RESIN-MOLDED ARTICLES, AND A PROCESS AND AN APPARATUS FOR MANUFACTURING THE SAME

Abstract

Resin-molded articles, to which such advantages as strength, rigidness and light weight are secured thanks to kneading with fibers, and which has excellent surface characteristics such as smoothness of the surface and beauty in the appearance, and resistance against weather, ultraviolet rays and light are provided.

The resin-molded article 10 is structured by sticking a resin surface skin member 3 provided with an adhering layer 2 to a molded fibrous base member 1 comprising any of carbon fibers, glass fibers and the complex thereof, and the resin-molded article is manufactured according to the following steps, specifically a step of placing a molded member comprising mixture of fibers and resin on a tray 23, a step to arrange a resin surface skin member provided with an adhering layer onto the molded member such that the adhering layer of the resin surface skin member is directed downward, a step to render the surroundings of the molded member and the resin surface skin member in a negatively-pressurized condition and to concurrently heat the resin surface skin member to raise the tray so that the molded member is closely contacted to the softened resin surface skin member, a step to render the upper part of the tray in a pressurized condition, a step to release the pressure applied to surrounding of the tray and a step to remove the molded base covered with the resin surface skin member.

Claims

1-15. (canceled)

16. A process for manufacturing a resin-molded article comprising the following steps: placing a molded base made of a fibrous base material comprising at least one of a carbon fiber, a glass fiber and a complex thereof on a tray, arranging a resin surface skin member provided with an adhering layer made of an acrylic adhesive over the molded base such that the adhering layer of the resin surface skin member is directed downward, wherein the resin surface skin member comprises at least one material selected from the group consisting of polycarbonate and ABS, and has a thickness of 0.1 to 0.5 mm, rendering surroundings of the molded base and the resin surface skin member in a negatively-pressurized state, heating the resin surface skin member and ascending the tray to thereby closely contact the molded base to the resin surface skin member, and rendering the upper region of the tray in a pressurized state and subsequently opening the surrounding of the tray to remove the molded base coated with the resin surface skin member.

17. The process for manufacturing the resin-molded article according to claim 16, wherein the resin surface skin member has a structure that an adhering layer is attached to an underside of a resin film and a decorative layer is formed on a surface of the molded base.

18. The process for manufacturing the resin-molded article according to claim 16, wherein the resin surface skin member has a structure that the adhering layer is attached to an underside of a resin film and a decorative layer is intervened between the resin film and the adhering layer.

19. The process for manufacturing the resin-molded article according to claim 16, wherein the resin surface skin member is prepared by etching an underside of the resin film and then attaching the adhering layer to the underside.

20. A process for manufacturing resin-molded articles according to claim 16, wherein the resin surface skin member comprises at least one material selected from a group consisting of acryl, polycarbonate, ABS, PET, vinyl chloride, polyurethane and polypropylene.

21. A process for manufacturing resin-molded articles according to claim 16, wherein the thickness of the resin surface skin member is in a range of from 0.1 mm to 0.5 mm.

22. The process for manufacturing the resin-molded article according to claim 16, further comprising preparing a molded article from the molded base material by adding a binding agent selected from the group consisting of ABS, polycarbonate, acryl and nylon to the fibrous base member and performing a molding.

23. An apparatus for manufacturing a resin-molded article comprising: a lower chamber box movably holding a tray for a molded fibrous base in a vertical direction, an upper chamber box having a heater built-in and movable in the vertical direction relative to the lower chamber box, a resin surface skin member extended over an area located between the upper and lower chamber boxes, a negative pressure biasing means arranged in both of the upper and lower chamber boxes and communicating them, a pneumatic biasing means communicated with the upper chamber box, a driving unit for moving the tray in the vertical direction, and a driving unit for moving the upper chamber box in the vertical direction, wherein the apparatus is configured such that the resin surface skin member is coated to the molded base by virtue of press given by the molded fibrous base on the tray against the resin surface skin member owing to the elevation of the lower chamber box, or application and release of bias generated by the negative pressure biasing means and the pneumatic biasing means, or heating by the heater.

Description

BRIEF EXPLANATION FOR THE DRAWINGS

[0038] FIG. 1 An enlarged cross section of the resin-molded article according to an embodiment of the present invention.

[0039] FIG. 2 An enlarged cross section of the resin-molded article according to the other embodiment of the present invention.

