalyst is of inorganic oxide or mixture of inorganic oxides type; the inorganic oxides are selected from Al.sub.2O.sub.3, MgO, CaO, ZrO.sub.2, TiO.sub.2, Ce.sub.2O.sub.3, and CeO.sub.2; the active phase deposited in and/or on the support by all types of techniques (impregnation, co-precipitation, etc.) consists of metal particles selected from Ni, Rh, Pt, Pd, Co, Mo, Cu, Fe and/or a mixture thereof; the active phase may be deposited in and/or on the support by all types of techniques (impregnation, co-precipitation, etc.).

(15) FIG. 1 gives examples of catalyst according to the invention.

(16) The pressure drops in the catalytic reactors are an essential parameter that influences the performance of certain gas/solid, liquid/solid or gas/liquid/solid processes. The pressure drop in a reactor is linked to the geometry of the catalyst and to the compactness of its packing and/or to the formation of fines during the packing due to its low mechanical strength. Certain gas/solid, liquid/solid or gas/liquid/solid processes involve several catalytic reactors that can have recycles (e.g. the stream leaving a secondary reactor is sent back to the top of a primary reactor). In these cases, compression steps may be necessary and may be detrimental to the overall efficiency of the process if the pressure drops in the reactors are too large. Furthermore, other processes may involve, downstream of the catalytic reactors, units whose performance may be reduced by too low an inlet pressure (e.g. purification units).

(17) The invention proposes novel geometries with high PFVE (greater than 70%) in order to reduce the pressure drops.

(18) Moreover, the gas/solid, liquid/solid or gas/liquid/solid catalytic reactions having rapid intrinsic kinetics are then limited by the transfer of material (transfer of reactants) either from the gaseous or liquid phases to the surface of the catalyst (extraparticle transfer), or from the surface of the catalyst to the active sites within the pores of the catalyst (intraparticle transfer). These material transfers are, in these cases, slower than the reaction and the step limiting the catalytic efficiency is the transport of the reactants to the active site where the reaction takes place.

(19) A key parameter of the catalyst that influences the internal and external transfers is the ratio S/V.

(20) The catalyst according to the invention may be used on any type of reaction (oxidation, hydrogenation, etc.). The main reactions targeted of gas/solid type will be the reactions for reforming a hydrocarbon (natural gas, naphtha, biogas, refinery off-gas, etc.), an alcohol (MeOH, EtOH), or glycerol, via an oxidant such as steam, CO.sub.2, oxygen or a mixture thereof, the reactions for converting a synthesis mixture rich in H.sub.2/CO such as the water-gas shift reaction, the reverse water-gas shift reaction, the reaction for synthesizing an alcohol (MeOH, etc.), and the methanation reaction.

(21) The use of the catalyst according to the invention is not limited to gas/solid type reactions but is applicable to liquid/solid and gas/liquid/solid reactions.

(22) The catalyst according to the invention may operate under pressure (1 to 60 at) and at temperature (150-1000 C.).

(23) Finally, another subject of the present invention is a catalytic reactor comprising a packing of catalysts according to the invention.

(24) The advantages of the subject of the invention have been illustrated by the example below.

EXAMPLES

Example 1

(25) Pressure drop and tracing (axial and radial dispersions) experiments were carried out in a reactor with a diameter of 15 cm and a height of 2.5 m (volume of the bed: 46.9 L). This pilot plant has 5 branch connections for the pressure drop measurements and 2 branch connections for the radial dispersion of the gas. The gas phase used is air with a flow rate that may vary from 0 to 185 m.sup.3/h (i.e 0 to 2.9 m/s) and the tracer is methane. For the tracing measurements, the methane is injected in a pulsed manner at the top and at the center of the section of the bed (FIG. 2). Regarding the axial dispersions, the concentration of methane is measured by an FID (Flame Ionization Detector) in a cone at the outlet of the reactor with an acquisition frequency of 100 Hz. For the radial dispersions, samplings are taken over the entire diameter of the reactor with the aid of pipes passing through the branch connections of the reactor (FIG. 2). The axial dispersions make it possible to have information on the performance of the reactor (ideal plug flow, dispersed plug flow, etc.) via the measurement of the Pclet number (Pe=vL/D.sub.ax) with v, the interstitial velocity (m/s), L, the height of the bed (m) and Dax the axial dispersion (m.sup.2/s). The higher the Pclet number, the more the reactor tends toward the completely plug-flow reactor. The information on the distribution of the fluid across the bed is obtained by the radial dispersion data.

