A transistor includes a multilayer film in which an oxide semiconductor film and an oxide film are stacked, a gate electrode, and a gate insulating film. The multilayer film overlaps with the gate electrode with the gate insulating film interposed therebetween. The multilayer film has a shape having a first angle between a bottom surface of the oxide semiconductor film and a side surface of the oxide semiconductor film and a second angle between a bottom surface of the oxide film and a side surface of the oxide film. The first angle is acute and smaller than the second angle. Further, a semiconductor device including such a transistor is manufactured.

The present invention relates to a method for manufacturing a diamond substrate, and more particularly, to a method of growing diamond after forming a structure of an air gap having a crystal correlation with a lower substrate by heat treatment of a photoresist pattern and an air gap forming film material on a substrate such as sapphire (Al.sub.2O.sub.3). Through such a method, a process is simplified and the cost is lowered when large-area/large-diameter single crystal diamond is heterogeneously grown, stress due to differences in a lattice constant and a coefficient of thermal expansion between the heterogeneous substrate and diamond is relieved, and an occurrence of defects or cracks is reduced even when a temperature drops, such that a high-quality single crystal diamond substrate may be manufactured and the diamond substrate may be easily self-separated from the heterogeneous substrate.

A method of forming a gallium oxide film is provided, and the method may include supplying mist of a material solution comprising gallium atoms and chlorine atoms to a surface of a substrate while heating the substrate so as to form the gallium oxide film on the surface of the substrate, in which a molar concentration of chlorine in the material solution is equal to or more than 3.0 times and equal to or less than 4.5 times a molar concentration of gallium in the material solution.

A semiconductor device is manufactured using a transistor in which an oxide semiconductor is included in a channel region and variation in electric characteristics due to a short-channel effect is less likely to be caused. The semiconductor device includes an oxide semiconductor film having a pair of oxynitride semiconductor regions including nitrogen and an oxide semiconductor region sandwiched between the pair of oxynitride semiconductor regions, a gate insulating film, and a gate electrode provided over the oxide semiconductor region with the gate insulating film positioned therebetween. Here, the pair of oxynitride semiconductor regions serves as a source region and a drain region of the transistor, and the oxide semiconductor region serves as the channel region of the transistor.

Provided are a substrate processing method and a substrate processing apparatus, wherein a silicon oxide film is favorably embedded. The substrate processing method includes forming a silicon oxide film by repeating a cycle a plurality of times, the cycle including: forming an adsorption layer by supplying a silicon-containing gas to a substrate having a depression formed therein and causing the silicon-containing gas to be adsorbed on the substrate; etching at least a portion of the adsorption layer by supplying a shape control gas to the substrate; and supplying an oxygen-containing gas to the substrate and causing the oxygen-containing gas to react with the adsorption layer, wherein the temperature of the substrate is 400° C. or lower.

A method of producing graphene or other two-dimensional material such as graphene including heating the substrate held within a reaction chamber to a temperature that is within a decomposition range of a precursor, and that allows two-dimensional crystalline material formation from a species released from the decomposed precursor; establishing a steep temperature gradient (preferably >1000° C. per meter) that extends away from the substrate surface towards an inlet for the precursor; and introducing precursor through the relatively cool inlet and across the temperature gradient towards the substrate surface. The steep temperature gradient ensures that the precursor remains substantially cool until it is proximate the substrate surface thus minimizing decomposition or other reaction of the precursor before it is proximate the substrate surface. The separation between the precursor inlet and the substrate is less than 100 mm.

A transistor includes a multilayer film in which an oxide semiconductor film and an oxide film are stacked, a gate electrode, and a gate insulating film. The multilayer film overlaps with the gate electrode with the gate insulating film interposed therebetween. The multilayer film has a shape having a first angle between a bottom surface of the oxide semiconductor film and a side surface of the oxide semiconductor film and a second angle between a bottom surface of the oxide film and a side surface of the oxide film. The first angle is acute and smaller than the second angle. Further, a semiconductor device including such a transistor is manufactured.

Light emitting diode (LED) devices comprise: a patterned substrate comprising a substrate body, a plurality of integral features protruding from the substrate body, and a base surface defined by spaces between the plurality of integral features; a selective layer comprising a dielectric material located on the surfaces of the integral features, wherein there is an absence of the selective layer on the base surface; and a III-nitride layer comprising a III-nitride material on the selective layer and the base surface.

To suppress a change in electrical characteristics and to improve reliability in a semiconductor device using a transistor including an oxide semiconductor. The semiconductor device includes a gate electrode over an insulating surface, an oxide semiconductor film overlapping with the gate electrode, a gate insulating film which is between the gate electrode and the oxide semiconductor film and is in contact with a surface of the oxide semiconductor film, a protective film in contact with an opposite surface of the surface of the oxide semiconductor film, and a pair of electrodes in contact with the oxide semiconductor film. In the gate insulating film or the protective film, the amount of gas having a mass-to-charge ratio m/z of 17 released by heat treatment is greater than the amount of nitrogen oxide released by heat treatment.

A method of producing graphene or other two-dimensional material such as graphene including heating the substrate held within a reaction chamber to a temperature that is within a decomposition range of a precursor, and that allows two-dimensional crystalline material formation from a species released from the decomposed precursor; establishing a steep temperature gradient (preferably >1000° C. per meter) that extends away from the substrate surface towards an inlet for the precursor; and introducing precursor through the relatively cool inlet and across the temperature gradient towards the substrate surface. The steep temperature gradient ensures that the precursor remains substantially cool until it is proximate the substrate surface thus minimizing decomposition or other reaction of the precursor before it is proximate the substrate surface. The separation between the precursor inlet and the substrate is less than 100 mm.