[0040] FIG. 3 An enlarged cross section of the resin-molded article according to still the other embodiment of the present invention.

[0041] FIG. 4 An enlarged cross section of the resin-molded article according to still the other embodiment of the present invention.

[0042] FIG. 5 A vertical cross section of the apparatus for manufacturing the resin-molded article according to an embodiment of the present invention.

[0043] FIG. 6 A schematic view showing the former steps of the manufacturing process for the resin-molded article according to an embodiment of the present invention.

[0044] FIG. 7 A schematic view showing the latter steps of the manufacturing process for the resin-molded article according to an embodiment of the present invention.

[0045] FIG. 8 A perspective view showing an example of using the resin-molded article according to the present invention.

[0046] FIG. 9 A perspective view showing the other example of using the resin-molded article according to the present invention.

DESCRIPTION OF REFERENCE NUMERALS

[0047] 1: Molded base [0048] 2: Adhering layer [0049] 3, 29: Resin surface skin member (Transparent resin film) [0050] 4: Decorative layer [0051] 5: Etching [0052] 10: Resin-molded article [0053] 20: Manufacturing apparatus for resin-molded articles [0054] 21: Lower chamber box [0055] 22: Upper chamber box [0056] 23: Tray [0057] 24, 31: Driving unit for vertical moving [0058] 26: Vacuum tank [0059] 27: Switching valve [0060] 28: Holding frame [0061] 30: Heater [0062] 32: Pneumatic tank [0063] 33: Cutter [0064] 41: Automotive bumper [0065] 42: Sideview mirror [0066] 50: Golf shaft

EMBODIMENT FOR CARRYING OUT THE INVENTION

[0067] Now, the present invention is explained by means of the examples given below with referring to the appended drawings. FIGS. 1 to 4 show the resin-molded article 10 prepared according to various examples of the present invention. FIG. 1 shows an example of the resin-molded article 10 which is prepared by sticking a resin surface skin film, for example a transparent resin film 3 via the adhering layer 2 to the upper surface of the molded article 1, which is prepared by mixing a fibrous base material comprising carbon fibers, glass fibers or the complex thereof to a binding agent, followed by molding the mixture. Although the surface of the molded article 1 mixed with the fibrous base material becomes irregular due to the fibrous base material, smooth surface can be attained by sticking the resin film 3 to the irregular surface. Therefore, the molded article 1 can be used for automotive interior and exterior trim parts such as a bumper without applying painting and surface polishing. Note that the molded article prepared by mixing and subsequently molding the fibrous base material and a resin is lightweight and excellent in strength, rigidness and mass-productivity.

[0068] As the manner for molding the fibrous base material, though various manners as exemplified below can be employed, it should not be limited to those manners given below. The molding manner includes molding the fibrous base material following to mixing a binding agent as a binder to the fibrous base material, molding after weaving or twisting the fibrous base material, molding by covering the fibrous base member formed by weaving the fibrous material with a binding agent, molding by covering the fibrous base member formed by twisting the fibrous material with a binding agent, molding by forming the fibrous material by employing the above-described manner and apply foundation painting to the surface, and molding by forming the fibrous material by employing the above-described manner and apply foundation painting to the surface and followed by sanding thereof. While, as the resin surface skin film, various types of synthetic resin sheets being capable of sticking to the fibrous base member may be employed. As an example, if acryl material is used for the transparent resin film 3, the resulted film may be resistant to weather and ultraviolet rays, and the film made of either PC or ABS material may acquire better moldability and productivity. Therefore, the material to be used can be appropriately selected depending on the application. For the adhering layer, an acrylic adhesive is the preferred. The thickness t of the resin surface skin film (transparent resin film 3) containing an adhering layer is preferably in a range of from 0.1 mm to 0.5 mm, however, it is arbitrary determined depending on the application such as place to be used of the molded article. The structures of the molded article 1, the adhering layer 2 and the resin surface skin film 3 as explained in the following are same as those described above, respectively. Note that the employable material examples to be used for the resin surface skin film 3, all materials respectively made of acryl, PC, ABS, PET, vinyl chloride, polyurethane and polypropylene may be given. While, for the binding agent, materials respectively made of ABS, polycarbonate, acryl and nylon are employable. However, the materials being employable for the resin surface skin member is not limited to those described above, any resin sheet that can stick to the molded article in the steps described latter and any material that can be molded with the fibrous material maybe employed for the resin surface skin member and the binding agent, respectively.