(26) Subsequently, the following will be denoted:

(27) DP: pressure drops (mbar or Pa)

(28) L: length of the bed (m)

(29) Q: volume flow rate of air (m.sup.3/h)

(30) u: superficial (empty tower) velocity (m/s)

(31) v: interstitial velocity (m/s)

(32) : porosity of the bed

(33) Dax: axial dispersion (m.sup.2/s)

(34) with u=v

(35) The article tested in this example is a helix with 3 blades of 0.4 cm and 5 turns and a length of 3.5 cm. It is compared with commercial articles which are glass beads having a diameter of 5 mm and 10-hole barrels having a diameter of 19 mm and a height of 15 mm with one central 5 mm hole and 9 peripheral 3 mm holes.

(36) Table 1 indicates the pressure drops of the 10-hole barrels as a function of the volume flow rate or the superficial (empty tower) velocity.

(37) Table 2 indicates the pressure drops of the glass beads as a function of the volume flow rate or the superficial (empty tower) velocity.

(38) Table 3 indicates the pressure drops of the helices as a function of the volume flow rate or the superficial (empty tower) velocity.

(39) FIG. 3 enables a comparison of the results given in Tables 1, 2 and 3. The triangles correspond to the pressure drops over the helices, the squares correspond to the pressure drops over the 10-hole barrels and the circles correspond to the pressure drops over the glass beads.

(40) Table 4 indicates the axial dispersion of the 10-hole barrels as a function of the superficial (empty tower) velocity.

(41) Table 5 indicates the axial dispersion of the helices as a function of the superficial (empty tower) velocity.

(42) FIG. 4 enables a comparison of the results given in Tables 4 and 5. The triangles correspond to the axial dispersion for the helices and the squares correspond to the axial dispersion for the 10-hole barrels.

(43) Table 6 indicates the Pclet number determined with a flow rate of 80 m.sup.3/h for the 10-hole barrels and the helices.

(44) TABLE-US-00001 TABLE 1 Q DP exp DP exp u m.sup.3/h mbar/m Pa/m m/s 44.95 3.80 379.64 0.71 49.71 4.55 455.49 0.78 59.70 6.26 625.67 0.94 70.99 8.71 871.23 1.12 81.24 11.11 1110.68 1.28 90.30 13.51 1350.56 1.42 102.80 17.42 1742.35 1.62 109.59 19.66 1965.68 1.72 119.86 23.52 2352.19 1.88 131.21 28.61 2861.28 2.06 147.27 36.04 3604.31 2.31 157.79 46.75 4675.35 2.48 138.83 31.93 3192.52 2.18 112.55 20.87 2086.86 1.77 90.86 13.61 1361.49 1.43 69.43 8.44 844.32 1.09 51.15 4.70 469.51 0.80 44.48 3.67 367.00 0.70

(45) TABLE-US-00002 TABLE 2 Q DP exp DP exp u m.sup.3/h mbar/m Pa/m m/s 10.43 2.96 296.32 0.16 15.22 5.54 554.19 0.24 20.42 9.11 911.37 0.32 25.71 13.53 1352.53 0.40 30.62 18.38 1838.29 0.48 41.02 29.97 2996.83 0.64 50.54 42.77 4276.65 0.79 60.89 58.75 5875.13 0.96 74.54 86.45 8645.15 1.17 60.29 58.23 5822.83 0.95 50.03 41.93 4193.42 0.79 40.73 29.77 2977.50 0.64 30.17 17.77 1776.67 0.47 20.87 9.28 928.11 0.33 10.28 2.88 288.35 0.16

