Thin tin oxide films are used as spacers in semiconductor device manufacturing. In one implementation, thin tin oxide film is conformally deposited onto a semiconductor substrate having an exposed layer of a first material (e.g., silicon oxide or silicon nitride) and a plurality of protruding features comprising a second material (e.g., silicon or carbon). For example, 10-100 nm thick tin oxide layer can be deposited using atomic layer deposition. Next, tin oxide film is removed from horizontal surfaces, without being completely removed from the sidewalls of the protruding features. Next, the material of protruding features is etched away, leaving tin oxide spacers on the substrate. This is followed by etching the unprotected portions of the first material, without removal of the spacers. Next, underlying layer is etched, and spacers are removed. Tin-containing particles can be removed from processing chambers by converting them to volatile tin hydride.

In an embodiment, a method includes: receiving, within a processing chamber, a wafer with a photoresist mask above a metal layer, wherein the processing chamber is connected to a gas source; applying an etchant configured to etch the metal layer in accordance with the photoresist mask within the processing chamber; and applying gas from the gas source to perform plasma ashing in the processing chamber.

Disclosed is a ring carrier used for transferring a ring member. The ring carrier includes a body having a plate shape, and a guide part protruding from an upper surface of the body to face an inner periphery of the ring member, and an alignment hole used when the ring carrier is aligned is formed in the body to pass through the body.

An etching method of the invention includes: a resist pattern-forming step of forming a resist layer on a target object, the resist layer being formed of a resin, the resist layer having a resist pattern; an etching step of etching the target object via the resist layer having the resist pattern; and a resist protective film-forming step of forming a resist protective film on the resist layer. The etching step is repetitively carried out multiple times. After the etching steps are repetitively carried out multiple times, the resist protective film-forming step is carried out.

An apparatus for perform metal etching and plasma ashing includes: a processing chamber having an enclosed area; an electrostatic chuck disposed in the enclosed area and configured to secure a wafer, the electrostatic chuck connected with a bias power; at least one coil connected with a source power; a etchant conduit configured provide an etchant to a metal of the wafer within the processing chamber in accordance with a photoresist mask of the wafer; and a gas intake conduit connected with a gas source, wherein the gas intake conduit is configured to supply the processing chamber with a gas from the gas source during performance of plasma ashing within the processing chamber.

An apparatus for processing a substrate is provided. The apparatus includes a chamber having at least one gas inlet and at least one gas outlet, a substrate support in the chamber, a plasma generator and a controller configured to cause (a) placing a substrate on the substrate support, the substrate including a target layer having a recess, (b) exposing the substrate to a silicon-containing precursor, thereby forming an adsorption layer on a sidewall of the recess, (c) generating a plasma from a gas mixture in the chamber, the gas mixture including an oxygen-containing gas and a halogen-containing gas, (d) exposing the substrate to the plasma, thereby forming a protection layer on the adsorption layer while etching a bottom of the recess and (e) repeating (b) to (d) in sequence.

Thin tin oxide films are used as spacers in semiconductor device manufacturing. In one implementation, thin tin oxide film is conformally deposited onto a semiconductor substrate having an exposed layer of a first material (e.g., silicon oxide or silicon nitride) and a plurality of protruding features comprising a second material (e.g., silicon or carbon). For example, 10-100 nm thick tin oxide layer can be deposited using atomic layer deposition. Next, tin oxide film is removed from horizontal surfaces, without being completely removed from the sidewalls of the protruding features. Next, the material of protruding features is etched away, leaving tin oxide spacers on the substrate. This is followed by etching the unprotected portions of the first material, without removal of the spacers. Next, underlying layer is etched, and spacers are removed. Tin-containing particles can be removed from processing chambers by converting them to volatile tin hydride.

Processes for removing a photoresist from a substrate after, for instance, ion implantation are provided. In one example implementation, a process can include placing a substrate having a bulk photoresist and a crust formed on the bulk photoresist in a processing chamber. The process can include initiating a first strip process in the processing chamber. The process can include accessing an optical emission signal associated with a plasma during the first strip process. The process can include identifying an endpoint for the first strip process based at least in part on the optical emission signal. The process can include terminating the first strip process based at least in part on the endpoint. The process can include initiating a second strip process to remove the photoresist from the substrate.

Provided is a method of trimming an inorganic resist in an integration scheme, the method comprising: disposing a substrate in a process chamber, the substrate having an inorganic resist layer and an underlying layer comprising an oxide layer, a silicon nitride layer, and a base layer, the inorganic resist layer having an inorganic structure pattern; performing an inorganic resist trimming process to selectively remove a portion of the inorganic resist structure pattern on the substrate, the trimming process using a first etchant gas mixture and generating a first pattern; controlling selected two or more operating variables of the integration scheme in order to achieve target integration objectives; wherein the first etchant gas mixture comprises a fluorine-containing gas and a diluent gas; and wherein the target integration objectives include a target critical dimension (CD), a target line edge roughness (LER), a target line width roughness (LWR) and a target substrate throughput.

Thin tin oxide films are used as spacers in semiconductor device manufacturing. In one implementation, thin tin oxide film is conformally deposited onto a semiconductor substrate having an exposed layer of a first material (e.g., silicon oxide or silicon nitride) and a plurality of protruding features comprising a second material (e.g., silicon or carbon). For example, 10-100 nm thick tin oxide layer can be deposited using atomic layer deposition. Next, tin oxide film is removed from horizontal surfaces, without being completely removed from the sidewalls of the protruding features. Next, the material of protruding features is etched away, leaving tin oxide spacers on the substrate. This is followed by etching the unprotected portions of the first material, without removal of the spacers. Next, underlying layer is etched, and spacers are removed. Tin-containing particles can be removed from processing chambers by converting them to volatile tin hydride.