[0069] With regard to the resin-molded article 10 according to the example shown in FIG. 2, a decorative layer 4 with letters, figures, etc. is formed by means of a printing means to the surface of the molded article 1 from the mixture of a fibrous base material and a resin material, an adhering layer 2 is attached to the surface of the molded article 1 including the decorative layer 4, and further a transparent film 3 is stuck to the upper side of the adhering layer 2. By structuring the adhering layer 2 with an acryl adhesive, the decorative layer 4 of the molded article will be visible from the outer side of the transparent film 3.

[0070] With regard to the resin-molded article 10 according to the example shown in FIG. 3, the transparent film 3 is stuck to the lower adhering layer 2 in such a state that the adhering layer 2 is attached to the upper side of the molded article 1 and the decorative layer 4 is intervened between the adhesive layer 2 and the transparent film 3. Similarly to the example shown in FIG. 2, the irregular surface of the molded article 1 is smoothed with the transparent film 3 and the decorative layer 4 will be visible from the outer side of the transparent film 3.

[0071] In respect of the resin-molded article 10 shown in FIG. 4, etching 5 is applied to the underside of the resin film and the etched underside is stuck to the upper side of the molded article 1 via the adhering layer 2. By using a transparent film for the resin film and forming the etching in a desired pattern, the etching will be visible as a decorated plane from the outer side of the transparent film 3. Furthermore, binding with the adhering layer 2 is further secured by virtue of the etching and the resin-molded article 10 with rigid surface property can be attained.

[0072] With referring to FIGS. 5 to 7, the process and apparatus for manufacturing resin-molded articles according to the present invention will now be explained. Referring to FIG. 5, the apparatus for manufacturing resin-molded articles 20 according to an example of the present invention is provided with a lower chamber box 21 and an upper chamber box 22 both of those which can be separated relative to the other in the vertical direction. Inside the lower chamber box 21, a tray 23 on which the molded base 1 (shown with a virtual line) made of a fibrous material comprising carbon fibers, glass fibers or the complex thereof is placed is arranged in a vertically-movable fashion. Specifically, a vertically-movable driving unit 24 is provided to the underside of the lower chamber box 21, an actuating rod 24a of the driving unit 24 is inserted into the lower chamber box 21 and a supporting table 25 of the tray 23 is connected to the actuating rod 24a. To the lower chamber box 21, a vacuum suction unit, for example a vacuum tank 26 is connected. The vacuum tank 26 is structured such that it communicates with the upper chamber box 22 via the switching valve 27. Yet, a film holding frame 28 is provided to the upper end of the lower chamber box 21, a resin surface skin film 29 comprising a resin film (a transparent film) as described in FIGS. 1 to 4, an adhering layer, a decorative layer, etc. is exchangeably attached to the holding frame 28, and the inside of the boxes are kept in sealed condition in such a state that the resin surface skin film 29 is attached to the opening located at the upper end of the lower chamber box 21.

[0073] Inside the upper chamber box 22 that ascends and descends relative to the lower chamber box 21, a heater 30 is arranged at the upper position. A vertically-moving driving unit 31 is provided to the upper position of the upper chamber box 22, and the actuating rod 31a thereof is connected to the upper side of the upper chamber box 22. Besides, a pressuring apparatus, e.g. a pneumatic tank 32, for rendering the inside of the upper chamber box 22 to be in a pressurized state is connected to said upper chamber box 22 via the switching valve 27. In such a state that the upper chamber box 22 is lowered and closely contacted to the lower chamber box 21 being attached with the resin surface skin film 29, both insides of the upper and lower chamber boxes 22, 21 are kept in a sealed condition.

[0074] Taking the manufacturing apparatus for the resin-molded articles configured as described above as an example, the process for manufacturing the resin-molded articles according to the present invention will now be explained with referring to FIG. 6 and FIG. 7. At first, as shown in FIG. 6(a), the upper chamber box 22 is ascended by the driving unit 31 to thereby place a target molded article 1, that has been prepared by mixing and subsequent molding of the fibrous base material, on a tray 23 provided inside the lower chamber box 21, and at the same time, a desired resin surface skin film 29 is set to the holding frame 28 of the resin surface skin film at the upper end of the lower chamber box. At this moment, the inside of the lower chamber box 21 is in a sealed condition. For the resin surface skin film 29, any one of the surface skin films, the one consisted of a transparent film and an adhering layer, the one consisted of a transparent film, a decorative layer and an adhering layer, and the one consisted of a transparent film, the underside of which being etched, and an adhering layer is selected corresponding to the type and application of the article. Note that the adhering layer of the resin surface skin film 29 is set downward, namely to the holding frame 28 so as to face off against the molded article 1 placed on the tray 23.

