A bonding wire and a method of manufacturing the bonding wire are provided. The bonding wire contains 90.0 to 99.0 wt % of silver (Ag); 0.2 to 2.0 wt % of gold (Au); 0.2 to 4.0 wt % of palladium (Pd), platinum (Pt), rhodium (Rh), or a combination thereof; 10 to 1000 ppm of dopants; and inevitable impurities. In the wire, the ratio of (a)/(b) is 3 to 5, in which (a) represents the amount of crystal grains having <100> orientation in crystalline orientations <hkl> in a wire lengthwise direction and (b) represents the amount of crystal grains having <111> orientation in crystalline orientations <hkl> in the wire lengthwise direction.

A bonding wire and a method of manufacturing the bonding wire are provided. The bonding wire contains 90.0 to 99.0 wt % of silver (Ag); 0.2 to 2.0 wt % of gold (Au); 0.2 to 4.0 wt % of palladium (Pd), platinum (Pt), rhodium (Rh), or a combination thereof; 10 to 1000 ppm of dopants; and inevitable impurities. In the wire, the ratio of (a)/(b) is 3 to 5, in which (a) represents the amount of crystal grains having <100> orientation in crystalline orientations <hkl> in a wire lengthwise direction and (b) represents the amount of crystal grains having <111> orientation in crystalline orientations <hkl> in the wire lengthwise direction.

There is provided an Al bonding wire which can provide a sufficient bonding reliability of bonded parts of the bonding wire under a high temperature state where a semiconductor device using the Al bonding wire is operated. The bonding wire is composed of Al or Al alloy, and is characterized in that an average crystal grain size in a cross-section of a core wire in a direction perpendicular to a wire axis of the bonding wire is 0.01 to 50 μm, and when measuring crystal orientations on the cross-section of the core wire in the direction perpendicular to the wire axis of the bonding wire, a crystal orientation <111> angled at 15 degrees or less to a wire longitudinal direction has a proportion of 30 to 90% among crystal orientations in the wire longitudinal direction.

A bonding wire for a semiconductor device, characterized in that the bonding wire includes a Cu alloy core material and a Pd coating layer formed on a surface of the Cu alloy core material, the bonding wire contains an element that provides bonding reliability in a high-temperature environment, and a strength ratio defined by the following Equation (1) is 1.1 to 1.6:
Strength ratio=ultimate strength/0.2% offset yield strength.(1)

There is provided a bonding wire for a semiconductor device including a coating layer having Pd as a main component on a surface of a Cu alloy core material and a skin alloy layer containing Au and Pd on a surface of the coating layer, the bonding wire further improving 2nd bondability on a Pd-plated lead frame and achieving excellent ball bondability even in a high-humidity heating condition. The bonding wire for a semiconductor device including the coating layer having Pd as a main component on the surface of the Cu alloy core material and the skin alloy layer containing Au and Pd on the surface of the coating layer has a Cu concentration of 1 to 10 at % at an outermost surface thereof and has the core material containing either or both of Pd and Pt in a total amount of 0.1 to 3.0% by mass, thereby achieving improvement in the 2nd bondability and excellent ball bondability in the high-humidity heating condition. Furthermore, a maximum concentration of Au in the skin alloy layer is preferably 15 at % to 75 at %.

There is provided a bonding wire for a semiconductor device including a coating layer having Pd as a main component on a surface of a Cu alloy core material and a skin alloy layer containing Au and Pd on a surface of the coating layer, the bonding wire further improving 2nd bondability on a Pd-plated lead frame and achieving excellent ball bondability even in a high-humidity heating condition. The bonding wire for a semiconductor device including the coating layer having Pd as a main component on the surface of the Cu alloy core material and the skin alloy layer containing Au and Pd on the surface of the coating layer has a Cu concentration of 1 to 10 at % at an outermost surface thereof and has the core material containing either or both of Pd and Pt in a total amount of 0.1 to 3.0% by mass, thereby achieving improvement in the 2nd bondability and excellent ball bondability in the high-humidity heating condition. Furthermore, a maximum concentration of Au in the skin alloy layer is preferably 15 at % to 75 at %.

The present invention provides a bonding wire which can satisfy bonding reliability, spring performance, and chip damage performance required in high-density packaging. A bonding wire contains one or more of In, Ga, and Cd for a total of 0.05 to 5 at %, and a balance being made up of Ag and incidental impurities.

A bonding wire includes a Cu alloy core material, and a Pd coating layer formed on the Cu alloy core material. The bonding wire contains at least one element selected from Ni, Zn, Rh, In, Ir, and Pt. A concentration of the elements in total relative to the entire wire is 0.03% by mass or more and 2% by mass or less. When measuring crystal orientations on a cross-section of the core material in a direction perpendicular to a wire axis of the bonding wire, a crystal orientation <100> angled at 15 degrees or less to a wire axis direction has a proportion of 50% or more among crystal orientations in the wire axis direction. An average crystal grain size in the cross-section of the core material in the direction perpendicular to the wire axis of the bonding wire is 0.9 m or more and 1.3 m or less.

A bonding wire for a semiconductor device includes a Cu alloy core material and a Pd coating layer on a surface of the Cu alloy core material, and contains Ga and Ge of 0.011 to 1.2% by mass in total, which is able to increase bonding longevity of the ball bonded part in the high-temperature, high-humidity environment, and thus to improve the bonding reliability. The thickness of the Pd coating layer is preferably 0.015 to 0.150 m. When the bonding wire further contains one or more elements of Ni, Ir, and Pt in an amount, for each element, of 0.011 to 1.2% by mass, it is able to improve the reliability of the ball bonded part in a high-temperature environment at 175 C. or more. When an alloy skin layer containing Au and Pd is further formed on a surface of the Pd coating layer, wedge bondability improves.

A bonding wire for a semiconductor device includes a Cu alloy core material and a Pd coating layer on a surface of the Cu alloy core material, and contains Ga and Ge of 0.011 to 1.2% by mass in total, which is able to increase bonding longevity of the ball bonded part in the high-temperature, high-humidity environment, and thus to improve the bonding reliability. The thickness of the Pd coating layer is preferably 0.015 to 0.150 m. When the bonding wire further contains one or more elements of Ni, Ir, and Pt in an amount, for each element, of 0.011 to 1.2% by mass, it is able to improve the reliability of the ball bonded part in a high-temperature environment at 175 C. or more. When an alloy skin layer containing Au and Pd is further formed on a surface of the Pd coating layer, wedge bondability improves.