According to the present invention, there is provided a SiC epitaxial wafer including: a 4H-SiC single crystal substrate which has a surface with an off angle with respect to a c-plane as a main surface and a bevel part on a peripheral part; and a SiC epitaxial layer having a film thickness of 20 μm or more, which is formed on the 4H-SiC single crystal substrate, in which a density of an interface dislocation extending from an outer peripheral edge of the SiC epitaxial layer is 10 lines/cm or less.

A method includes depositing a silicon layer, which includes first portions over a plurality of strips, and second portions filled into trenches between the plurality of strips. The plurality of strips protrudes higher than a base structure. The method further includes performing an anneal to allow parts of the first portions of the silicon layer to migrate toward lower parts of the plurality of trenches, and performing an etching on the silicon layer to remove some portions of the silicon layer.

Embodiments are directed to high electron mobility transistor (HEMT) devices and methods. One such HEMT device includes a substrate having a first surface, and first and second heterostructures on the substrate and facing each other. Each of the first and second heterostructures includes a first semiconductor layer on the first surface of the substrate, a second semiconductor layer on the first surface of the substrate, and a two-dimensional electrode gas (2DEG) layer between the first and second semiconductor layers. A doped semiconductor layer is disposed between the first and second heterostructures, and a source contact is disposed on the first heterostructure and the second heterostructure.

A stack including at least a semiconductor drift layer stacked on a single-crystal diamond substrate having a coalescence boundary, wherein the coalescence boundary of the single-crystal diamond substrate is a region that exhibits, in a Raman spectrum at a laser excitation wavelength of 785 nm, a full width at half maximum of a peak near 1332 cm.sup.−1 due to diamond that is observed to be broader than a full width at half maximum of the peak exhibited by a region different from the coalescence boundary, the coalescence boundary has a width of 200 μm or more, and the semiconductor drift layer is stacked on at least the coalescence boundary.

An electrostatically controlled sensor includes a GaN/AlGaN heterostructure having a 2DEG channel in the GaN layer. Source and drain contacts are electrically coupled to the 2DEG channel through the AlGaN layer. A gate dielectric is formed over the AlGaN layer, and gate electrodes are formed over the gate dielectric, wherein each gate electrode extends substantially entirely between the source and drain contacts, wherein the gate electrodes are separated by one or more gaps (which also extend substantially entirely between the source and drain contacts). Each of the one or more gaps defines a corresponding sensing area between the gate electrodes for receiving an external influence. A bias voltage is applied to the gate electrodes, such that regions of the 2DEG channel below the gate electrodes are completely depleted, and regions of the 2DEG channel below the one or more gaps in the direction from source to drain are partially depleted.

A method of forming a structure having a coating layer includes the following steps: providing a substrate; coating a fluid on the surface of the substrate, where the fluid includes a carrier and a plurality of silicon-containing nanoparticles; and performing a heating process to remove the carrier and convert the silicon-containing nanoparticles into a silicon-containing layer, a silicide layer, or a stack layer including the silicide layer and the silicon-containing layer.

A single crystal semiconductor structure includes: an amorphous substrate; a single crystal semiconductor layer provided on the amorphous substrate; and a thin orienting film provided between the amorphous substrate and the single crystal semiconductor layer, wherein the thin orienting film is a single crystal thin film, and the thin orienting film has a non-zero thickness that is equal to or less than 10 times a critical thickness h.sub.c.

A single crystal semiconductor structure includes: an amorphous substrate; a single crystal semiconductor layer provided on the amorphous substrate; and a thin orienting film provided between the amorphous substrate and the single crystal semiconductor layer, wherein the thin orienting film is a single crystal thin film, and the thin orienting film has a non-zero thickness that is equal to or less than 10 times a critical thickness h.sub.c.

A substrate made of doped single-crystal silicon has an upper surface. A doped single-crystal silicon layer is formed by epitaxy on top of and in contact with the upper surface of the substrate. Either before or after forming the doped single-crystal silicon layer, and before any other thermal treatment step at a temperature in the range from 600° C. to 900° C., a denuding thermal treatment is applied to the substrate for several hours. This denuding thermal treatment is at a temperature higher than or equal to 1,000° C.

A method includes depositing a silicon layer, which includes first portions over a plurality of strips, and second portions filled into trenches between the plurality of strips. The plurality of strips protrudes higher than a base structure. The method further includes performing an anneal to allow parts of the first portions of the silicon layer to migrate toward lower parts of the plurality of trenches, and performing an etching on the silicon layer to remove some portions of the silicon layer.