BIO-BASED THERMOFORMED PACKAGING AND METHODS OF FORMING THE SAME

Abstract

In various aspects, the present disclosure pertains to thermoformed webs that comprise polymer films having one or more thermoformed cavities contained therein, the polymer films comprising a polymer blend of amorphous polyethylene terephthalate (APET), polyethylene furanoate (PEF), and a copolyester that comprises (a) dicarboxylic acid residues (e.g., dicarboxylic acid residues that comprise terephthalic acid residues and, optionally, one or more additional dicarboxylic acid residues) and (b) diol residues (e.g., diol residues comprising ethylene glycol residues and, optionally, one or more additional diol monomer residues). Other aspects of the disclosure pertain to methods of forming such thermoformed webs, packaged products comprising such thermoformed webs, and methods of recycling such thermoformed webs.

Claims

1. A thermoformed web comprising a polymer film and having one or more thermoformed cavities contained therein, wherein the polymer film comprises a polymer blend of 0 wt % to 95 wt % of amorphous polyethylene terephthalate (APET), 0 wt % to 95% polyethylene furanoate (PEF), and 5 wt % to 50 wt % of a copolyester that comprises (a) dicarboxylic acid residues comprising polyethylene terephthalate residues and (b) diol residues comprising (i) ethylene glycol residues and (ii) one or more additional diol monomer residues selected from neopentyl glycol residues, 1,4-cyclohexanedimethanol residues, or diethylene glycol residues, wherein the polymer film has a maximum shrinkage during processing of 8% or less.

2. The thermoformed web of claim 1, wherein the polymer film has a crystallization time of at least 2.5 minutes at an isothermal crystallization temperature of 120° C. but not more than 30 minutes at an isothermal crystallization temperature of 165° C. as measured by DSC.

3. A thermoformed web comprising a polymeric film and having one or more thermoformed cavities contained therein, wherein the polymer film comprises a polymer blend of amorphous polyethylene terephthalate (APET), polyethylene furanoate (PEF), and a copolyester that comprises (a) dicarboxylic acid residues comprising polyethylene terephthalate residues and (b) diol residues comprising (i) ethylene glycol residues and (ii) one or more additional diol monomer residues, wherein the polymer film has a crystallization time of at least 2 minutes at an isothermal crystallization temperature of 120° C. as measured by DSC, wherein the polymer film has a maximum shrinkage during processing of 8% or less.

4. The thermoformed web of claim 1, wherein the copolyester, the PEF, and the APET are miscible and the blend is homogeneous.

5. The thermoformed web of claim 1, wherein the polymeric film comprises a core layer disposed between two outer skin layers, wherein the core layer and the skin layers contain the polymer blend and wherein from 0.05 to 10 wt % of inorganic particles are further added to the skin layers.

6. The thermoformed web of claim 1, wherein the polymer film has a melting point ranging from 225 to 255° C.

7. The thermoformed web of claim 1, wherein the polymer film ranges from 25 microns to 2000 microns in thickness.

8. The thermoformed web of claim 1, where the polymer film is formed by extruding the polymer blend in a sheet having one or more layers.

9. The thermoformed web of claim 8, wherein the copolyester, the PEF, and the APET are compounded via a process selected from co-rotating twin screw extrusion, counter-rotating twin screw extrusion, and planetary extrusion.

10. The thermoformed web of claim 1, wherein the polymer film is a blown film, a cast film or a co-extruded film.

11. The thermoformed web of claim 1, wherein the polymer film is a calendared polymer film.

12. The thermoformed web of claim 1, wherein the thermoformed web meets the clumping criteria set forth in Association of Plastic Recyclers (APR) Document Code PET-S-08, or wherein the thermoformed web meets the criteria specified by the Association of Plastics Recyclers (APR) Critical Guidance Protocol for Clear PET Resin and Molded Articles (APR Protocol PET-CG-01).

13. A method of forming a thermoformed web in accordance with claim 1, comprising heating the polymer film to a temperature whereby a softened polymer film is formed and forcing the softened film into one or more mold cavities of a mold.

14. The method of claim 13, wherein the polymer film is heated to a temperature ranging from 70 to 150° C. throughout.

15. The method of claim 13, (a) wherein the thermoformed web is formed on an unsupported machine and the polymer film has a maximum shrinkage during processing in a range of +/−5% in any direction or (b) wherein the thermoformed web is formed on a supported machine and the polymer film has a maximum shrinkage during processing in a range of +/−8%.

