The present invention relates to paste compositions comprising an indium metal powder; and an organic vehicle. The organic vehicle includes one or more C8-C18 fatty acids; a salt formed from a C4-C6 carboxylic acid and a tertiary alkanolamine; a cationic catalyst; a thixotrope; and a diluent.

Some implementations of the disclosure are directed to a thermal interface material. In some implementations, a method comprises: applying a solder paste between a surface of a heat generating device and a surface of a heat transferring device to form an assembly; and reflow soldering the assembly to form a solder composite, wherein the solder composite provides a thermal interface between the heat generating device and the heat transferring device, wherein the solder paste comprises: a solder powder; particles having a higher melting temperature than a soldering temperature of the solder paste, wherein the solder paste has a volume ratio of solder powder to high melting temperature particles between 5:1 and 1:1.5; and flux.

A lead-free solder alloy may comprise tin, silver, copper, bismuth, cobalt, and antimony. The alloy may further comprise nickel. The silver may be present in an amount from about 2.0% to 2.8% by weight of the solder. The copper may be present in an amount from about 0.2% to 1.2% by weight of the solder. The bismuth may be present in an amount from about 0.0% to about 5.0% by weight of the solder. In some embodiments, the bismuth may be present in an amount from about 1.5% to 3.2% by weight of the solder. The cobalt may be present in an amount from about 0.001% to about 0.2% by weight of the solder. The antimony may be present in an amount between about 0.0% to about 0.1% by weight of the solder. The balance of the solder is tin.

A solder alloy has an alloy composition consisting of, in mass %, Ag: 0 to 4%, Cu: 0.1 to 1.0%, Ni: 0.01 to 0.3%, Sb: 5.1 to 7.5%, Bi: 0.1 to 4.5%, Co: 0.001 to 0.3%, P: 0.001 to 0.2%, and the balance being Sn.

A method of connecting two CMC substrates that includes providing two substrates; placing one substrate approximate to the other substrate, such that at least a portion of the two substrates overlap and define a brazing area; placing a brazing material approximate the brazing area; defining a primary raster pattern that encompasses the brazing area and a portion of the two substrates outside the brazing area; defining a secondary raster pattern that encompasses the brazing area; allowing a laser to scan the primary raster pattern to preheat the brazing area to a temperature below the brazing material's melting point; allowing the laser to scan the secondary raster pattern to heat the brazing area to a temperature that is above the brazing material's melting point; melting and allowing the brazing material to flow within the brazing area; and cooling the brazing area to form a brazed joint connecting the two substrates.

A printing method for selectively depositing braze powders on a surface comprises extruding a filament from a nozzle moving relative to a surface, where the filament comprises a flowable carrier mixed with a braze powder. As the nozzle moves, the filament is deposited on the surface in a predetermined pattern defined by the motion of the nozzle relative to the surface; thus, the braze powders are deposited at one or more predetermined locations on the surface.

A flux comprising an organic acid; a solvent; and polyoxyethylene behenyl alcohol having an average number of moles of ethylene oxide added of 7 to 40 mol.

Provided is a lead-free solder alloy that has excellent tensile strength and ductility, does not deform after heat cycles, and does not crack. The In and Bi content are optimized and the Sb and Ni content are adjusted. As a result, this solder alloy has an alloy composition including, by mass, 1.0 to 7.0% of In, 1.5 to 5.5% of Bi, 1.0 to 4.0% of Ag, 0.01 to 0.2% of Ni, and 0.01 to 0.15% of Sb, with the remainder made up by Sn.

This invention aims at providing a carbon-coated metal powder having few impurities, a narrower particle size distribution, and sintering properties particularly suitable as a conductive powder of a conductive paste for forming internal conductors in a ceramic multilayer electronic component obtained by co-firing multilayered ceramic sheets and internal conductor layers; a conductive paste containing the carbon-coated metal powder; a multilayer electronic component using the conductive paste; and a method for manufacturing the carbon-coated metal powder. The carbon-coated metal powder has specific properties in TMA or ESCA measurements. The carbon-coated metal powder can be obtained by melting and vaporizing a metallic raw material in a reaction vessel, conveying the generated metal vapor into a cooling tube and rapidly cooling the metal vapor by endothermically decomposing a carbon source supplied into the cooling tube, and forming a carbon coating film on metal nuclei surfaces in parallel with generation of the metal nuclei.

An object of the present invention is to provide a method for producing a conductive material that allows a low electric resistance to be generated, and that is obtained by using an inexpensive and stable conductive material composition containing no adhesive. The conductive material can be provided by a producing method that includes the step of sintering a first conductive material composition that contains silver particles having an average particle diameter (median diameter) of 0.1 μm to 15 μm, and a metal oxide, so as to obtain a conductive material. The conductive material can be provided also by a method that includes the step of sintering a second conductive material composition that contains silver particles having an average particle diameter (median diameter) of 0.1 μm to 15 μm in an atmosphere of oxygen or ozone, or ambient atmosphere, at a temperature in a range of 150° C. to 320° C., so as to obtain a conductive material.