Provided is a surface-treated copper foil in which in order to avoid failures of electronic parts by corrosion, a high bond strength between an electrolytic copper foil and a resin base material can be maintained even when the surface-treated copper foil is exposed to corrosive gases and microparticles, and a method for manufacturing the same. The surface-treated copper foil of the present invention comprises an electrolytic copper foil, a roughened layer covering at least one surface side of the electrolytic copper foil, and a rust preventive layer further covering the roughened layer, wherein the rust preventive layer is at least one surface of the surface-treated copper foil; the rust preventive layer comprises at least a nickel layer; and the thickness of the nickel layer is 0.8 to 4.4 g/m.sup.2 in terms of mass per unit area of nickel; and the noncontact roughness Spd of the rust preventive layer is 1.4 to 2.6 peaks/μm.sup.2 and the surface roughness RzJIS of the rust preventive layer is 1.0 to 2.5 μm. The method for manufacturing the surface-treated copper foil forms the roughened layer having higher roughnesses than the noncontact roughness Spd and surface roughness RzJIS on one surface of the electrolytic copper foil, and thereafter forming the rust preventive layer meeting the predetermined condition.

A method comprising: cold-spraying a surface of a substrate with a bond material to form a bond coating; and cold-spraying a surface of the bond coating with a coating material to form a top coating. The bond material is different from the coating material and harder than the surface of the substrate.

A black plated steel sheet includes a steel sheet and an Al—Mg—Si-based plating layer disposed on one surface or both surfaces of the steel sheet; in which the plating layer includes a black layer on the outermost surface thereof, and the black layer has a weight ratio of O to (Al+Mg+Si+O) of 0.01 to 0.6.

A high-performance thermoformed component provided with a coating, and a manufacturing method therefor. The thermoformed component comprises a substrate and a coating thereon. The substrate comprises the following ingredients in percentage by weight: 0.01-0.8% of C, 0.05-1.0% of Si, 0.1-5% of Mn, 0.001-0.3% of P, 0.001-0.1% of S, 0.001-0.3% of Al, 0.001-0.5% of Ti, 0.0005-0.1% of B, 0.001-0.5% of Nb, 0.001-0.5% of V, and the remainder being Fe and other unavoidable impurities. The appearance of the thermoformed component has no color difference and no mottling. The surface oxygen content of the thermoformed component is 0.1-20 wt. %, and the ratio of the standard deviation to the average value of the surface oxygen content satisfies: 0<standard deviation of oxygen content/average value of oxygen content ≤0.3. In the manufacturing method, a coated steel plate that has undergone heat treatment, transfer processing, and hot stamping is not treated with oil.

The present invention pertains to a method for producing a graphene-coated steel sheet, the method comprising the steps of: modifying the surface of the steel sheet so that the surface is negatively charged; forming a positively-charged first graphene oxide layer on the surface-modified steel sheet; forming a negatively-charged second graphene oxide layer on the first graphene oxide layer; and heat-treating the steel sheet on which the first and second graphene oxide layers are formed. The present invention provides a graphene coating method which can be easily applied to large-area coating through a simple process without a special dispersant or binder, and has the effect of allowing the excellent physical properties of graphene to be more efficiently exhibited.

The present disclosure relates to an aluminum alloy-plated steel sheet having excellent workability and corrosion resistance and a method for manufacturing the same, and more particularly, to an aluminum alloy-plated steel sheet preventing microcracks generated during hot forming and has excellent seizure resistance and corrosion resistance, and a method for manufacturing the same.

Some embodiments include a method of forming a conductive structure. A metal-containing conductive material is formed over a supporting substrate. A surface of the metal-containing conductive material is exposed to at least one radical form of hydrogen and to at least one oxidant. The exposure alters at least a portion of the metal-containing conductive material to thereby form at least a portion of the conductive structure. Some embodiments include a conductive structure which has a metal-containing conductive material with a first region adjacent to a second region. The first region has a greater concentration of one or both of fluorine and boron relative to the second region.

An article and a method of manufacturing the article is disclosed. The method includes providing the article including a substrate and a coating at least partially disposed on the substrate. The coating includes an outer surface. The coating further includes platinum and chromium. The method further includes applying cold work to the outer surface of the coating to produce a cold-worked layer extending from the outer surface of the coating to a cold work depth. The cold-worked layer includes approximately 45% cold work. The cold work depth is between about 30 microns to about 150 microns from the outer surface of the coating.

In one example, a method for forming an environmental barrier coating (EBC) and/or abradable coating on a substrate. The method may include depositing a coating on a ceramic or ceramic matrix composite (CMC) substrate to form an as-deposited coating, wherein the coating includes at least one of an environmental barrier coating (EBC) and an abradable coating. The method further comprises heat treating the as-deposited coating at or above a first temperature for a first period of time following the deposition of the as-deposited coating on the substrate, wherein heat treating the as-deposited coating includes heating the as-deposited coating to or above the first temperature at a controlled rate. The heat treatment may be configured to at least one of decrease the open pores and/or microcracks of the heat-treated coating compared to the as-deposited coating or control a grain size of the heat-treated coating.

The present disclosure relates to an aluminum alloy-plated steel sheet having excellent workability and corrosion resistance and a method for manufacturing the same, and more particularly, to an aluminum alloy-plated steel sheet preventing microcracks generated during hot forming and has excellent seizure resistance and corrosion resistance, and a method for manufacturing the same.