16. A packaged product comprising (a) the thermoformed web of claim 1, (b) lidding applied to the thermoformed web, and (c) one or more products positioned in the one or more thermoformed cavities and between the lidding and the thermoformed web.

17. The packaged product of claim 16, wherein the one or more products are consumable products.

18. The packaged product of claim 16, wherein a thickness of the film ranges from 100 to 550 microns.

19. The packaged product of claim 16, wherein the lidding comprises a rupturable layer and a burst resistant layer that can be removed from the rupturable layer, a rupturable layer that can be opened by pressure on an opposite side of the packaged product, or a peelable layer that can be removed from the thermoformed web giving access to the one or more products.

20. The packaged product of claim 16, wherein the one or more products comprise a medical device, a food product or a consumer product.

21. The packaged product of claim 20, wherein a thickness of the film ranges from 200 to 2000 microns.

22. The packaged product of claim 20, wherein the lidding comprises a polymer and/or paper.

23. A process of forming a packaged product in accordance with claim 16 comprising (a) positioning the one or more products in the one or more thermoformed cavities of the thermoformed web and (b) sealing lidding to the thermoformed web thereby enclosing the one or more products in the one or more thermoformed cavities.

24. A method of recycling comprising (a) combining (i) polyethylene terephthalate flakes and/or pellets and (ii) and flakes of a thermoformed web in accordance with claim 1 and/or pellets formed from flakes of a thermoformed web in accordance with claim 1 to form a mixture and (b) crystallizing the mixture at elevated temperature to form a free-flowing crystallized mixture.

25. A recycle stream comprising (a) recycled polyethylene terephthalate flakes and/or pellets and (b) recycled flakes of a thermoformed web in accordance with claim 1 and/or pellets formed from flakes of a thermoformed web in accordance with claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0038] FIG. 1 is a schematic illustration of a blister package that includes a thermoformed web containing an array of thermoformed cavities, known as blisters, which contain a consumable product of interest, in accordance with an embodiment of the present disclosure.

[0039] FIG. 2 is a schematic illustration of a medical device package that includes a thermoformed web containing one or more thermoformed cavities, which contain one or medical devices, in accordance with an embodiment of the present disclosure.

DETAILED DESCRIPTION

[0040] With reference now to FIG. 1, a blister package 100 typically includes a polymer film 102 containing an array of thermoformed cavities, known as blisters 102b, which contain a consumable product 104 of interest (e.g., pharmaceutical dosage forms, food products, tobacco products, cannabis products, chewing gums, etc.) and onto which a cover 106, also known as a lidding, is applied. The lidding 106 can be formed from one or more materials known in the art such as foils, polymer films and/or paper. The lidding 106 is generally scaled to the flat portion 102f of the polymer film 102 that remains as a sealing-area outside and between the blisters 102b, often with a heat seal lacquer.

[0041] During thermoforming, the polymer film 102 is heated to a softening temperature and blisters 102b of a given shape are thermoformed across the film. The resulting product (i.e., the polymer film 102 with blister cavities 102b formed therein), is also referred to herein as a thermoformed web.

[0042] Most blister packaging machines use heat and gas pressure (with or without plug assist) to form blisters in a polymer film obtained from a roll or in the form of a sheet. In a typical process, a polymer film is unwound from a roll and guided through the blister packaging machine. The polymer film 200 passes through contact heaters (or radiant heaters) to reach an elevated temperature such that the polymer film will soften and become pliable. The softened polymer film is then blown into cavities in a mold by using a pressurized gas (e.g., compressed air, etc.), with or without plug assist, which will form blisters in the polymer film, thus creating a thermoformed web. The mold is typically cooled such that the polymer film becomes sufficiently rigid so that the thermoformed web maintains its shape, allowing the thermoformed web to be removed from the mold. (Other processes are known as well, including processes in which blisters are formed by drawing the polymer film into cavities of a forming tool via a vacuum, after the polymer film is heated and softened, with or without plug assist.) Blister packaging machines are commonly unsupported web machines, meaning that the polymer film is pulled through the machine without the sides of the film being clamped, pinned, or otherwise supported. A filling device is then used to place the desired product into the blisters. Subsequently, a sealing station is used to seal the lidding onto the surface of the thermoformed web at a suitable temperature and pressure, which seals the desired product in the blisters. Polymer film thicknesses for processing into blister packaging machines typically range from 100 microns or less to 550 microns or more, for example ranging from 100 to 150 to 200 to 250 to 300 to 350 to 400 to 450 to 500 to 550 microns (in other words, ranging between any two of the preceding values).

