Sintered product having a relative density of greater than 90%, with, to more than 80% of the volume thereof, a stack of flat ceramic platelets, the assembly of the platelets having a mean thickness of less than 3 μm, having a width of greater than 50 mm, and including more than 20% of alumina, as a percentage on the basis of the weight of the product. The width of the product is the largest dimension measured in the plane in which the length of the product is measured, along a direction perpendicular to the direction of the length. The length of the product is the largest dimension thereof in a plane parallel to the general plane in which the platelets extend.

A ceramic electronic component includes a body including a dielectric layer and an internal electrode, and an external electrode disposed on the body and connected to the internal electrode. The dielectric layer includes a plurality of dielectric grains, and at least one of the plurality of dielectric grains has a core-dual shell structure having a core and a dual shell. The dual shell includes a first shell surrounding at least a portion of the core, and a second shell surrounding at least a portion of the first shell, and a concentration of a rare earth element included in the second shell is more than 1.3 times to less than 3.8 times a concentration of a rare earth element included in the first shell.

Provided is a ceramic composite material and a wavelength converter. The ceramic composite material includes: an alumina matrix, a fluorescent powder uniformly distributed in the alumina matrix, and scattering centers uniformly distributed in the alumina matrix, wherein the alumina matrix is an alumina ceramics, the scattering centers are alumina particles, the alumina particles each have a particle diameter of 1 μm to 10 μm, and the fluorescent powder has a particle diameter of 13 μm to 20 μm.

An embodiment of a PCD insert comprises an embodiment of a PCD element joined to a cemented carbide substrate at an interface. The PCD element has internal diamond surfaces defining interstices between them. The PCD element comprises a masked or passivated region and an unmasked or unpassivated region, the unmasked or unpassivated region defining a boundary with the substrate, the boundary being the interface. At least some of the internal diamond surfaces of the masked or passivated region contact a mask or passivation medium, and some or all of the interstices of the masked or passivated region and of the unmasked or unpassivated region are at least partially filled with an infiltrant material.

A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950° C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000° C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 μm and an average width of 1 to 2 μm, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

A multilayer ceramic capacitor includes: a multilayer structure in which each of dielectric layers and each of internal electrode layers are stacked, wherein a relationship of 8.0≥I.sub.A/I.sub.B>1.40 is satisfied in a TSDC (Thermally Stimulated Depolarization Currents) of temperature elevation rate of 10 degrees C./min under a condition of 130 degrees C., 5 V/μm and a polarization of 30 min, when a peak current value on a lower temperature side in a temperature range of 130 degrees C. to 190 degrees C. is I.sub.A and a peak current value on a higher temperature side in a temperature range of 190 degrees C. to 280 degrees C. is I.sub.B.

A method of producing a core-shell particle includes introducing a barium titanate-based base powder and an additive to a reactor, and exposing the barium titanate-based base powder and the additive to a thermal plasma torch to obtain core-shell particles including a core portion having barium titanate (BaTiO.sub.3) and a shell portion including the additive and formed on a surface of the core portion.

Polycrystalline cubic boron nitride, PCBN, material and methods of making PCBN. A method includes providing a matrix precursor powder comprising particles having an average particle size no greater than 250 nm, providing a cubic boron nitride, cBN, powder comprising particles of cBN having an average particle size of at least 0.2 intimately mixing the matrix precursor powder and the cBN powder, and sintering the intimately mixed powders at a temperature of at least 1100° C. and a pressure of at least 3.5 GPa to form the PCBN material comprising particles of cubic boron nitride, cBN dispersed in a matrix material.

A solid electrolyte includes partially stabilized zirconia in which a stabilizer forms a solid solution in zirconia. The partially stabilized zirconia includes at least monoclinic phase particles and cubic phase particles as crystal particles that configure the partially stabilized zirconia, and an abundance ratio of the monoclinic phase particle is 5 to 25% by volume. The partially stabilized zirconia includes stabilizer low-concentration phase particles of which concentration of the stabilizer at a particle center is equal to or less than 1 mol %, as the crystal particles. The stabilizer low-concentration phase particles have a particle-size distribution of number frequency thereof having a peak at which an average particle size is 0.6 to 1.0 μm, and a particle size at 10% of a cumulative number is 0.5 μm or greater, and of the overall low-concentration phase particles, 50% by volume or greater belong to the peak.

A method of producing a core-shell particle includes introducing a barium titanate-based base powder and an additive to a reactor, and exposing the barium titanate-based base powder and the additive to a thermal plasma torch to obtain core-shell particles including a core portion having barium titanate (BaTiO.sub.3) and a shell portion including the additive and formed on a surface of the core portion.