A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950° C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000° C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 μm and an average width of 1 to 2 μm, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950° C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000° C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 μm and an average width of 1 to 2 μm, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

According to various implementations of the invention, high quality a-axis XBCO may be grown with low surface roughness. According to various implementations of the invention, low surface roughness may be obtained by: 1) adequate substrate preparation; 2) calibration of flux rates for constituent atoms; and/or 3) appropriate control of temperature during crystal growth. According to various implementations of the invention, a wafer comprises a smoothing layer of c-axis XBCO; a first conducting layer of a-axis XBCO formed on the smoothing layer; an insulating layer formed on the first conducting layer; and a second conducting layer of a-axis XBCO formed on the insulating layer, where, for a same surface roughness, a thickness of the smoothing layer and the first conducting layer combined is greater than a thickness of the first conducting layer without the smoothing layer.

A method of in-situ transfer during fabrication of a component comprising a 2-dimensional crystalline thin film on a substrate is disclosed. In one embodiment, the method includes forming a layered structure comprising a polymer, a 2-dimensional crystalline thin film, a metal catalyst, and a substrate. The metal catalyst, being a growth medium for the two-dimensional crystalline thin film, is etched and removed by infiltrating liquid to enable the in-situ transfer of the two-dimensional crystalline thin film directly onto the underlying substrate.

A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950° C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000° C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 μm and an average width of 1 to 2 μm, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950° C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000° C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 μm and an average width of 1 to 2 μm, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

Methods are provided for separating a crystalline film from its main body. The method uses ion implantation to generate an ion damaged layer underneath the surface of the crystalline object. The ion damage changes the crystal structure of the ion damaged layer, so it will have different optical transmittance and absorption characteristics from the undamaged part of the crystalline object. A laser beam with a wavelength that is higher than the absorption edge of the non-ion damaged material, but within the absorption range of the ion damaged material is irradiated at or past the ion damaged layer, causing further damage to the ion damaged layer. The film can then be separated from the main body of the crystalline object.

A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950° C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000° C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 μm and an average width of 1 to 2 μm, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

A method of producing polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y (Y-358) whereby powders of yttrium (III) oxide, a barium (II) salt, and copper (II) oxide are pelletized, calcined at 850 to 950 C. for 8 to 16 hours, ball milled under controlled conditions, pelletized again and sintered in an oxygen atmosphere at 900 to 1000 C. for up to 72 hours. The polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y thus produced is in the form of elongated crystals having an average length of 2 to 10 m and an average width of 1 to 2 m, and embedded with spherical nanoparticles of yttrium deficient Y.sub.3Ba.sub.5Cu.sub.8O.sub.y having an average diameter of 5 to 20 nm. The spherical nanoparticles are present as agglomerates having flower-like morphology with an average particles size of 30 to 60 nm. The ball milled polycrystalline Y.sub.3Ba.sub.5Cu.sub.8O.sub.y prepared under controlled conditions shows significant enhancement of superconducting and flux pinning properties.

Methods are provided for separating a crystalline film from its main body. The method uses ion implantation to generate an ion damaged layer underneath the surface of the crystalline object. The ion damage changes the crystal structure of the ion damaged layer, so it will have different optical transmittance and absorption characteristics from the undamaged part of the crystalline object. A laser beam with a wavelength that is higher than the absorption edge of the non-ion damaged material, but within the absorption range of the ion damaged material is irradiated at or past the ion damaged layer, causing further damage to the ion damaged layer. The film can then be separated from the main body of the crystalline object.