[0043] With reference now to FIG. 2, a medical device package 110 commonly includes a polymer film 112 containing one or more thermoformed cavities 112c, which contain, for example, one or more medical devices, medical device components, and/or medical device accessories, and onto which a cover 116, also known as lidding is applied. The lidding 116 can be formed from one or more materials known in the medical device packaging art, for example, polymeric lidding materials such as TYVEK® (a spun bonded material formed from high-density polyethylene fibers, available from DuPont de Nemours, Inc., Wilmington, Del., USA) and/or paper. The lidding 116 is generally scaled to the flat portion of the polymer film 112 that remains as a sealing-area outside the one or more thermoformed cavities 112c (as well as between the one or more thermoformed cavities 112c, in the event there are multiple cavities). Although not shown, the medical device package 110 may be enclosed and sealed within an outer foil pouch.

[0044] During thermoforming of medical device packaging, the polymer film 112 is heated to a softening temperature (e.g., with contact or radiant heaters) and one or more thermoformed cavities 112c of a given shape are thermoformed across the film. The resulting product (i.e., the polymer film 112 with one or more cavities 112c formed therein) is also referred to herein as a thermoformed web.

[0045] In a typical process, a polymer film is unwound from a roll and guided through a medical device packaging machine. The polymer film is heated to reach an elevated temperature such that the polymer film will soften and become pliable. The softened polymer film is then blown or drawn into cavities in a mold by using a pressurized gas (e.g., compressed air, etc.) or vacuum, with or without plug assist, which will form one or more cavities in the polymer film, thus creating a thermoformed web. The mold is typically cooled such that the polymer film becomes sufficiently rigid so that the thermoformed web maintains its shape, allowing the thermoformed web to be removed from the mold. Medical device packaging machines are commonly supported web machines, meaning that the sides of the polymer film are supported at points during the process, for example, with clamps or pins or other supports. One or more medical devices, medical device components, and/or medical device accessories, are then placed into the one or more cavities. Subsequently, a sealing station is used to seal the lidding onto the surface of the thermoformed web at a suitable temperature and pressure, which seals the desired product in the cavities. Polymer film thicknesses for processing into medical device packaging machines typically range from 200 microns or less to 1800 microns or more, for example, ranging from 200 to 400 to 600 to 800 to 1000 to 1200 to 1400 microns.

[0046] Food packaging, consumer product packaging, and other thermoformed articles, like medical device packaging, are commonly performed on a supported web machine. Heating may be performed, for example, using radiant heat.

[0047] The present disclosure pertains to thermoformed webs that comprise a polymer film having one or more thermoformed cavities contained therein, wherein the polymer film comprises a polymer blend of amorphous polyethylene terephthalate (APET), polyethylene furanoate (PEF), and a copolyester that comprises (a) dicarboxylic acid residues (e.g., dicarboxylic acid residues that comprise terephthalic acid residues and, optionally, one or more additional dicarboxylic acid residues) and (b) diol residues (e.g., diol residues comprising ethylene glycol residues and, optionally, one or more additional diol monomer residues).

[0048] In various embodiments, the polymer film comprises a polymer blend of amorphous polyethylene terephthalate (APET), polyethylene furanoate (PEF), and a copolyester that comprises (a) dicarboxylic acid residues comprising polyethylene terephthalate residues and (b) diol residues comprising (i) ethylene glycol residues and (ii) one or more additional diol monomer residues selected from neopentyl glycol residues, 1,4-cyclohexanedimethanol residues, diethylene glycol residues, or triethylene glycol residues.

[0049] In various embodiments, the polymer film comprises a polymer blend of 0 wt % to 95 wt % of amorphous polyethylene terephthalate (APET), 0 wt % to 95% polyethylene furanoate (PEF), and 5 wt % to 50 wt % of a copolyester that comprises (a) dicarboxylic acid residues (e.g., dicarboxylic acid residues that comprise terephthalic acid residues and, optionally, one or more additional dicarboxylic acid residues) and (b) diol residues (e.g., diol residues comprising ethylene glycol residues and, optionally, one or more additional diol monomer residues, for example, one or more additional diol monomer residues selected from neopentyl glycol residues, 1,4-cyclohexanedimethanol residues, or diethylene glycol residues).