[0075] Then, as shown in FIG. 6(b), the upper chamber box 22 is descended by the driving unit 31 so as to closely contact to the lower chamber box 21, and as shown in FIG. 6(c), by manipulating the switching valve 27, the insides of both upper and lower chamber boxes 22, 21 is vacuum sucked by the vacuum suction unit (vacuum tank 26) so as to be in a negatively-pressurized condition. At the same time, a heater 30 is biased to heat the resin surface skin film 29 in the box to soften the surface skin film. Hanging down of the resin surface skin film 29 somewhat toward the tray 23 side in FIG. 6(c) indicates that the surface skin film has been softened due to heating with the heater 30.

[0076] Then, as shown in FIG. 6(d), the molded article 1 on the tray 23 is ascended by the driving unit 24 and is pressed against the softened resin surface skin film 29 so that the resin surface skin film 29 is stuck to the molded article 1.

[0077] Subsequently, the inside of the upper chamber box 22 is shifted from the negative pressurized state to either opened-to-air state or pneumatic state while actuating the heater 30 inside the upper chamber box 22 to thereby accelerate the adhesion of the resin surface skin film 29 to the surface of the molded article. FIG. 6(e) shows the state that the inside of the upper chamber box 22 is opened to air, and FIG. 6(f) shows the state that the inside of the upper chamber box 22 has been in a pneumatic condition by means of a pneumatic apparatus and the pneumatic tank 32. Although either state may be employed to the manufacturing process, the pneumatic addition configuration as shown in FIG. 6(f) must be employed when the objective article requires more strong sticking property. Following thereto, the pneumatic state and the vacuum suction are released as shown in FIG. 7(a) and the upper chamber box 22 is ascended to remove the resin-molded article being stuck with the surface skin film 29 from the tray 23. Since the peripheral portion of the resin surface skin film 29 protrude slightly from the molded article 1 in this state, the portion of the resin surface skin film 29 that protrudes from the molded article 1 is cut by trimming with a cutter 33 as shown in FIG. 7(b) so that the resin-molded article 10 can be finished. Note that no protrusion of the resin surface skin film from the molded article has been found, trimming work as shown in FIG. 7(b) may be omitted.

[0078] The resin-molded article to which surface processing having been applied according to the present invention may be used for various applications because it has advantages of high strength and rigidness, light weight, highly resistant to weather and ultraviolet rays, smoothed surface irregularity and beautiful appearance. FIG. 8 shows an example of applying the resin-molded article to an automotive bumper 41 and a rear holding member 42a to be used for a sideview mirror 42. The resin-molded article according to the present invention can be simply replaced with existing automotive parts and exert performance in the strength, etc., and it can be accepted further for automotive parts as a material capable of exerting sufficient beauty. Moreover, the molded articles according to the present invention can also be applied to automotive interior trims and various automotive parts, such as a dashboard in front of a driver seat and a handle. Yet, the molded articles according to the present invention can further be applied to e.g. fishing poles, golf gear, rackets for ball game, climbing gear, or care tools such as sticks, powered suits and walking training equipments. FIG. 9 is an example to apply the resin-molded articles 10 according to the present invention to a golf shaft 50, and it is possible to provide a golf shaft that can satisfy various performance having been required by the existing golf shafts and is superior in the beautiful appearance. The application of the resin-molded articles 10 according to the present invention is not limited to the two examples described above and is applicable to various daily commodity and structural parts over the wide-range.

INDUSTRIAL USE OF THE INVENTION

[0079] According to the present invention, an resin-molded article having excellent surface property, such as surface smoothness and beautiful appearance, while securing advantages of strength, rigidness and lightweight given by virtue of kneading of fibers, and further being provided with resistance against weather, ultraviolet rays and light can be attained. In addition, a process and an apparatus for manufacturing resin-molded articles, which enables easy surface processing to the surface of a molded article comprising a fibrous base member, reduction of the manufacturing steps and homogenization of the surface aspect, such as smoothening of surface, can also attained.