An anisotropic conductive film has a three-layer structure in which a first connection layer is sandwiched between a second connection layer and a third connection layer that each are formed mainly of an insulating resin. The first connection layer has a structure in which conductive particles are arranged in a single layer in the plane direction of an insulating resin layer on a side of the second connection layer, and the thickness of the insulating resin layer in central regions between adjacent ones of the conductive particles is smaller than that of the insulating resin layer in regions in proximity to the conductive particles.

A bond tip for thermocompression bonding a bottom surface includes a die contact area and a low surface energy material covering at least a portion of the bottom surface. The low surface energy material may cover substantially all of the bottom surface, or only a peripheral portion surrounding the die contact area. The die contact area may be recessed with respect to the peripheral portion a depth at least as great as a thickness of a semiconductor die to be received in the recessed die contact area. A method of thermocompression bonding is also disclosed.

The present invention relates to a film-shaped firing material (1) which contains: sinterable metal particles (10); a binder component (20) that is a solid at room temperature; and a liquid component (30) that is a liquid at room temperature, the liquid component having a boiling point from 300 to 450° C.

To provide a wound body of a sheet for sintering bonding with a base material that realizes a satisfactory operational efficiency in a process of producing a semiconductor device comprising sintering bonding portions of semiconductor chips and that also has both a satisfactory storage stability and a high storage efficiency. A wound body 1 according to the present invention has a form in which a sheet for sintering bonding with a base material X is wound around a winding core 2 into a roll shape, the sheet for sintering bonding with a base material X having a laminated structure comprising: a base material 11; and a sheet for sintering bonding 10, comprising an electrically conductive metal containing sinterable particle and a binder component.

An anisotropic conductive film in which conductive particles are disposed in an insulating resin layer has a particle disposition of the conductive particles such that a first orthorhombic lattice region being formed by arranging a plurality of arrangement axes of the conductive particles, disposed in an a direction at a predetermined pitch, in a b direction inclined with respect to the a direction at an angle, and a second orthorhombic lattice region being formed by arranging a plurality of arrangement axes of the conductive particles, disposed in the a direction at a predetermined pitch, in a c direction obtained by inverting the b direction with respect to the a direction are repeatedly disposed.

A method is provided for localised deposition of a material over an element, including deposition of a portion of the material over a portion of a surface of a support; positioning of a portion of the element against the portion of the material; annealing of the material portion increasing, at the end of the treatment, the adhesion force of the material against the portion of the element, the materials of the portion of the element and of the portion of the surface of the support being selected such that the adhesion of the material against the portion of the element is, at the end of the annealing, higher than that of the material against the portion of the surface of the support; and separation of the element and the support at the interface between the material and the portion of the surface of the support, the material remaining secured to the portion of the element.

The present disclosure relates to a method for manufacturing a semiconductor package including vacuum-laminating a non-conductive film on a substrate on which a plurality of through silicon vias are provided and bump electrodes are formed, and then performing UV irradiation, wherein an increase in melt viscosity before and after UV irradiation can be adjusted to 30% or less, whereby a bonding can be performed without voids during thermo-compression bonding, and resin-insertion phenomenon between solders can be prevented, fillets can be minimized and reliability can be improved.

A semiconductor device manufacturing method includes a preparation step and a sinter bonding step. In the preparation step, a sinter-bonding work having a multilayer structure including a substrate, semiconductor chips, and sinter-bonding material layers is prepared. The semiconductor chips are disposed on, and will bond to, one side of the substrate. Each sinter-bonding material layer contains sinterable particles and is disposed between each semiconductor chip and the substrate. In the sinter bonding step, a cushioning sheet having a thickness of 5 to 5000 μm and a tensile elastic modulus of 2 to 150 MPa is placed on the sinter-bonding work, the resulting stack is held between a pair of pressing faces, and, in this state, the sinter-bonding work between the pressing faces undergoes a heating process while being pressurized in its lamination direction, to form a sintered layer from each sinter-bonding material layer.

A dicing die attach film including a dicing film and a die attach film laminated on the dicing film, in which the die attach film has an arithmetic average roughness Ra1 of from 0.05 to 2.50 μm at a surface in contact with the dicing film, and a value of ratio of Ra1 to an arithmetic average roughness Ra2 at a surface that is of the die attach film and is opposite to the surface in contact with the dicing film is from 1.05 to 28.00.

A dicing die attach film including a dicing film and a die attach film laminated on the dicing film, in which the die attach film has an arithmetic average roughness Ra1 of from 0.05 to 2.50 μm at a surface in contact with the dicing film, and a value of ratio of Ra1 to an arithmetic average roughness Ra2 at a surface that is of the die attach film and is opposite to the surface in contact with the dicing film is from 1.05 to 28.00.