[0050] In various embodiments, the polymer film will comprise a polymer blend of 0 wt % or less to 95 wt % or more of amorphous polyethylene terephthalate, for example, ranging from 0 wt % to 5 wt % to 10 wt % to 15 wt % to 20 wt % to 25 wt % to 30 wt % to 35 wt % to 40 wt % to 45 wt % to 50 wt % to 55 wt % to 60 wt % to 65 wt % to 70 wt % to 75 wt % to 80 wt % to 85 wt % to 87.5 wt % to 90 wt % to 92.5 wt % to 95 wt % amorphous polyethylene terephthalate; 0 wt % or less to 95 wt % or more of polyethylene furanoate (PEF), for example, ranging from 0 wt % to 5 wt % to 10 wt % to 15 wt % to 20 wt % to 25 wt % to 30 wt % to 35 wt % to 40 wt % to 45 wt % to 50 wt % to 55 wt % to 60 wt % to 65 wt % to 70 wt % to 75 wt % to 80 wt % to 85 wt % to 87.5 wt % to 90 wt % to 92.5 wt % to 95 wt % polyethylene furanoate (PEF); and 5 wt % or less to 50 wt % or more of the copolyester, for example, ranging from 5 wt % to 7.5 wt % to 10 wt % to 12.5 wt % to 15 wt % to 20 wt % to 25 wt % to 30 wt % to 35 wt % to 40 wt % to 45 wt % to 50 wt % of the copolyester.

[0051] In various embodiments, the dicarboxylic acid residues of the copolyester will comprise 70 mol % or more of terephthalic acid residues. For example the dicarboxylic acid residues of the copolyester may comprise from 70 mol % to 75 mol % to 80 mol % to 85 mol % to 90 mol % to 95 or 97.5 mol % to 99 mol % to 100 mol % of terephthalic acid residues. In some embodiments, the dicarboxylic acid residues of the copolyester may further comprise 30 mol % or less of additional dicarboxylic acid residues selected from aromatic dicarboxylic acid residues (other than terephthalic acid residues), aliphatic dicarboxylic acid residues having up to 20 carbon atoms, or both. For example, the additional dicarboxylic acid residues of the copolyester may comprise from 30 mol % to 25 mol % to 20 mol % to 15 mol % to 5 mol % to 2.5 mol % to 1 mol % to 0 mol % of additional dicarboxylic acid residues. Specific examples of such additional dicarboxylic acid residues include isophthalic acid, biphenyldicarboxylic acid, naphthalenedicarboxylic acid, stilbenedicarboxylic acid, cyclohexanedicarboxylic, malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, and/or dodecanedioic dicarboxylic acid, among others.

[0052] In various embodiments the diol residues of the copolyester will comprise 70 mol % or more of ethylene glycol residues. For example the diol residues of the copolyester may comprise from 70 mol % to 75 mol % to 80 mol % to 85 mol % to 90 mol % to 95 mol % to 97.5 mol % to 99 mol % ethylene glycol residues. In various embodiments, the diol residues of the copolyester will comprise from 30 mol % or less of the additional diol residues. For example, the additional diol residues may comprise from 30 mol % to 25 mol % to 20 mol % to 15 mol % to 5 mol % to 2.5 mol % to 1 mol % of additional diol residues. In some embodiments, the additional diol residues of the copolyester may comprise 30 mol % or less of neopentyl glycol residues, for example, from 30 mol % to 25 mol % to 20 mol % to 15 mol % to 5 mol % to 2.5 mol % to 1 mol % to 0 mol % of neopentyl glycol residues. In some embodiments, the additional diol residues of the copolyester may comprise 30 mol % or less of 1,4-cyclohexanedimethanol residues, for example, from 30 mol % to 25 mol % to 20 mol % to 15 mol % to 5 mol % to 2.5 mol % to 1 mol % to 0 mol % of 1,4-cyclohexanedimethanol residues. In some embodiments, the additional diol residues may comprise 30 mol % or less of diethylene glycol residues, for example, from 30 mol % to 25 mol % to 20 mol % to 15 mol % to 5 mol % to 2.5 mol % to 1 mol % to 0 mol % of diethylene glycol residues. In some embodiments, the additional diol residues may comprise 30 mol % or less of triethylene glycol residues, for example, from 30 mol % to 25 mol % to 20 mol % to 15 mol % to 5 mol % to 2.5 mol % to 1 mol % to 0 mol % of triethylene glycol residues.

[0053] In various embodiments, APET, PEF, and the copolyester are miscible and the blend is homogeneous.

[0054] In embodiments where the thermoformed web is used in blister packaging, the polymer film will typically range from 100 microns or less to 550 microns or more, for example ranging from 100 to 150 to 200 to 250 to 300 to 350 to 400 to 450 to 500 to 550 microns, in thickness.

