Invention compositions are a replacement for high melting temperature solder pastes and preforms in high operating temperature and step-soldering applications. In the use of the invention, a mixture of metallic powders reacts below 350 degrees C. to form a dense metallic joint that does not remelt at the original process temperature.

Invention compositions are a replacement for high melting temperature solder pastes and preforms in high operating temperature and step-soldering applications. In the use of the invention, a mixture of metallic powders reacts below 350 degrees C. to form a dense metallic joint that does not remelt at the original process temperature.

Sintering die-attach materials provide a lead-free solution for semiconductor packages with superior electrical, thermal and mechanical performance to prior art alternatives. Wafer-applied sintering materials form a metallurgical bond to both semiconductor die and adherends as well as throughout the die-attach joint and do not remelt at the original process temperature. Application to either one or both sides of the wafer, as well as paste a film application are disclosed.

Sintering die-attach materials provide a lead-free solution for semiconductor packages with superior electrical, thermal and mechanical performance to prior art alternatives. Wafer-applied sintering materials form a metallurgical bond to both semiconductor die and adherends as well as throughout the die-attach joint and do not remelt at the original process temperature. Application to either one or both sides of the wafer, as well as paste a film application are disclosed.