(46) TABLE-US-00003 TABLE 3 Q DP exp DP exp u m.sup.3/h mbar/m Pa/m m/s 68.06 2.69 269.01 1.07 75.14 3.50 350.01 1.18 86.81 4.48 447.81 1.36 94.18 5.55 555.16 1.48 103.69 7.03 703.47 1.63 119.16 9.30 930.22 1.87 127.04 11.00 1099.96 2.00 140.86 13.59 1358.92 2.21 154.61 16.43 1642.98 2.43 164.74 19.17 1916.72 2.59 173.90 21.42 2142.02 2.73 186.51 24.81 2480.72 2.93 172.42 20.80 2079.79 2.71 152.62 16.27 1627.32 2.40 138.98 13.15 1314.87 2.18 119.37 9.64 964.11 1.88 104.31 6.82 682.45 1.64 86.55 4.74 474.01 1.36 67.97 2.68 268.30 1.07

(47) TABLE-US-00004 TABLE 4 Dax v (m/s) u (m/s) (m.sup.2/s) 1.97 0.97 1.93E002 2.49 1.22 2.15E002 3.44 1.69 2.73E002

(48) TABLE-US-00005 TABLE 5 Dax v (m/s) u (m/s) (m.sup.2/s) 1.13 0.89 3.39E003 1.46 1.16 4.39E003 1.95 1.54 5.45E003

(49) TABLE-US-00006 TABLE 6 Particle Axial Pclet number 10-hole barrels (19 15 mm) 280 Helices 800

(50) In summary, the pressure drops are better for the helices than for the 10-hole barrels and the 5 mm beads.

(51) The helices have a higher bed Pclet number than that of the 10-hole barrels (800 and 280 respectively). Consequently, a reactor filled with helices will have an operation closer to that of a completely plug-flow reactor. This result is confirmed by the calculations of the axial dispersions as a function of the superficial (empty tower) velocities. Indeed, as FIG. 4 shows, the axial dispersions (Dax) of the helices are lower than those of the 10-hole barrels, in other words the deviations relative to a completely plug flow are lower with the helices.

Example 2

(52) Radial dispersion measurements were carried out in a tube with a diameter of 15 cm and a height of 80 cm. The tube was filled over 40 cm with the various particles and the measurements were carried out with an air flow rate of 40 m.sup.3/h. The experiment consisted in injecting pulses of methane at a height of 28 cm relative to the support grid, the injector being located in the packing. The samplings were carried out using a pipe under the grid for supporting the particles over 9 points per axis (distances with respect to the center: 7.5 cm; 5.5 cm; 3.5 cm; 1.5 cm; 0 cm; 1.5 cm; 3.5 cm; 5.5 cm; 7.5 cm) and over 6 axes spaced apart by 30 degrees (i.e. at 0, 30, 60, 90, 120 and 150 degrees).

(53) The article tested in this example is a helix with 3 blades of 0.4 cm and 5 turns and a length of 3.5 cm. It is compared with commercial articles which are glass beads having a diameter of 5 mm.

(54) The methane concentration profiles are given in FIGS. 5a) and 5b).

(55) Helix-type shapes greatly improve the radial dispersion of the packings compared to the bead packings. Indeed, the radial dispersion in the helix packing is 50 times greater compared to that of the bead packing.

(56) It will be understood that many additional changes in the details, materials, steps and arrangement of parts, which have been herein described in order to explain the nature of the invention, may be made by those skilled in the art within the principle and scope of the invention as expressed in the appended claims. Thus, the present invention is not intended to be limited to the specific embodiments in the examples given above.