[0055] In embodiments where the thermoformed web is used in medical device, food, and consumer product packaging, the polymer film will typically range from 200 microns or less to 1800 microns or more, for example, ranging from 200 to 400 to 600 to 800 to 100 to 1200 to 1400 microns, in thickness.

[0056] In various embodiments, the polymer film has a melting point ranging from 225 to 255° C. for example, ranging from 225° C. to 230° C. to 235° C. to 240° C. to 245° C. to 250° C. to 255° C.

[0057] In some embodiments, the polymer film will further comprise pigments in an amount sufficient to give the film color. These include transparent colors such as transparent blue and transparent green colors. In some embodiments, additives are added to achieve a dark color with an L* value <40, from the CIELAB color space where L* denotes brightness from 0 (black) to 100 (white), and/or NIR (near infrared) reflectance <=10%.

[0058] In some embodiments, the polymer film will comprise a core layer of the polymer blend between two outer skin layers to which a small amount (e.g., from 0.05 to 10 wt %) of inorganic particles such as mineral particles are added to the blend, which will improve the ease at which layers of the thermoformed web can be separated from one another when stacked. Typically each skin layer will comprise between 2.5 to 20% of the overall fill thickness and the core layer will comprise between 60 to 95% of the overall fill thickness.

[0059] In some aspects, the present disclosure pertains to methods of forming a thermoformed web that has one or more thermoformed cavities contained therein. The thermoformed web is formed from a polymer film that comprises a blend of amorphous polyethylene terephthalate, polyethylene furanoate, and a copolyester as detailed elsewhere herein. The methods comprise heating the polymer film to a temperature whereby a softened polymer film is formed, and forcing the softened film into one or more cavities in a mold (e.g., by blowing the softened film into the one or more cavities using positive pressure, by drawing the softened film into the one or more cavities using a vacuum, with or without plug assist, etc.), thereby forming the one or more cavities. The polymer film is then cooled and removed from the mold.

[0060] In some embodiments, the thermoforming temperature of the polymer film ranges from 70° C. to 150° C. (e.g., ranging from 70° C. to 80° C. to 90° C. to 100° C. to 110° C. to 120° C. to 130° C. to 140° C. to 150° C.), and preferably from 100 to 125° C. in certain embodiments.

[0061] In some embodiments, the polymer film is formed on an unsupported web machine and has a maximum shrinkage in any direction during processing in the range of +/−1%, +/−2%, +/−3%, +/−4%, or +/−5%. In some embodiments, the polymer film is formed on a supported web machine and has a maximum shrinkage in any direction during processing in the range of +1-1%, +/−2%, +/−3%, +/−4%, +/−5%, +/−6%, +/−7%, or +/−8%. As discussed below, the direction of greatest shrinkage is typically the direction transverse to the unwind, or machine, direction of the film.

[0062] In some aspects, the present disclosure pertains to processes for forming a polymer film that can subsequently be used to create a thermoformed web that has one or more thermoformed cavities. The processes may comprise drying pieces (e.g., flakes and/or pellets) of an amorphous polyethylene terephthalate and of a copolyester as detailed elsewhere herein until the residual moisture level is below 100 ppm (preferably as low as possible), and extruding a mixture of the amorphous polyethylene terephthalate and the copolyester to form a polymer film. In some embodiments, the polymer film is calendared.

[0063] In some embodiments, the amorphous polyethylene terephthalate and polyethylene furanoate pieces are dried at a temperature ranging from 120 to 140° C. for a period ranging from 8 to 12 hours and the copolyester is dried at a temperature ranging from 60 to 72° C. for a period ranging from 12 to 16 hours.

[0064] In some embodiments, the extrusion is performed using an extruder that comprises at least one extruder barrel, screw and feed system, a feed block (e.g., a two-layer feed block, three-layer feed block, etc.) and a die or a multi-manifold die. Each layer type will have its own extruder barrel, screw and feeder (for example, an A/B/A tri-layer film has two extruders) and there can be screen changers and melt pumps on commercial equipment. All of the extrusion materials will flow into a feed block followed by a die or a multi-manifold die. In some embodiments, the polymer blend can be extruded under conditions where the extruder that is operated at a barrel temperature ranging from 235 to 290° C., at a feed block temperature ranging from 235 to 290° C., and at a die temperature ranging from 230 to 270° C.

