Gallium nitride (GaN) integrated circuit technology is described. In an example, an integrated circuit structure includes a substrate including silicon, the substrate having a top surface. A first trench is in the substrate, the first trench having a first width. A second trench is in the substrate, the second trench having a second width less than the first width. A first island is in the first trench, the first island including gallium and nitrogen and having first corner facets below the top surface of the substrate. A second island is in the second trench, the second island including gallium and nitrogen and having second corner facets below the top surface of the substrate.

PECVD methods for depositing a film at a low deposition rate comprising intermittent activation of the plasma are disclosed. The flowable film can be deposited using at least a polysilane precursor and a plasma gas. The deposition rate of the disclosed processes may be less than 500 Å/min.

A method for forming a doped layer is disclosed. The doped layer may be used in a NMOS or a silicon germanium application. The doped layer may be created using an n-type halide species in a n-type dopant application, for example.

The present disclosure describes a semiconductor device and methods for forming the same. The semiconductor device includes nanostructures on a substrate and a source/drain region in contact with the nanostructures. The source/drain region includes epitaxial end caps, where each epitaxial end cap is formed at an end portion of a nanostructure of the nanostructures. The source/drain region also includes an epitaxial body in contact with the epitaxial end caps and an epitaxial top cap formed on the epitaxial body. The semiconductor device further includes gate structure formed on the nanostructures.

A method is provided for forming Group IIIA-nitride layers, such as GaN, on substrates. The Group IIIA-nitride layers may be deposited on mesa-patterned semiconductor-on-insulator (SOI, e.g., silicon-on-insulator) substrates. The Group IIIA-nitride layers may be deposited by heteroepitaxial deposition on mesa-patterned semiconductor-on-insulator (SOI, e.g., silicon-on-insulator) substrates.

A semiconductor laminate includes a silicon carbide substrate having a first main surface and a second main surface opposite the first main surface, and an epitaxial layer composed of silicon carbide disposed on the first main surface. The second main surface has an average value of roughness Ra of 0.1 μm or more and 1 μm or less with a standard deviation of 25% or less of the average value.

A method of depositing a silicon film on a recess formed in a surface of a substrate is provided. The substrate is placed on a rotary table in a vacuum vessel, so as to pass through first, second, and third processing regions in the vacuum vessel. An interior of the vacuum vessel is set to a first temperature capable of breaking an Si—H bond. In the first processing region, Si.sub.2H.sub.6 gas having a temperature less than the first temperature is supplied to form an SiH.sub.3 molecular layer on its surface. In the second processing region, a silicon atomic layer is exposed on the surface of the substrate, by breaking the Si—H bond in the SiH.sub.3 molecular layer. In the third processing region, by anisotropic etching, the silicon atomic layer on an upper portion of an inner wall of the recess is selectively removed.

A method of forming Si or Ge-based and III-V based vertically integrated nanowires on a single substrate and the resulting device are provided. Embodiments include forming first trenches in a Si, Ge, III-V, or Si.sub.xGe.sub.1-x substrate; forming a conformal SiN, SiO.sub.xC.sub.yN.sub.z layer over side and bottom surfaces of the first trenches; filling the first trenches with SiO.sub.x; forming a first mask over portions of the Si, Ge, III-V, or Si.sub.xGe.sub.1-x substrate; removing exposed portions of the Si, Ge, III-V, or Si.sub.xGe.sub.1-x substrate, forming second trenches; forming III-V, III-V.sub.xM.sub.y, or Si nanowires in the second trenches; removing the first mask and forming a second mask over the III-V, III-V.sub.xM.sub.y, or Si nanowires and intervening first trenches; removing the SiO.sub.x layer, forming third trenches; and removing the second mask.

A film deposition method may include preparing a non-planar substrate including a first surface, a second surface, and an inclined surface between the first surface and the second surface; depositing a film having a thickness deviation on the first surface, the second surface, and the inclined surface; and etching the film deposited on the first surface, the second surface, and the inclined surface. A height of the second surface may be different than a height of the first surface.

Embodiments of the present disclosure include techniques related to techniques for processing materials for manufacture of group-III metal nitride and gallium based substrates. More specifically, embodiments of the disclosure include techniques for growing large area substrates using a combination of processing techniques. Merely by way of example, the disclosure can be applied to growing crystals of GaN, AlN, InN, InGaN, AlGaN, and AlInGaN, and others for manufacture of bulk or patterned substrates. Such bulk or patterned substrates can be used for a variety of applications including optoelectronic and electronic devices, lasers, light emitting diodes, solar cells, photo electrochemical water splitting and hydrogen generation, photodetectors, integrated circuits, and transistors, and others.