A manganese-zinc ferrite with a high magnetic permeability at negative temperature and low loss at high temperature consists of Fe.sub.2O.sub.3, MnO and ZnO, and additives consisting of CaCO.sub.3, ZrO.sub.2, Co.sub.2O.sub.3 and SnO.sub.2 are also added. A method for preparing the manganese-zinc ferrite is further provided. According to the method, by reasonably adjusting a ratio of Mn to Zn to Fe and appropriately increasing the content of Co in the additives, a manganese-zinc ferrite material with both a high magnetic permeability and low loss at about −20° C. and low loss at 120-140° C. is obtained. The manganese-zinc ferrite material has two loss valleys at about −20° C. and about 100° C. in a temperature range of −30° C. to 140° C., which expands the application range of the manganese-zinc ferrite material.

A ferrite sintered magnet comprising an M type Sr ferrite having a hexagonal structure as a main phase, wherein the ferrite sintered magnet comprises La and Co, a content of B is 0.005 to 0.9% by mass in terms of B.sub.2O.sub.3, a content of Zn is 0.01 to 1.2% by mass in terms of ZnO, and the ferrite sintered magnet satisfies [La]/[Zn]≤0.79 and [Co]/[Zn]≤0.67 when an atomic concentration of La is represented by [La], an atomic concentration of Co is represented by [Co], and an atomic concentration of Zn is represented by [Zn].

The invention relates to a ceramic material, comprising lead zirconate titanate, which additionally contains K and optionally Cu. The ceramic material can be used in an electroceramic component, for example a piezoelectric actuator. The invention also relates to methods for producing the ceramic material and the electronic component.

In some embodiments, a ceramic armor product includes: a ceramic powder; an at least one metal-based additive; and a density of 4.3-4.7 g/cc, wherein the ceramic armor product is substantially lacking grain orientation. In some embodiments, a ceramic armor product, includes: a ceramic powder, wherein the ceramic powder is titanium diboride (TiB2); an at least one metal-based additive, wherein the at least one metal based additive comprises elements ranging from atomic numbers 21 through 30, 39 through 51, and 57 through 77; and a density of 4.3-4.7 g/cc, wherein the ceramic armor product is substantially lacking grain orientation.

The present disclosure describes a lithium solid state battery, including a cathode that includes an active material such as lithium, and an additive having a lower melting point than the active material. The additive can provide a composite cathode where a cathode-electrolyte interphase has high electronic and ionic conductivity, good mechanical deformability, and high oxidation potential.

According to the present invention, there are provided a composite body that enables the formation of a lithium ion conductor that exhibits good lithium ion conductivity by a pressurization treatment without sintering at a high temperature (about 1,000° C.) while using a lithium-containing oxide having excellent safety and stability, as well as a lithium ion conductor, an all-solid state lithium ion secondary battery, an electrode sheet for an all-solid state lithium ion secondary battery, and lithium tetraborate. The composite body according to the embodiment of the present invention contains a lithium compound having a lithium ion conductivity of 1.0×10.sup.−6 S/cm or more at 25° C. and lithium tetraborate that satisfies the following requirement 1.

The requirement 1: In a reduced two-body distribution function G(r) obtained from an X-ray total scattering measurement of the lithium tetraborate, a first peak in which a peak top is located in a range where r is 1.43±0.2 Å and a second peak in which a peak top is located in a range where r is 2.40±0.2 Å are present, G(r) of the peak top of the first peak and G(r) of the peak top of the second peak indicate more than 1.0, and an absolute value of G(r) is less than 1.0 in a range where r is more than 5 Å and 10 Å or less.

A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950° C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000° C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 μm and an average width of 1 to 2 μm, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

A lanthanum molybdenum composite oxide is provided. The lanthanum molybdenum composite oxide has a primary crystal phase formed of La.sub.2Mo.sub.2O.sub.9. The lanthanum molybdenum composite oxide also has a secondary crystal phase formed of a lanthanum molybdenum composite oxide species other than La.sub.2Mo.sub.2O.sub.9. The secondary crystal phase may contain at least one species selected from a group consisting of La.sub.2Mo.sub.3O.sub.12, La.sub.6MoO.sub.12, La.sub.7Mo.sub.7O.sub.30, La.sub.2Mo.sub.4O.sub.15, La.sub.2MoO.sub.6, La.sub.4MoO.sub.9, and LaMo.sub.2O.sub.5.

A method for improving the Bs of an MnZn power ferrite material by moving the valley point includes the following steps: 1) mixing Fe.sub.2O.sub.3, MnO and ZnO, and performing primary sanding; 2) adding glue, performing spraying and granulating, and then performing pre-sintering to obtain a pre-sintered material; 3) adding additives to the pre-sintered material, and performing secondary sanding; and 4) adding glue to the secondary sanded material, performing spraying and granulating, pressing into a standard ring, and then performing sintering. The method controls and moves the valley point, reduces loss and improves the Bs of a material by controlling the Fe.sub.2O.sub.3 content and the Co.sub.2O.sub.3 content, and the method is relatively simple and suitable for industrialization.

The present invention relates to a ceramic, to a process for preparing the ceramic and to the use of the ceramic as a dielectric in a capacitor.