[0065] In some aspects, the present disclosure pertains to blister packages that include (a) a thermoformed web that has one or more thermoformed blister cavities contained therein and is formed from a polymer film that comprises a blend of amorphous polyethylene terephthalate, polyethylene furanoate, and a copolyester as described in more detail elsewhere herein, (b) lidding applied to the thermoformed web, and (c) one or more consumable products positioned in the one or more thermoformed blister cavities and between the lidding and the thermoformed web. Examples of such consumable products include solid, semi-solid and liquid pharmaceutical dosage forms (e.g., tablets, pills, capsules, powders and syrups), tobacco products, cannabis products, consumer products (e.g., razors, toothbrushes, and pens) and food products (e.g., chewing gum, yogurt, and spreads), among others. In certain embodiments, the lidding is laid over and bonded to an area of the thermoformed web surrounding each blister cavity with a heat seal lacquer. In certain embodiments, the lidding comprises a rupturable layer such as a rupturable foil layer, one or more layers of polymers, or paper, among others, which may be scored in some cases to enhance rupturability. The lidding may also contain a burst resistant layer that provides burst security until it is removed. For example, the burst resistant layer may be a label adhered to an external surface of the rupturable layer.

[0066] In some aspects, the present disclosure pertains to medical device packages that include (a) a thermoformed web that has one or more thermoformed cavities contained therein and is formed from a polymer film that comprises a blend of amorphous polyethylene terephthalate, polyethylene furanoate, and a copolyester as described in more detail elsewhere herein, (b) lidding applied to the thermoformed web, and (c) one or more medical devices, medical device components and/or medical device accessories positioned in the one or more thermoformed cavities and between the lidding and the thermoformed web. Examples of such medical devices include, for example, orthopedic devices, catheters, injectables, surgical kits, and inhalers, among many others. In certain embodiments, the lidding is laid over and bonded to an area of the thermoformed web surrounding each cavity with a heat seal lacquer. In certain embodiments, the lidding comprises polymeric material and/or paper. Commonly used lidding materials are those that let gases pass but not a pathogenic agent (e.g., a bacterial or viral microorganism). These materials include a spun bonded material formed from high-density polyethylene fibers (e.g., TYVEK®) and special paper grades. The porosity of these materials enables sterilization by ethylene oxide and works by penetration of this gas through the lidding. In both cases, a peelable adhesive is typically used on the lidding, which is grid coated to let the gas pass as well. Alternatively, polymeric films are also available that can be sterilized by e-beam or gamma radiation. In some cases the medical device package may be enclosed and sealed within an outer foil pouch.

[0067] In various embodiments, the present disclosure is directed to processes that comprise (a) placing a product (e.g., consumer product, medical device, medical device component, medical device accessory, etc.) in a cavity of a thermoformed web that is formed from a polymer film that comprises a blend of amorphous polyethylene terephthalate, polyethylene furanoate (PEF), and a copolyester as described elsewhere herein, and (b) sealing a lidding to the thermoformed web. In some embodiments, the lidding is sealed to the thermoformed web at an elevated sealing temperature. For example, the lidding may be attached to the thermoformed web at a sealing temperature ranging from 110 to 210° C., for example, ranging from 110° C. to 120° C. to 130° C. to 140° C. to 150° C. to 160° C. to 170° C. to 180° C. to 190° C. to 200° C. to 210° C.

[0068] Other aspects of the present disclosure pertain to methods of recycling that comprise (a) combining (i) polyethylene terephthalate flakes and/or polyethylene terephthalate pellets and (ii) flakes of a thermoformed web that has one or more thermoformed cavities contained therein and that is formed from a polymer film that comprises a blend of amorphous polyethylene terephthalate, polyethylene furanoate, and a copolyester as detailed elsewhere herein and/or pellets formed from such flakes of thermoformed web to form a mixture of flakes and/or pellets. In some embodiments, the mixture is crystallized at elevated temperature for a suitable time (e.g., 160 to 170° C. for 15 to 45 minutes) to form a crystallized mixture. The crystallized mixture can then be fed into further process streams. For example, the crystallized mixture may be dried and be fed into an extruder to form an extruded product (e.g., film, pellets, or strand).

[0069] Other aspects of the present disclosure pertain to recycle streams that comprise (a) recycled polyethylene terephthalate flakes and/or pellets and having admixed therewith (b) recycled flakes of a thermoformed web that has one or more thermoformed cavities contained therein and that is formed from polymer film that comprises a blend of amorphous polyethylene terephthalate, polyethylene furanoate, and a copolyester as detailed elsewhere herein and/or pellets formed from such recycled flakes of thermoformed web.